[1]黄允芳,蔡锡昌.铝型材立式阳极氧化线“两头色差”问题的研究[J].电镀与精饰,2019,(1):33-36.[doi:10.3969/j.issn.1001?3849.2019.01.007]
　HUANG Yunfang,CAI Xichang.Studies on the Problem of “Color Difference between Two Ends” in the Anodizing Vertical Line for the Aluminum Profile[J].Plating & Finishing,2019,(1):33-36.[doi:10.3969/j.issn.1001?3849.2019.01.007]

点击复制

铝型材立式阳极氧化线“两头色差”问题的研究

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG] 卷: 期数: 2019年1 页码: 33-36 栏目: 出版日期: 2019-01-07

Title:: Studies on the Problem of “Color Difference between Two Ends” in the Anodizing Vertical Line for the Aluminum Profile

作者:: 黄允芳¹; 蔡锡昌²; 1.江苏商贸职业学院，江苏南通 226011； 2.精细化学品集团有限公司，浙江台州318020

Author(s):: HUANG Yunfang¹; CAI Xichang^²; 1. Jiangsu Vocational College of Business, Nantong 226011, China; 2. Fine Chemicals Group Ltd., Taizhou 318020, China

关键词:: 铝型材; 立式线; 阳极氧化; 电解着色

Keywords:: aluminum profile; vertical line; anodic oxidation; electrolytic coloring

分类号:: TQ153.6

DOI:: 10.3969/j.issn.1001?3849.2019.01.007

文献标志码:: A

摘要:: 铝型材立式阳极氧化线以高效和生产成本较低两大优点，越来越得到大型铝型材企业的青睐。本文针对铝型材立式阳极氧化线，在电解着色中更易出现“两头色差”的问题进行了深入剖析，首先分析了具有共性的铝型材卧式阳极氧化线出现“两头色差”问题的原因，之后深入分析了立式阳极氧化线的几种附加原因，最后根据生产实践经验，提出了相应的改进与防止措施。相关研究分析结果对解决铝型材立式阳极氧化线“两头色差”问题具有一定的指导意义。

Abstract:: Vertical anodizing line for aluminium profiles is becoming more and more popular in large-scale aluminium profiles enterprises because of its high efficiency and low production cost. In this paper, the problem of "color difference between two ends", which occurs more easily in electrolytic coloring of vertical anodized aluminum profiles, was analyzed. Firstly, the common causes of "color difference between two ends" in horizontal anodizing line for aluminum profiles were analyzed, and then several additional causes for vertical anodizing line were analyzed in depth. Finally, the corresponding improvement and prevention measures were put forward according to the production practice experience. Relevant research and analysis results provide certain significant reference for solving the problem of "color difference between two ends" in vertical anodizing line for aluminum profiles.

参考文献/References:

［1］蔡锡昌，等. 6063铝合金基材质量对阳极氧化和电解着色的影响[C]//Lw 2016第六届铝加工技术（国际）论坛文集, 杭州: Lw铝业加工技术中心, 2016: 857.
［2］朱祖芳. 铝合金阳极氧化与表面处理技术（第2版）. [M]. 北京: 化学工业出版社, 2010: 125.
［3］唐业勤. 铝型材立式氧化表面处理在高效、节能、环保方面我应用与探讨（二）[C]//第8第六届广东铝加工技术（国际）研讨会论文集, 广东: 广东省有色金属学会铝加工专业委员会, 2017: 748.
［4］李营祥. 单镍盐住化法生产深古铜的工艺技术研究[J]. 铝型材专刊, 2018, 108(5): 31-33.

相似文献/References:

[1]黄允芳*,蔡锡昌.铝型材电解着色工艺向环保型工艺转换的研究[J].电镀与精饰,2019,(12):10.[doi:10.3969/j.issn.1001-3849.2019.12.003]
　HUANG Yunfang*,CAI Xichang.Studies on Environmentally Friendly Technology Transformation of Electrolytic Coloring for Al Profile[J].Plating & Finishing,2019,(1):10.[doi:10.3969/j.issn.1001-3849.2019.12.003]
[2]黄允芳*,蔡锡昌.二次电解着色法防紫铜色铝型材褪色工艺[J].电镀与精饰,2021,(10):55.[doi:10.3969/j.issn.1001-3849.2021.10.011]
　HUANG Yunfang*,CAI Xichang.Process of the Seconday Electrolytic Coloring Method to Prevent Copper Color Discoloration on Al Profile[J].Plating & Finishing,2021,(1):55.[doi:10.3969/j.issn.1001-3849.2021.10.011]

备注/Memo

收稿日期： 2018-09-29
修回日期： 2018-10-18

更新日期/Last Update: 2019-01-16