SONG Zhengwei*,DING Lifeng,WANG Peilin,et al.Preparation and Corrosion Resistance of Ni-P/Cu-Zn Super-Hydrophobic Composite Coating on the Surface of Mg Alloy[J].Plating & Finishing,2021,(7):10-14.[doi:10.3969/j.issn.1001-3849.2021.07.002]
镁合金表面Ni-P/Cu-Zn超疏水复合涂层制备及耐蚀性研究
- Title:
- Preparation and Corrosion Resistance of Ni-P/Cu-Zn Super-Hydrophobic Composite Coating on the Surface of Mg Alloy
- 文献标志码:
- A
- 摘要:
- 本文主要研究了镁合金表面Ni-P/Cu-Zn超疏水复合涂层的制备和耐蚀性。复合涂层通过化学镀镍磷、电镀铜锌合金、阳极氧化、表面修饰后获得,化学镀Ni-P层为内层,电镀Cu-Zn层为中间层,超疏水层为外层。对复合涂层的结构和性能进行了表征。实验结果表明,复合涂层与基底结合力强,无鼓泡脱落现象,涂层厚度约为34 μm。Ni-P/Cu-Zn涂层氧化后表面形成微纳米结构,用十八烷基硫醇修饰后的涂层具有优良的超疏水性,水的表面接触角约为155°,涂层的自腐蚀电流密度相对于未修饰涂层和基底下降1~2个数量级,阻抗大幅提升,说明涂层具有很好的耐蚀性,能够为镁合金提供较好的保护。
- Abstract:
- The preparation and corrosion resistance of Ni-P/Cu-Zn super-hydrophobic composite coating on the surface of magnesium alloy was studied in this paper, the composite coating was obtained via electroless Ni-P plating, Cu-Zn alloys plating, anodic oxidation, and surface modification processes, electroless Ni-P as inner layer, electroplating Cu-Zn alloys as interlayer and super-hydrophobic coating as outer layer. The structure and properties of composite coating were characterized. The test results shown that the obtained composite coating has strong binding force with the substrate, no bubbling and falling off phenomenon was detected, the thickness of coating was about 34 μm. Micro/nano structure was formed on the surface of Ni-P/Cu-Zn coating after anodic oxidation treatment. The coating modified by octadecanethiol showed excellent super-hydrophobicity with a water contact angle of about 155°, the corrosion current density (icorr) of the modified coating decreases by 1-2 orders of magnitude relative to the unmodified coating and substrate, and the impedance was greatly improved, which indicates that the coating has good corrosion resistance which can provide better protection for magnesium alloys.
参考文献/References:
[1] 潘复生. "镁合金腐蚀与防护"专题序言[J]. 表面技术, 2019, 48: 11-12.
Pan F S. Thematic introduction of corrosion and proctection of Mg alloy[J]. Surface Technology, 2019, 48:11-12(in chinese).
[2] 王福会. 镁合金防护涂层技术[C]// 2018中国铸造活动周. 2018.
Wang F H. Protective coating technology of magnesium alloy[C]// China Foundry week 2018, 2018(in chinese).
[3] Chen J L, Fang L, Wu F, et al. Corrosion resistance of a self-healing rose-like MgAl-LDH coating intercalated with aspartic acid on AZ31 Mg alloy[J]. Progress in Organic Coatings, 2019, 136: 105234.
[4] Ghavidel N, Allahkaram S R, Naderi R, et al. Corrosion and wear behavior of an electroless Ni-P/nano-SiC coating on AZ31 Mg alloy obtained through environmentally-friendly conversion coating[J]. Surface and Coatings Technology, 2020, 382: 125156.
[5] Han J P, Tang S W, San H S, et al. Formation mechanism of calcium phosphate coating on a plasma electrolytic oxidized magnesium and its corrosion behavior in simulated body fluids[J]. Journal of Alloys and Compounds, 2020, 818: 152834.
[6] Xu Z, Eduok U, Szpunar J. Effect of annealing temperature on the corrosion resistance of MgO coatings on Mg alloy[J]. Surface and Coatings Technology, 2019, 357: 691-697.
[7] Zhang J, Xie Z H, Chen H, et al. Electroless deposition and characterization of a double-layered Ni-B/Ni-P coating on AZ91D Mg alloy from eco-friendly fluoride-free baths[J]. Surface and Coatings Technology, 2018, 342: 178-189.
[8] Zhang Z Q, Zeng R C, Yan W, et al. Corrosion resistance of one-step superhydrophobic polypropylene coating on magnesium hydroxide-pretreated magnesium alloy AZ31[J]. Journal of Alloys and Compounds, 2020, 821: 153515.
[9] 宿辉,栾柏瑞. AZ91D镁合金表面无铬无氟前处理工艺研究[J]. 电镀与精饰, 2019, 41(1): 14-18.
Xu H, Luan B R. Study on Chromium-Free and Fluorine-Free Pretreatment Process of AZ91D Magnesium Alloy[J]. Electroplating and Finishing, 2019, 41(1):14-18(in chinese).
[10] Song Z W, Xie Z H, Yu G, et al. A novel palladium-free surface activation process for electroless nickel deposition on micro-arc oxidation film of AZ91D Mg alloy[J]. Journal of Alloys and Compounds, 2015, 623: 274-281.
