LUO Cong,MA Shuo *.Effect of Chromium-Free Sealing Treatment on Corrosion Resistance of Anodic Oxide Films on ZL101A Aluminum Alloy[J].Plating & Finishing,2022,(2):46-50.[doi:10.3969/j.issn.1001-3849.2022.02.010]
无铬封闭处理对ZL101A铝合金阳极氧化膜耐蚀性能的影响
- Title:
- Effect of Chromium-Free Sealing Treatment on Corrosion Resistance of Anodic Oxide Films on ZL101A Aluminum Alloy
- 分类号:
- TQ153.6
- 文献标志码:
- A
- 摘要:
- 对汽车用 ZL101A 铝合金进行阳极氧化,并分别采用热水封闭、钴盐封闭、锆盐封闭和铈盐封闭等无铬封闭工艺对阳极氧化膜进行封闭处理。表征了封闭前后阳极氧化膜的形貌,并测试分析了封闭前后阳极氧化膜的厚度和耐蚀性能。结果表明:与未封闭阳极氧化膜相比,封闭处理后阳极氧化膜的孔隙率降低,表面平整度和致密性改善,耐蚀性能有不同程度提高,但厚度变化不大。铈盐封闭阳极氧化膜表面平整度和致密性最好,粗糙度为 0.216 μ m ,电荷转移电阻达到 1.93×105 Ω ·cm 2 ,腐蚀质量损失为 1.79 g/m 2 ,其耐蚀性能优于热水封闭、钴盐封闭和锆盐封闭阳极氧化膜。铈盐封闭是效果最好的无铬封闭工艺。
- Abstract:
- Anodic oxidation of ZL101A aluminum alloy for automobile was carried out , and the anodic oxidation film was sealed by chrome-free sealing process of hot water sealing , cobalt sealing , zirconium sealing and cerium salt sealing , respectively. The morphology of the anodic oxide films before and after sealing was characterized , and the thickness and corrosion resistance of the anodic oxide films before and after sealing were tested and analyzed. The results showed that compared with the unsealed anodic oxide film , the porosity of the anodic oxide film after sealing treatment was decreased , the surface roughness and compactness were improved , and the corrosion resistance was improved to different degrees , but the thickness was almost unchanged. The surface roughness and densification of the anodic oxide film sealed with cerium salt was 0.216 μ m , the charge transfer resistance reached 1.93×10 5 Ω ·cm 2 and the corrosion loss was 1.79 g/m 2 . The corrosion resistance of the anodic oxide film sealed with cerium salt was better than that of the anodic oxide films sealed with hot water , cobalt salt and zirconium salt. Cerium salt sealing was the best chrome-free sealing process.
参考文献/References:
[1] 程飞 , 兰文奎 , 梁代春 . 汽车轮毂用 ZL101A 铝合金的热处理新工艺研究 [J]. 热加工工艺 , 2013, (22): 190-191.
Cheng F, Lan W K, Liang D C. Study on heat treatment new technology of hub ZL101A AI alloy used for car wheel [J]. Hot Working Technology, 2013, (22): 190-191 (in Chinese).
[2] 王新节 , 王维 . 消失模铸造重型汽车 ZL101A 变速箱壳体的缺陷分析 [J]. 特种铸造及有色合金 , 2014, 34(12): 1292-1294.
Wang X J, Wang W. Defects analysis of aluminum alloy gear box housing for heavy duty truck in lost foam casting [J]. Special Casting & Nonferrous Alloys, 2014, 34(12): 1292-1294 (in Chinese).
[3] 吴忠 . 汽车用 ZL101A 铝合金表面 Ni-Co 合金镀层的硬度 [J]. 电镀与精饰 , 2018, 40(11): 5-9.
Wu Z. Hardness of Ni-Co alloy coatings prepared on the surface of ZL101A aluminum alloy for automobile [J]. Plating & Finishing, 2018, 40(11): 5-9 (in Chinese).
