　WANG Li,LI Tinggui,WANG Feng.High Temperature Manganese Phosphating Treatment of Piston Pin for Hydraulic Cylinder[J].Plating & Finishing,2020,(4):32-35.[doi:10.3969/j.issn.1001-3849.2020.04.0070]
点击复制

液压缸活塞销高温锰系磷化处理()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2020年4
页码:
32-35
栏目:
出版日期:
2020-04-15

文章信息/Info

Title:
High Temperature Manganese Phosphating Treatment of Piston Pin for Hydraulic Cylinder
作者:
王 莉1; 李庭贵1; 王 凤2
1. 泸州职业技术学院 机械工程学院， 四川 泸州 646000； 2. 西华大学， 四川 成都 610039
Author(s):
WANG Li1;  LI Tinggui1;  WANG Feng2
1. School of Mechanical Engineering, Luzhou Vocational and Technical College, Luzhou 646000, China　2. Xihua University, Chengdu 610039, China
关键词:
活塞销; 高温锰系磷化; 表调处理; 显微硬度; 耐磨性能
Keywords:
piston pin high temperature manganese phosphating surface conditioning treatment microhardness wear resistance
DOI:
10.3969/j.issn.1001-3849.2020.04.0070
文献标志码:
A
摘要:
为满足使用环境对液压缸活塞销耐磨性提出的较高要求，采用两种方法对活塞销样件进行高温锰系磷化处理，表征和测试了锰系磷化处理后样件的形貌和性能，并与原始样件进行了对比。结果表明：采用高温锰系磷化处理后，活塞销样件宏观上都呈黑色，其显微硬度有不同程度的提高，耐磨性能也有所改善。其中，在表调处理后再进行高温锰系磷化处理对于提高活塞销样件的耐磨性能效果最好。
Abstract:
In order to meet the high requirement of using environment for the wear resistance of piston pin for hydraulic cylinder, the piston pin samples were treated by high temperature manganese phosphating with two different methods. The morphology and properties of the samples after manganese phosphating treatment were characterized and tested, and were compared with that of the original sample. The results showed that the piston pin sample after high temperature manganese phosphating treatment show light black at the macro level, and its microhardness and wear resistance have been improved. It was the best effect to improve the wear resistance of piston pin samples to be treated with high temperature manganese phosphating after surface conditioning treatment.

参考文献/References:

[1] 谢明,李丽波,李悠,等.常温锌锰系磷化工艺及磷化膜性能研究[J]. 电镀与环保, 2018, 38(6): 63-65.
[2] 关锰, 孟园月, 张春华, 等. 紧固件表面锰系磷化膜的制备及摩擦磨损性能[J]. 沈阳工业大学学报, 2016, 38(2):147-152.
[3] 李文平, 赵冉. 磷化处理对齿轮材料摩擦磨损特性的影响[J]. 汽车工艺与材料, 2016, 9: 57-59.
[4] 马刘宝, 朱靖, 赖兴涛. 油套管接箍锰系磷化工艺研究[J]. 钢管, 2011, 40(6): 49-52.
[5] 韩谦逊. 无氟制冷压缩机主部件锰系耐磨磷化工艺的应用及改进[J]. 材料保护, 2005, 38(12): 77-79.
[6] 许艳, 杨栋波. 一种薄壁无缝轴套的研究[J]. 内燃机与配件, 2014, 9: 33-34.
[7] 方金梅. 活塞销的连接配合与故障分析[J]. 农机使用与维修, 2014, 5: 40-41.
[8] 曹阳, 李新立, 沈继洲, 等. 液体表面调整剂的研究[J]. 材料保护, 2004, 37(5): 28-30.
[9] 李万钟, 徐颖强, 孙戬, 等. 滑动摩擦结合面磨合磨损表征方法与影响因素[J]. 中国表面工程, 2017, 30(1): 125-131.

备注/Memo

备注/Memo:
收稿日期： 2020-01-03；修回日期： 2020-03-10
通讯作者： 王莉（1974-），女，副教授，主要研究方向为机械材料、机械基础、化工机械，Email：luzhou_646000@163.com
基金项目： 四川省科技计划项目（2019YFG0064）；泸州市科技项目（2015-S-53（4/5））
更新日期/Last Update: 2020-04-10