[1]付 亮*.气压机入口管线法兰焊缝腐蚀失效分析?/div>[J].电镀与精饰,2023,(6):67-72.[doi:10.3969/j.issn.1001-3849.2023.06.011]
　Fu Liang *.Corrosion failure analysis on the welding line of gas compressor inlet pipeline flange[J].Plating & Finishing,2023,(6):67-72.[doi:10.3969/j.issn.1001-3849.2023.06.011]
点击复制

气压机入口管线法兰焊缝腐蚀失效分析?/div>
()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2023年6
页码:
67-72
栏目:
出版日期:
2023-06-15

文章信息/Info

Title:
Corrosion failure analysis on the welding line of gas compressor inlet pipeline flange
作者:
付 亮*
（吉林工业职业技术学院 智能制造学院，吉林 吉林 132013）
Author(s):
Fu Liang *
（College of Intelligent Manufacturing， Jilin Vocational College of Industry and Technology， Jilin 132013， China）
关键词:
管线法兰; 腐蚀失效; 电化学腐蚀
Keywords:
pipeline flange ;  corrosion failure ;  electrochemical corrosion
分类号:
TG172.2
DOI:
10.3969/j.issn.1001-3849.2023.06.011
文献标志码:
A
摘要:
对失效部位试样的化学成分、金相组织和显微硬度进行研究，通过扫描电镜、能谱分析和 X 射线衍射分析失效工件的腐蚀产物形貌和腐蚀产物组成，选用 S 2- 溶液和 S 2- 、 Cl - 混合溶液对试样进行电化学腐蚀对比实验。结果表明：气压机管线法兰焊缝腐蚀原因是法兰材质不符合标准，法兰与短接管的焊缝属于异种金属不等壁厚焊接，导致焊缝耐腐蚀性下降，在潮湿环境中与硫化物、氯化物等腐蚀介质发生综合作用，焊缝发生快速腐蚀，导致气压机管线法兰焊缝腐蚀、失效。
Abstract:
： The chemical composition ， metallographic structure and microhardness of the failure parts samples were studied and the morphology and composition of corrosion products were analyzed by scanning electron microscope ， energy spectrum analysis and X-ray diffraction test. The electrochemical behavior of the samples in different electrolyte was used to carry out the electrochemical corrosion comparison test ， and the electrolyte was S 2- solution and S 2- ， Cl - mixed solution ， respectively. The results show that the reason for the corrosion of the flange weld is that the material of the flange does not meet the standard ， and the weld of the flange and short pipe is dissimilar materials and unequal wall welding ， which leads to the decrease of the corrosion resistance of the weld. Under the humid environ ment ， the comprehensive interaction of weld with sulfide ， chloride and other corrosive media ， the corrosion of weld occurs rapidly ， which resulting in the corrosion and failure of pneumatic pipeline flange.

参考文献/References:



[1] 胡章枝 , 周学杰 , 吴军 . Q235 碳钢在石化大气环境中初期腐蚀行为 [J]. 装备环境工程 , 2011, 8(3): 30-33.

[2] 杜存臣 , 林慧珠 . 天燃气管道的腐蚀与防护 [J]. 化工装备技术 , 2004, 25(2): 63-65.

[3] Feliu S, Morcillo M, Feliu S J. The prediction of atmospheric corrosion from meteorological and pollution parameters-I. annual corrosion[J]. Corrosion Science, 1993, 34(3): 403-414.

[4] Bhaumik M, Raju K, Arunachellan I, et al. High-performance supercapacitors based on doped polyaniline nanotubes decorated with Ni(OH) 2 nano sponge and on ion-like carbons derived from used car tyres [J]. Electrochimica Acta, 2020, 342: 136111.

[5] 于利宝 , 徐兆东 , 孙海星 , 等 . 剥离 PE 防腐层破损点下钢质管线的阴极保护 [J]. 全面腐蚀控制 , 2016, 30(11): 41-44.

[6] Wang C Y, Qi Z F. Chemical composition and property of atmospheric corrosion resistant steel[J]. Special Steel, 1997, 18(1): 13-19.

备注/Memo

备注/Memo:
收稿日期： 2022-02-07 修回日期： 2022-03-24 * 通信作者： 付亮（ 1983 —），男，硕士研究生，讲师， email ： 289494984@qq.com 基金项目： 2021 年度吉林省职业教育与成人教育教学改革研究课题：产教融合背景下吉林省高职院校双师型师资队伍建设研究（ 2021ZCY108 ）?/html>
更新日期/Last Update: 2023-06-09