[4] 王小亭 , 常学义 , 邱永福 . 多孔阳极氧化铝膜制备方法的研究进展 [J]. 东莞理工学院学报 , 2019, 26(3): 46-52.
Wang X T, Chang X Y, Qiu Y F. Advances in the preparation of porous anodic aluminum oxide films [J]. Journal of Dongguan University of Technology, 2019, 26(3): 46-52 (in Chinese).
[5] Lee W, Park S J. Porous anodic aluminum oxide: anodization and templated synthesis of functional nanostructures [J]. Chemical Reviews, 2014, 114(15): 7487-7556.
[6] Satake T, Yokoyama K, Shirakawa S, et al. Electromigration in aluminum film stripes coated with anodic aluminum oxide films [J]. Japanese Journal of Applied Physics, 2014, 12(2): 518-522.
[7] 张培 . 铝合金阳极氧化膜结构、制备工艺及显微硬度的关系研究 [D]. 北京 : 北京化工大学 , 2013.
[8] 李陵川 , 卢立柱 , 张懿 . 铝阳极氧化膜微孔内电沉积超细金属微粒 [J]. 过程工程学报 , 2001, 1(3): 281-284.
Li L C, Lu L Z, Zhang Y. Electrodeposited ultrafine metal particles in pores of porous anodic films of aluminum [J]. Chinese Journal of Process Engineering, 2001, 1(3): 281-284 (in Chinese).
[9] 梁钊源 , 麻彦龙 , 朱彭舟 , 等 . 铝锂合金酒石酸 - 硫酸阳极氧化膜的低能耗封闭处理研究 [J]. 重庆理工大学学报 ( 自然科学 ), 2020, 34(2): 100-106.
Liang Z Y, Ma Y L, Zhu P Z, et al. Low energy-consumption sealing treatment study of tartaric-sulphuric acid anodic film on aluminum-lithium alloy [J]. Journal of Chongqing University of Technology(Natural Science), 2020, 34(2): 100-106 (in Chinese).
[10] Daniman M, Kocaba M, Curioni M, et al. Investigation of porous anodic film formation on AA1050 by electrochemical impedance spectroscopy [J]. Surface Review and Letters, 2020, 27(8): 1950186.
相似文献/References:
[1]祁怀伟*,吴心元,王亮兵,等.6061铝合金阳极氧化膜的抗霉菌研究[J].电镀与精饰,2020,(11):39.[doi:10.3969/j.issn.1001-3849.2020.11.0080]
QI Huaiwei*,WU Xinyuan,WANG Liangbing,et al.Study on the Anti-Mold Performance of 6061Aluminum Alloy Anodic Oxidation Film[J].Plating & Finishing,2020,(2):39.[doi:10.3969/j.issn.1001-3849.2020.11.0080]
[2]王宏智,吴心元,吕成斌,等.3A21铝合金本色阳极氧化膜的抗霉菌研究[J].电镀与精饰,2021,(7):52.[doi:10.3969/j.issn.1001-3849.2021.07.010]
WANG Hongzhi,WU Xinyuan,LYU Chengbin,et al.Study on the Antifungal Activity of 3A21 Aluminum Alloy Anodic Oxidation Film[J].Plating & Finishing,2021,(2):52.[doi:10.3969/j.issn.1001-3849.2021.07.010]
[3]郭绍福,赵春红*.植酸封孔对铝制件阳极氧化膜耐蚀性的影响[J].电镀与精饰,2021,(8):6.[doi:10.3969/j.issn.1001-3849.2021.08.002]
GUO Shaofu,ZHAO Chunhong*.Effect of Phytic Acid Sealing on Corrosion Resistance of Anodic Oxidation Film on Aluminum Parts[J].Plating & Finishing,2021,(2):6.[doi:10.3969/j.issn.1001-3849.2021.08.002]
