[1]袁军平*,金莉莉,郭礼淳,等.防指纹膜技术在18K金合金表面的应用探讨[J].电镀与精饰,2022,(3):40-46.[doi:10.3969/j.issn.1001-3849.2022.03.008]
　YUAN Junping *,JIN Lili,GUO Lizhun,et al.Discussion of the Application of Anti-Fingerprint Coating Technology on Gold Alloy Surface for Jewelry[J].Plating & Finishing,2022,(3):40-46.[doi:10.3969/j.issn.1001-3849.2022.03.008]
点击复制

防指纹膜技术在18K金合金表面的应用探讨()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2022年3
页码:
40-46
栏目:
出版日期:
2022-03-01

文章信息/Info

Title:
Discussion of the Application of Anti-Fingerprint Coating Technology on Gold Alloy Surface for Jewelry
作者:
袁军平1*; 金莉莉1; 郭礼淳2; 王 昶1; 梁健辉3; 陶震东3
（1.广州番禺职业技术学院珠宝学院，广东 广州 511483； 2.深圳昊翀珠宝科技有限公司，广东 深圳 518000； 3.国家珠宝检测中心（广东）有限责任公司，广东 广州 511483）
Author(s):
YUAN Junping 1* ;  JIN Lili 1 ;  GUO Lizhun 2 ;  WANG Chang 1 ;  LIANG Jianhui 3;  TAO Zhendong 3
( 1.Jewelry Institute of Guangzhou Panyu Polytechnic Guangzhou 511483 China 2.Shenzhen Haochong Jewelry Technology Co. Ltd Shenzhen 518000 China 3.Guangzhou Laboratory of National Gemstone Testing Center Guangzhou 511483 China )
关键词:
首饰; 真空蒸镀; 防指纹膜; 接触角; 膜层性能
Keywords:
jewelry;  vacuum evaporation depositing;  anti-fingerprint coating;  contact angle;  coating performance
分类号:
TQ153.12
DOI:
10.3969/j.issn.1001-3849.2022.03.008
文献标志码:
Ａ
摘要:
首饰表面在佩戴使用中常易黏附指纹、油污等，影响其外观效果。本文采用 18K 金合金首饰材料为基底，采用反应磁控溅射工艺在其表面沉积二氧化硅底膜，再用真空蒸镀法沉积有机氟化物防指纹膜。采用 X 射线荧光光谱分析仪检测基材的成色，采用接触角测试仪、橡皮摩擦试验仪、激光共聚焦显微镜、原子力显微镜、测色仪、耐变黄老化试验箱、人工汗液浸泡试验槽等分别检测了膜层的疏水（油）性能、表面形貌及耐摩擦性能、颜色及耐蚀性等。结果表明，在合适的工艺参数下，防指纹膜层的平均水接触角可达 115° ，油接触角可达 110° ，有优良的抗脏污效果和顺滑触感。经摩擦、腐蚀、老化等试验后，膜层的疏水自洁性能依然良好。防指纹膜不会改变首饰贵金属成色，但会对 XRF 检测成色的精度以及首饰外观颜色产生影响，且影响程度与镀膜工艺参数相关。因此，生产中需要从防指纹性能、成色检测保证和外观效果等方面综合权衡来优化镀膜工艺。
Abstract:
： Jewelry surface is prone to adhere fingerprint and greasy dirt when it is worn ， which diminishes its appearance. In this paper ， 18K gold alloy for jewelry was used as the substrate material ， and SiO 2 bottom film was deposited on the substrate by reactive magnetron sputtering technology ， and anti-fingerprint coating of organic fluoride was further deposited by vacuum evaporation process. The fineness of the base material was tested with X ray fluorescence spectrometer ， and the coating ’ s performances ， including the hydrophobicity ， lipophobicity ， topography ， abrasion resistance ， color and corrosion resistance ， were tested with contact angle tester ， rubber friction tester ， Laser Scanning Confocal Microscope ， spectrophotometer ， aging resistance test chamber ， artificial sweat soaking test chamber ， etc. The results show that under the suitable process conditions ， the average contact angle of the anti- fingerprint coating for water and oil is no less than 115° and 110° respectively ， which shows excellent smudginess resistance and smooth feeling. After the abrasion test ， aging test and corrosion test ， the coating still keeps good hydrophobicity and self-cleaning property. The anti-fingerprint film does not change the precious metal fineness ， but it will interfere with the nondestructive XRF testing result and affect the jewelry appearance color ， while the influence degree is related to the coating process parameters. Therefore ， to determine the optimized coating process ， it is necessary to balance the anti-fingerprint performance ， the guarantee of fineness detection and the appearance effect.

