SU Zhan,YU Jinshan,DONG Hao,et al.Preparation Process of Ni ( OH ) 2 Positive Electrode Materials by Solvothermal Method and Orthogonal Test[J].Plating & Finishing,2022,(6):47-51.
正交试验法优化Ni(OH)2超电材料溶剂热法制备工艺
- Title:
- Preparation Process of Ni ( OH ) 2 Positive Electrode Materials by Solvothermal Method and Orthogonal Test
- Keywords:
- supercapacitor; ??i (OH )2 ; solvothermal method ; orthogonal experiment
- 分类号:
- TQ152
- 文献标志码:
- A
- 摘要:
- 采用溶剂热法并设计正交试验,以 NiCl 2 ·6H 2 O 为原料在不同条件下制备得到了 9 组 Ni( OH ) 2 电极材料,对其进行了物理表征和电化学性能测试。选取 3 A?span>· g -1 下材料的质量比容量值为评价指标,确定了最佳制备条件:水热温度 180 ℃ ,反应时间 10 h ,加入 200 mg 聚苯乙烯磺酸钠( PSS ),体积比为 1 ∶ 1 的水 / 乙二醇溶液作为溶剂。
- Abstract:
- : By solvothermal method and orthogonal experiment design , the nine Ni ( OH ) 2 electrode materials were prepared from NiCl 2 ·6H 2 O. The physical characterization and electrochemical tests were carried out. The mass specific capacity of the material under 3 A?span>· g -1 was selected as the evaluation index , and the optimal preparation conditions were determined as follows : the hydrothermal temperature was 180 ℃ , the hydrothermal time was 10 h , 200 mg poly sodium styrene sulfonate ( PSS ) was added , and the solvent was 1 ∶ 1 water/glycol solution by volume.
参考文献/References:
[1] He D, Wan J, Liu G, et al. Design and construction of hierarchical α -Co(OH) 2 -coated ultra-thin ZnO flower nanostructures on nickel foam for high performance supercapacitors[J]. Journal of Alloys and Compounds, 2020, 838: 155556.
[2] González A, Goikolea E, Barrena J A, et al. Review on supercapacitors: Technologies and materials[J]. Renewable and Sustainable Energy Reviews, 2016, 58: 1189-1206.
[3] K?tz R, Carlen M. Principles and applications of electrochemical capacitors[J]. Electrochimica Acta, 2000, 45(15): 2483-2498.
[4] Chen Y, Zheng C G. New precursors derived activated carbon and graphene for aqueous supercapacitors with unequal electrode capacitances[J]. Acta Physico-Chimica Sinica, 2020, 36(2): 1904025.
[5] Patrice Simon, Yury Gogotsi. Materials for electrochemical capacitors.[J].Nature Materials, 2008, 7(11): 845-854.
[6] Wang G, Zhang L, Zhang J . A review of electrode materials for electrochemical supercapacitors[J]. Chemical Society Reviews, 2012, 41(2):797-828.
[7] Lokhande C D, Dubal D P, Joo O. Metal oxide thin film based supercapacitors[J]. Current Applied Physics, 2011, 11(3): 255-270.
[8] Wang Y, Guo J, Wang T, et al. Mesoporous transition metal oxides for supercapacitors[J]. Nanomaterials, 2015, 5(4): 1667-1689.
[9] An C, Zhang Y, Guo H, et al. Metal oxide-based supercapacitors: Progress and prospectives[J]. Nanoscale advances, 2019, 1(12): 4644-4658.
[10] Mohd Abdah M A A, Azman N H N, Kulandaivalu S, et al. Review of the use of transition-metal-oxide and conducting polymer-based fibres for high-performance supercapacitors[J]. Materials & Design, 2020, 186: 108199.
[11] Han Y, Dai L. Conducting polymers for flexible supercapacitors[J]. Macromolecular Chemistry and Physics, 2019, 220(3): 1800355.
[12] Li L, Xia G, Yu W, et al. Low-energy hydrothermal fabrication of α -Ni(OH) 2 nanosheet arrays as efficient electrodes for sustainable supercapacitors[J]. Sustainable Materials and Technologies, 2019, 20: e85.
[13] Hou C, Lang X, Wen Z, et al. Single-crystalline Ni(OH) 2 nanosheets vertically aligned on a three-dimensional nanoporous metal for high-performance asymmetric supercapacitors[J]. Journal of Materials Chemistry A, 2015, 3(46): 23412-23419.
[14] Wang Y, Gai S, Li C, et al. Controlled synthesis and enhanced supercapacitor performance of uniform pompon-like β -Ni(OH) 2 hollow microspheres[J]. Electrochimica Acta, 2013, 90: 673-681.
相似文献/References:
[1]张永霞,王 玫,方 华*,等.Co3O4/碳纳米管复合膜的超级电容器性能[J].电镀与精饰,2020,(2):1.[doi:10.3969/j.issn.1001-3849.2020.02.001]
ZHANG Yongxia,WANG Mei,FANG Hua*,et al.Co3O4/Carbon Nanotube Composite Film for Supercapacitor and Its Performances[J].Plating & Finishing,2020,(6):1.[doi:10.3969/j.issn.1001-3849.2020.02.001]
[2]于金山,苏 展,裴 锋,等.超级电容器寿命预测的研究进展[J].电镀与精饰,2020,(12):26.[doi:10.3969/j.issn.1001-3849.2020.12.0060]
YU Jinshan,SU Zhan,PEI Feng,et al.Research Progress on Life Prediction of Supercapacitors[J].Plating & Finishing,2020,(6):26.[doi:10.3969/j.issn.1001-3849.2020.12.0060]
[3]苏展,于金山,裴锋,等.溶剂热法制备形貌可控的NiCo2O4超电材料及其性能研究[J].电镀与精饰,2021,(12):1.[doi:10.3969/j.issn.1001-3849.2021.12.001]
SU Zhan,YU Jinshan,PEI Feng,et al.Preparation of NiCo2O4 Supercapacitor Electrode Materials with Controllable Morphology by Solvent-Thermal Method and Research of Their Properties[J].Plating & Finishing,2021,(6):1.[doi:10.3969/j.issn.1001-3849.2021.12.001]
[4]苏展,于金山,董 浩,等.花状Ni(OH)2的制备及其电化学性能研究[J].电镀与精饰,2022,(2):16.[doi:10.3969/j.issn.1001-3849.2022.02.004]
SU Zhan,YU Jinshan,DONG Hao,et al.Preparation and Electrochemical Properties of Floral Ni ( OH ) 2[J].Plating & Finishing,2022,(6):16.[doi:10.3969/j.issn.1001-3849.2022.02.004]
[5]巩鹏妮,弓巧娟 *,梁云霞,等.镍钴硫化物、石墨烯与聚苯胺复合材料在超级电容器中的应用研究进展[J].电镀与精饰,2023,(3):90.[doi:10.3969/j.issn.1001-3849.2023.03.013]
Gong Pengni,Gong Qiaojuan *,Liang Yunxia,et al.Research progress of Ni-Co sulfide graphene and polyaniline composites applied in supercapacitors[J].Plating & Finishing,2023,(6):90.[doi:10.3969/j.issn.1001-3849.2023.03.013]
备注/Memo
收稿日期: 2021-04-27 修回日期: 2021-06-17 作者简介: 苏展( 1986 —),男,本科,高级工程师, email : 504020249@qq.com 通信作者: 王宏智( 1973 —),男,博士,副教授, email : wanghz@tju.edu.cn?/html>