[4]李海宏,郝 健*.铝合金柠檬酸-硫酸阳极氧化及性能研究[J].电镀与精饰,2022,(2):20.[doi:10.3969/j.issn.1001-3849.2022.02.005]
LI Haihong,HAO Jian *.Anodic Oxidation of Aluminum Alloy with Citric Acid-Sulfuric Acid and Its Properties[J].Plating & Finishing,2022,(2):20.[doi:10.3969/j.issn.1001-3849.2022.02.005]
[5]吴姗姗,于瑾佳*,刘历波.铈盐封孔对建筑铝合金阳极氧化膜耐蚀性的影响[J].电镀与精饰,2022,(4):1.[doi:10.3969/j.issn.1001-3849.2022.04.001]
WU Shanshan,YU Jinjia*,LIU Libo.Effect of Cerium Salt Sealing on Corrosion Resistance of Anodic Oxide Film on Architectural Aluminum Alloy[J].Plating & Finishing,2022,(2):1.[doi:10.3969/j.issn.1001-3849.2022.04.001]
[6]高培云.锆盐封孔对建筑铝合金阳极氧化膜耐蚀性能的影响[J].电镀与精饰,2022,(5):44.[doi:10.3969/j.issn.1001-3849.2022.05.008]
GAO Peiyun.Effect of Zirconium Salt Sealing on Corrosion Resistance of Anodic Oxide Film on Aluminium Alloy Used in Construction[J].Plating & Finishing,2022,(2):44.[doi:10.3969/j.issn.1001-3849.2022.05.008]
[7]成张佳宁,黄坤坤.建筑铝合金表面制备耐久性超疏水阳极氧化膜[J].电镀与精饰,2022,(6):16.[doi:10.3969/j.issn.1001-3849.2022.06.004]
CHENG Zhangjianing,HUANG Kunkun.Preparation of Durable Super-Hydrophobic Anodic Oxide Film on Aluminum Alloy for Construction[J].Plating & Finishing,2022,(2):16.[doi:10.3969/j.issn.1001-3849.2022.06.004]
[8]王臻卓.电力设备材料酒石酸阳极氧化及其腐蚀行为研究[J].电镀与精饰,2022,(6):26.[doi:10.3969/j.issn.1001-3849.2022.06.006]
WANG Zhenzhuo.Study on Tartaric Acid Anodic Oxidation of Electrical Equipment Materials and Its Corrosion Behavior[J].Plating & Finishing,2022,(2):26.[doi:10.3969/j.issn.1001-3849.2022.06.006]
[9]邱小云,王冀恒. 铝合金阳极氧化膜沸水-稀土盐双重封闭及力学性能研究 [J].电镀与精饰,2022,(7):30.[doi:10.3969/j.issn.1001-3849.2022.07.006]
QIU Xiaoyun,WANG Jiheng.Dual Sealing of Anodic Oxidation Film on Aluminum Alloy with Boiling Water and Rare Earth Salt and Mechanical Properties[J].Plating & Finishing,2022,(2):30.[doi:10.3969/j.issn.1001-3849.2022.07.006]
[10]王薇薇.稀土铈对建筑铝材表面阳极氧化膜腐蚀防护性能的影响?/div>[J].电镀与精饰,2022,(11):59.[doi:10.3969/j.issn.1001-3849.2022.11.011]
WANG Weiwei.Effect of Rare Earth Cerium on Corrosion Protection of Anodic Oxidation Film on Surface of Construction Aluminum[J].Plating & Finishing,2022,(2):59.[doi:10.3969/j.issn.1001-3849.2022.11.011]
备注/Memo
收稿日期: 2021-06-17 修回日期: 2021-07-27 作者简介: 骆骢( 1976 —),男,本科,教授, email : Luo_7878@126.com 通信作者: 马硕( 1981 —),男,博士,讲师,主要研究方向:汽车材料、表面工程应用等, email : mashuo@whut.edu.cn 基金项目: 2013 新疆维吾尔自治区教育厅课题(新教职成 18 号)