SHI Hui*,WANG Shuchen.师 辉1*,王树臣2[J].Plating & Finishing,2021,(2):22-27.[doi:10.3969/j.issn.1001-3849.2021.02.0050]
稀土硝酸铈对油管锌钙系磷化膜形貌和性能的影响
- Title:
- 师 辉1*,王树臣2
- 文献标志码:
- A
- 摘要:
- 以油管常用的材料45#钢作为基体,在添加了稀土硝酸铈的磷化液中制备锌钙系磷化膜。研究了硝酸铈质量浓度对磷化膜的元素组成、膜重、厚度和耐蚀性的影响。结果表明:硝酸铈不会改变磷化膜的元素组成,但是会改变磷化膜的形貌、膜重和厚度,从而显著影响其耐蚀性。随着硝酸铈质量浓度增加到100 mg/L,磷化膜中Zn和Ca质量分数均先升高后降低,P质量分数基本呈降低的趋势,磷化膜的晶粒形态及晶粒间隙有所不同,膜重先增加后下降,厚度先增加后减薄,与之对应的磷化膜耐蚀性先逐渐提高随后变差。当硝酸铈质量浓度为50 mg/L时,制备的磷化膜晶粒细小、均匀且致密度较高,膜重最高,达到12.45 g/m2,厚度达到8.1 μm,该磷化膜表现出良好的耐蚀性,明显优于其他磷化膜。
- Abstract:
- The zinc-calcium phosphating film was prepared by adding rare earth cerium nitrate into the phosphating solution using 45# steel as the matrix. And the influence of cerium nitrate mass concentration on the elemental composition, weight, thickness and corrosion resistance of phosphating film was studied. The results showed that cerium nitrate did not change the elemental composition of phosphating film, but it can change the morphology, weight and thickness, thus significantly affecting the corrosion resistance of phosphating film. As the mass concentration of cerium nitrate increased to 100 mg/L, the mass fraction of Zn and Ca in phosphating film first increased and then decreased, while the mass fraction of P showed a trend of decrease. The grain morphology and grain gap of phosphating film were different. The weight and thickness increased first and then decreased, which lead to a gradual improvement in the corrosion resistance followed by deterioration. When the cerium nitrate mass concentration was 50 mg/L, the phosphating film with uniform grain size and high density had the highest weight up to 12.45 g/m2 and thickness up to 8.1 μm. The phosphating film showed good corrosion resistance, obviously better than that of the other phosphating film.
参考文献/References:
[1] 温翠玲, 张磊. 工艺参数对Q345钢表面锌-钙系磷化膜耐蚀性的影响[J]. 电镀与环保, 2020, 40(2): 31-33.
Wen C L, Zhang L. Influence of process parameters on corrosion resistance of Zn-Ca phosphating film on Q345 steel[J]. Electroplating & Pollution Control, 2020, 40(2):31-33 (in Chinese).
[2] 田浩亮, 魏世丞, 陈永雄, 等. 高速电弧喷涂在工程机械零部件再制造领域中的应用现状[J]. 表面技术,2013, 42(3): 99-102.
Tian H L,Wei S C,Chen Y X, et al. Application status of high velocity arc spraying technology in remanufacturing construction machinery parts[J]. Surface Technology, 2013, 42(3): 99-102 (in Chinese).
[3] Zhang S L, Zhang X L, Chen H H, et al.The role of rare earth nitrate (REN) in phosphating of aluminum alloy[J]. Metal Finishing, 2017, 105(6): 39-45.
[4] 郭国才, 莫振宇, 吴清源, 等. 稀土铈对中温锌系磷化的影响[J]. 电镀与环保, 2018, 38(4): 37-41.
Guo G C, Mo Z Y, Wu Q Y, et al. Effect of rare earth element cerium on zinc phosphating process at middle temperature[J]. Electroplating & Pollution Control, 2018, 38(4): 37-41 (in Chinese).
[5] 张海峰, 刘双枝, 王芳, 等. 稀土硝酸镧对6061铝合金原位磷化涂层性能和表面形貌的影响[J]. 材料保护,2017, 50(1): 49-52.
Zhang H F, Liu S Z, Wang F, et al. Effect of rare earth lanthanum nitrate on corrosion resistance and surface morphology of in-situ phosphatizing organic coatings on 6061 aluminum alloy[J]. Materials Protection, 2017,50(1): 49-52 (in Chinese).
[6] 王晓华. 钢铁黑膜磷化的研究[D]. 大连: 辽宁师范大学, 2010.
[7] 张瑜, 赵佳新, 代永祺. 硝酸铈对镁合金锌、锰系磷酸盐转化膜性能的影响[J]. 电镀与环保, 2019, 39(4):58-61.
