CHENG Baogai,LI Baozeng,XIE Meifang,et al.Influence of Sandblasting on Morphology and Adhesion of Water-Borne Film[J].Plating & Finishing,2019,(7):31-35.[doi:10.3969/j.issn.1001-3849.2019.07.007]
喷砂对水性涂装漆膜形貌与性能的影响
- Title:
- Influence of Sandblasting on Morphology and Adhesion of Water-Borne Film
- Keywords:
- water-based coating; sandblasting; adhesion; corrosion resistance
- 文献标志码:
- A
- 摘要:
- 户外服役高压开关漆膜破坏后采用硅烷处理加水性涂料进行现场维修存在附着力不良的现象。本文研究了喷砂前处理+水性涂料在维修过程中的施工工艺，并采用测厚仪、拉拔仪与盐雾试验箱测试其生成膜层的厚度、附着力与耐蚀性能。结果表明，最佳的前处理工艺为喷嘴直径0.6 mm，压力0.5 MPa，距离为600 mm，走枪速度为0.6 m/s，石英砂粒径为80～100目。制备水性涂料涂层，附着力均大于5 MPa，中性盐雾试验1000 h无任何的起泡、剥落、生锈与开裂现象，可以满足生产的技术要求。
- Abstract:
- When the film of high-voltage switch in outdoor service is damaged, adhesion is poor after on-site repair with silane treatment and waterborne paint. In this paper, the construction technology of sand blasting pretreatment and waterborne coatings in maintenance process were studied. Thickness, adhesion and corrosion resistance of the films were tested by thickness gauge, drawing instrument and salt spray test box. The results showed that the optimum pretreatment process was as follows: nozzle diameter of 0.6 mm, pressure of 0.5 MPa, distance of 600 mm, shooting speed of 0.6 m/s and quartz sand with particle size of 80-100 mesh. The adhesion of the prepared waterborne coatings was greater than 5 MPa, there was no foaming, peeling, rusting and cracking after neutral salt spray test for 1000 h, which can meet the technical requirements of production.
参考文献/References:
[1] 胡中, 许飞, 庄振宇, 等. 基于自增稠型羟基丙烯酸乳液的水性珠光涂料的制备[J]. 涂料工业, 2017, 47(5): 11-16.
[2] 曾宪光, 龚敏, 刘朝辉, 等. 水性聚氨酯涂料的研究现状[J]. 电镀与涂饰, 2018, 37: 1060-1067.
[3] 张爱黎, 田坤, 常彩彩, 等. 改性环氧丙烯酸水性防腐涂料制备研究[J]. 电镀与精饰, 2015, 37(11): 15-19.
[4] 李卓麟, 梁亮, 江建东, 等. 水性仿金属塑料漆的研制[J]. 电镀与涂饰, 2016, 35(6): 295-299.
[5] 赵欣. 涂装前处理[J]. 电镀与精饰, 2011, 33(9): 36-38.
[6] 李红艳, 李增权, 徐明磊. 农用机械便利型涂装修复技术[J]. 电镀与精饰, 2018, 40(12): 33-37.
[7] 唐春华. 现代磷化工艺实践第九部分—涂装预处理工艺[J]. 电镀与涂饰, 2016, 35(6): 98-107.
[8] 王传忠, 张磊, 曹志刚, 等. 浅析表面粗糙度对涂装的影响[J]. 现代涂料与涂装, 2011, 14(5): 66-67.
相似文献/References:
[1]孙海静,徐佳新,姚宇煊,等.水性有机硅改性环氧丙烯酸树脂的制备及性能研究[J].电镀与精饰,2020,(3):18.[doi:10.3969/j.issn.1001-3849.2020.03.004]
SUN Haijing,XU Jiaxin,YAO Yuxuan,et al.Preparation and Study on Water-based Silicone Modified Epoxy-Acrylate Resin[J].Plating & Finishing,2020,(7):18.[doi:10.3969/j.issn.1001-3849.2020.03.004]
[2]王朝琳*,宋斌,刘娟,等.直升机桨叶包片胶接前激光毛化处理的有效性研究[J].电镀与精饰,2021,(12):29.[doi:10.3969/j.issn.1001-3849.2021.12.006]
WANG Chaolin*,SONG Bin,LIU Juan,et al.The Effectiveness of Laser Texturing Technology in Surface Treatment of the Bonding Quality of Helicopter Slurry Pack[J].Plating & Finishing,2021,(7):29.[doi:10.3969/j.issn.1001-3849.2021.12.006]
[3]赵金龙*,张华云. 喷砂对45#钢表面耐蚀性的影响 [J].电镀与精饰,2023,(3):95.[doi:10.3969/j.issn.1001-3849.2023.03.014]
Zhao Jinlong*,Zhang Huayun.Effect of sandblasting on corrosion resistance of 45 # steel surface[J].Plating & Finishing,2023,(7):95.[doi:10.3969/j.issn.1001-3849.2023.03.014]
[4]陈婧*.粗糙度对水性涂料涂装膜层结合力的影响?/div>[J].电镀与精饰,2022,(12):25.[doi:10.3969/j.issn.1001-3849.2022.12.004]
CHEN Jing *.Effect of Roughness on Adhesion of Waterborne Coatings[J].Plating & Finishing,2022,(7):25.[doi:10.3969/j.issn.1001-3849.2022.12.004]
备注/Memo
收稿日期： 2019-01-21；修回日期： 2019-03-05
基金项目： 国家电网有限公司总部科技项目(SGSHDK00SPJS1800621)