[11] 牟世辉, 尹鸿鹍,代肇一. 镀铜优化对AZ91D镁合金疏水膜性能的影响[J]. 电镀与精饰, 2019, 41(6): 29-32.
Mu S H, Yin H K, Dai Z Y. Effect of Copper Plating Optimization on the Performance of AZ91D Magnesium Alloy Hydrophobic Membrane[J]. Electroplating and Finishing, 2019, 41(6): 29-32(in chinese).
相似文献/References:
[1]徐美玲,亢淑梅,陈婷婷,等.添加氯化铈对镁合金Ni?P化学镀镀层性能影响[J].电镀与精饰,2019,(1):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
XU Meiling,KANG Shumei,CHEN Tingting,et al.Properties of Electroless Plating Ni?P on Magnesium AlloySubstrate by Adding CeCl3[J].Plating & Finishing,2019,(7):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
[2]牟世辉,尹鸿鹍,代肇一.镀铜优化对AZ91D镁合金疏水膜性能的影响[J].电镀与精饰,2019,(6):29.[doi:10.3969/j.issn.1001-3849.2019.06.006]
MU Shihui,YIN Hongkun,DAI Zhaoyi.Effect of Copper Plating Optimization on the Performance of AZ91D Magnesium Alloy Hydrophobic Membrane[J].Plating & Finishing,2019,(7):29.[doi:10.3969/j.issn.1001-3849.2019.06.006]
[3]刘 玮,安成强*,郝建军,等.钼酸钠对AZ91D镁合金钒/锆复合转化膜性能的影响[J].电镀与精饰,2019,(8):10.[doi:10.3969/j.issn.1001-3849.2019.08.003]
LIU Wei,AN Chengqiang*,HAO Jianjun,et al.Effect of Na2MoO4 on Properties of Vanadium/Zirconate Conversion Coating on AZ91D Magnesium Alloy[J].Plating & Finishing,2019,(7):10.[doi:10.3969/j.issn.1001-3849.2019.08.003]
[4]李佳霖,郝建军,牟世辉.Fe2+对镁合金电化学磷化改性研究[J].电镀与精饰,2019,(10):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
LI Jialin,HAO Jianjun,MOU Shihui.Study on Electrochemical Phosphating Modification of Magnesium Alloy by Fe2+[J].Plating & Finishing,2019,(7):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
[5]贾启华,许晓娟*.沉积时间对镁合金化学镀镍的影响[J].电镀与精饰,2019,(12):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
JIA Qihua,XU Xiaojuan*.Effect of Deposition Time on Direct Electroless Plating of Magnesium Alloys[J].Plating & Finishing,2019,(7):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
[6]王 丽,顾 威,郭 荣,等.环保型无机缓蚀剂对AZ91D镁合金的缓蚀效果[J].电镀与精饰,2020,(4):18.[doi:10.3969/j.issn.1001-3849.2020.04.0040]
WANG Li,GU Wei,GUO Rong,et al.Inhibition Effect of Environmental Protection Inorganic Corrosion Inhibitor on AZ91D Magnesium Alloy[J].Plating & Finishing,2020,(7):18.[doi:10.3969/j.issn.1001-3849.2020.04.0040]
[7]党在清*.镁合金复合镀层的制备及其结构与性能表征[J].电镀与精饰,2020,(11):16.[doi:10.3969/j.issn.1001-3849.2020.11.0040]
DANG Zaiqing*.Study on the Structure and Properties of Composite Coating on Magnesium Alloy[J].Plating & Finishing,2020,(7):16.[doi:10.3969/j.issn.1001-3849.2020.11.0040]
[8]王晓奇*,曹 慧,雷 彪.镁合金表面电弧离子镀TiAlN薄膜的结构与性能研究[J].电镀与精饰,2021,(6):25.[doi:10.3969/j.issn.1001-3849.2021.06.006]
WANG Xiaoqi*,CAO Hui,LEI Biao.Structure and Properties of TiAlN Films by Arc Ion Plating on Mg Alloys[J].Plating & Finishing,2021,(7):25.[doi:10.3969/j.issn.1001-3849.2021.06.006]
[9]牟世辉*,李鑫宇.恒电流作用下AZ91D镁合金磷化膜生长研究[J].电镀与精饰,2021,(9):1.[doi:10.3969/j.issn.1001-3849.2021.09.001]
MU Shihui*,LI Xinyu.Growth of Phosphating Film on AZ91D Magnesium Alloy Under Constant Current[J].Plating & Finishing,2021,(7):1.[doi:10.3969/j.issn.1001-3849.2021.09.001]
[10]陈 力*,陈玉峰,张鉴达.镁合金表面硅酸盐封闭磷化膜的腐蚀失效行为[J].电镀与精饰,2022,(1):57.[doi:10.3969/j.issn.1001-3849.2022.01.010]
CHEN Li*,CHEN Yufeng,ZHANG Jianda.Corrosion Failure Behavior of Silicate Sealed Phosphating Film on Surface of Magnesium Alloy[J].Plating & Finishing,2022,(7):57.[doi:10.3969/j.issn.1001-3849.2022.01.010]
备注/Memo
收稿日期: 2020-07-25;修回日期: 2020-10-10
*通信作者: 宋政伟,adsszw@163.com.
基金项目: 山西省教育厅科技创新项目(2020L0656)