Zhang Y, Zhao J X, Dai Y Q,et al. Effect of cerium nitrate on properties of zinc and manganese phosphate conversion coatings on magnesium alloy[J]. Electroplating & Pollution Control, 2019, 39(4): 58-61 (in Chinese).
[8] Kuang J C. Advance effect of rare earth nitrates on green process of phosphating[J]. Advanced Materials Research, 2013, (838-841): 2802-2805.
[9] Nooman M A, Khan M N, Hossain S D, et al. Study the physical, electrical and dielectric properties of calcium doped Ni-Zn ferrites[J]. Modern Physics Letters B, 2019, 33(12): 145-152.
[10] 王鹏飞. AZ91D镁合金环保型钙系磷化膜的制备与耐腐蚀性能研究[D]. 青岛: 青岛科技大学, 2014.
[11] Kuang J C, Huang Y. Effect of rare earth on the coating-forming and mechanism of phosphatization[J]. Journal of Rare Earths, 2010, (S1): 132-135.
[12] Koclega D, Radziszewska A, Dymek S, et al. Improvement of corrosion resistance of 13CrMo4-5 steel by Ni-based laser cladding coatings[J]. Journal of Materials Engineering and Performance, 2020, (29): 3702-3713.
[13] 朱红梅, 胡际鹏, 李柏春, 等. 铁基材料表面激光熔覆不锈钢涂层的研究进展[J]. 表面技术, 2020, 49(3):74-84.
Zhu H M, Hu J P, Li B C, et al. Research progress of laser cladding stainless steel coating on iron-based materials[J]. Surface Technology, 2020, 49(3): 74-84 (in Chinese).
相似文献/References:
[1]于海青*,丁春燕.中温锌钙系磷化工艺在Q345钢防腐蚀中的应用[J].电镀与精饰,2020,(5):44.[doi:10.3969/j.issn.1001-3849.2020.05.0070]
YU Haiqing*,DING Chunyan.Application of Medium Temperature Zn-Ca Phosphating Process in Corrosion Protection of Q345 Steel[J].Plating & Finishing,2020,(2):44.[doi:10.3969/j.issn.1001-3849.2020.05.0070]
[2]白玉伟*,陈锐.封闭处理对工程车用件磷化膜形貌和耐蚀性的影响[J].电镀与精饰,2021,(3):1.[doi:10.3969/j.issn.1001-3849.2021.03.001]
BAI Yuwei*,CHEN Rui.白玉伟*,陈锐[J].Plating & Finishing,2021,(2):1.[doi:10.3969/j.issn.1001-3849.2021.03.001]
[3]于海青*,王金涛,王 东.Q345钢表面SiC颗粒掺杂锌钙系磷化膜的制备与性能[J].电镀与精饰,2021,(7):20.[doi:10.3969/j.issn.1001-3849.2021.07.004]
YU Haiqing*,WANG Jintao,WANG Dong.Preparation and Properties of Zinc-Calcium Phosphate Film Doped with SiC Particles on Q345 Steel[J].Plating & Finishing,2021,(2):20.[doi:10.3969/j.issn.1001-3849.2021.07.004]
[4]孙 伟*,许 霞,张伟华.建筑结构钢锌钙系磷化膜的结构与耐蚀性研究[J].电镀与精饰,2022,(10):60.[doi:10.3969/j.issn.1001-3849.2022.10.010]
SUN Wei*,XU Xia,ZHANG Weihua.Investigation on Structure and Corrosion Resistance of Zinc-Calcium Phosphating Films on Building Structural Steel[J].Plating & Finishing,2022,(2):60.[doi:10.3969/j.issn.1001-3849.2022.10.010]
[5]孙伟*,杨辉,徐秀凤,等.促进剂对建筑结构钢锌钙系磷化膜形貌和耐蚀性的影响[J].电镀与精饰,2023,(4):8.[doi:10.3969/j.issn.1001-3849.2023.04.002]
Sun Wei*,Yang Hui,Xu Xiufeng,et al.Effects of accelerating agents on morphology and corrosion resistance of zinc-calcium phosphating films on building structural steel[J].Plating & Finishing,2023,(2):8.[doi:10.3969/j.issn.1001-3849.2023.04.002]
备注/Memo
收稿日期: 2020-07-24;修回日期: 2020-10-06
作者简介: 师辉(1974—),高级讲师,主要研究方向:机械制造技术、材料表面处理技术等。email:fxsh2020@sina.com
基金项目: 江苏省职业技术教育学会2019年度课题(XHYBLX2019136);国家重点研究计划项目(2017YFA0700203)