参考文献/References:



[1] 袁军平 , 吴海超 , 卢焕洵 , 等 . 成型和表面处理工艺对 316L 不锈钢镍释放率的影响 [J]. 特殊钢 , 2015,36(5): 59-63.

[2] 刘江斌 . 黄金首饰的变色和清洗 [J]. 黄金 , 1999, 20(1): 54.

[3] 袁军平 , 王昶 . 饰用贵金属材料 [M]. 武汉 : 中国地质大学出版社 , 2020.

[4] Barthlott W, Neinhuis C. Purity of the sacred lotus or escape from contamination in biological surfaces[J]. Planta, 1997, 202(1):1-8.

[5] 李天平 . 仿生超疏水表面的制备及其海水腐蚀防护性能研究 [D]. 北京 : 中国科学院大学海洋研究所 , 2017.

[6] 肖成龙 , 梁世雍 , 于兆勤 . 可控阵列微柱超疏水表面实验研究 [J]. 电镀与精饰 , 2020, 42(7): 27-32.

[7] 蒋帆 , 赵越 , 胡吉明 . 超疏水表面在金属防护中应用的研究进展 [J]. 表面技术 , 2020,49(2): 109-123.

[8] 李国军 , 李剑飞 , 李国栋 . 玻璃上 AR/AF 膜的技术研发 [C]// 广东省真空学会 : 珠三角光电产业与真空科技创新论坛暨 2016 年广东省真空学会学术年会论文集 . 广州 , 2016: 72-76.

[9] Samuel C, Meez I, Peter M, et al. Fingerprint composition and aging: A literature review[J]. Science & Justice, 2015, 55(4): 219-238.

[10] 龙梦影 . 基于聚二甲基硅氧烷的仿生超疏水材料的制备及其性能 [D]. 广州 : 华南理工大学 , 2019.

[11] 宋圆 . 新型氟硅材料的制备及疏水疏油性能研究 [D]. 武汉 : 湖北大学 , 2012.

[12] Zhang H, Li D Y, Hu Y M, et al. Progress of Surfaces with Stimuli-Responsive Wettability[J]. Material Sciences, 2018,8(5): 471-481.

[13] 张静 . 透明耐磨超疏水膜层的制备及其界面结构的控制 [D]. 厦门 : 厦门大学 , 2019.

[14] 汉斯·吕斯著 , 王聪 , 孙莹 , 王蕾译 . 固态表面界面与薄膜 ( 第 6 版 )[M]. 北京 : 高等教育出版社 , 2019.

[15] Jiang Q, Lu H M. Size dependent interface energy and its applications[J]. Surface Science Reports, 2008, 63: 427-464.

[16] 李桂双 , 陈燕兰 , 袁军平 , 等 . 改性足金材料的耐蚀性能研究 [J]. 黄金 , 2015,36(3) : 6-9.

备注/Memo

备注/Memo:
收稿日期： 2021-04-12 修回日期： 2021-08-27 * 通 信作者 ： 袁军平（ 1969 —），男， 研究生（博士）， 教授级高工， E-mail ： yuanjp@gzpyp.edu.cn 基金项目： 广东省高职院校珠宝首饰产教融合创新平台（ 2021CJPT001 ）， 广州市高等职业教育双师工作室项目（穗教高教［ 2019 ］ 15 号）
更新日期/Last Update: 2022-03-11