WANG Yanwei.Influence of Filling Process on Color Difference of Aluminum Alloy Shell after Chromic Acid Anodization[J].Plating & Finishing,2019,(7):40-43.[doi:10.3969/j.issn.1001-3849.2019.07.009]
填充工序对铝合金壳体零件铬酸阳极化色差的影响
- Title:
- Influence of Filling Process on Color Difference of Aluminum Alloy Shell after Chromic Acid Anodization
- Keywords:
- aluminum alloy; chromic acid anodization; filling; color difference
- 文献标志码:
- A
- 摘要:
- 本文通过梳理铝合金零件铬酸阳极化工艺流程,采用故障树图对零件外观出现色差的原因进行了分析讨论。结果表明,同类材料、同种加工表面状态的铝合金零件经过铬酸阳极化后,互相之间的色差根源在于后处理填充槽液浓度的不合理。通过规范填充槽液管理,可有效消除铬酸阳极化膜层存在的色差问题。
- Abstract:
- In this paper, the process flow of chromic acid anodization for aluminium alloy parts was carded, and the cause of color difference in the appearance of parts was analyzed and discussed by using fault tree diagram. The results showed that the color difference between aluminium alloy parts with the same material and the same machined surface state after chromic acid anodization was due to the unreasonable concentration of filling bath in the post-processing. The color difference of chromic acid anodized film layer could be eliminated by the standardized management of filling tank liquor. The problem of color difference in chromic acid anodic film could be effectively eliminated by standardizing the management of filling bath liquid.
参考文献/References:
[1] 穆强, 于文刚, 卢刚. 铝及铝合金的铬酸阳极化[J]. 山东化工, 2016, 45(5): 26-28.
[2] 郑瑞庭. 铝及铝合金的铬酸阳极化[J]. 电镀与精饰, 2003, 25(1): 13-15.
[3] Shulman G P, Bauman A J. Organic acid sealants for anodized aluminum a new method for corrosion protection[J]. Metal Fishing, 1995, 93(7): 16-21.
[4] 马海泉, 姜涛, 张兵, 等. 计量器壳体铬酸阳极化表面色差原因分析[J]. 失效分析与预防, 2009, 4(4): 238-241.
[5] 杨景伟, 赵永岗, 孙杰, 等. 铝合金铬酸阳极氧化后表面缺陷分析[J]. 表面技术, 2014, 43(2): 72-74.
[6] Patermarakis G, Papandreadis N. Effect of the structure of porous anodic Al2O3 films on the mechanism of their hydration and pore closure during hydrothermal treatment[J]. Electrochemica Acta, 1993, 38(10): 1413-1416.
[7] 郑瑞庭. 铝及铝合金氧化工艺问题[J]. 腐蚀与防护, 2000, 21(12): 568-577.
[8] 李婷. 铝叶片铬酸阳极化后封闭产生缺陷分析[J]. 中国新技术新产品, 2012, (23): 108-109.
[9] 程红霞, 罗静, 易茂生, 等. 铝合金铬酸阳极化膜的低铬封孔工艺研究[J]. 材料保护, 2004, 37(7): 32-33.
[10] 张允诚, 胡如南, 向荣, 等. 电镀手册(第4版)[M]. 北京: 国防工业出版社, 2011: 676-681.
相似文献/References:
[1]黄碧芳*,李远会,王 丽,等.铝合金磷钼酸亚铁转化体系工艺研究[J].电镀与精饰,2019,(9):29.[doi:10.3969/j.issn.1001-3849.2019.09.006]
HUANG Bifang*,LI Yuanhui,WANG Li,et al.Study on the Conversion Process of Ferrous Phosphomolybdate on Aluminum Alloy[J].Plating & Finishing,2019,(7):29.[doi:10.3969/j.issn.1001-3849.2019.09.006]
[2]元 泉,邱 媛*,刘 洋,等.铝合金漆层与氧化层激光清洗应用研究[J].电镀与精饰,2019,(12):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
YUAN Quan,QIU Yuan#,LIU Yang,et al.Research on Laser Cleaning Application for Coating and Oxide Layer of Aluminum Alloy[J].Plating & Finishing,2019,(7):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
[3]王立亮*,颜杰红,李 森.铬酸阳极化中温去离子水封闭工艺研究[J].电镀与精饰,2020,(6):30.[doi:10.3969/j.issn.1001-3849.2020.06.0070]
WANG Liliang*,YAN Jiehong,LI Sen.Study on Medium Temperature Deionized Water Seal of Chromic Acid Anodizing[J].Plating & Finishing,2020,(7):30.[doi:10.3969/j.issn.1001-3849.2020.06.0070]
[4]季 伟,孟繁东,潘科宇,等.铝合金表面油污清洗剂的制备及其腐蚀性研究[J].电镀与精饰,2021,(2):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
JI Wei,MENG Fandong,PAN Keyu,et al.季 伟1,孟繁东1,潘科宇1,王文军1,潘明华1,韩怡秋2,邵明亮2,刘 东3,周 勇3*[J].Plating & Finishing,2021,(7):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
[5]张子聪,郝建军*,赵荣兴.铝合金复合石墨烯薄膜的制备及腐蚀性能研究[J].电镀与精饰,2021,(7):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
ZHANG Zicong,HAO Jianjun*,ZHAO Rongxing.Study on Preparation and Corrosion Performance of Aluminum Alloy Composite Graphene Film[J].Plating & Finishing,2021,(7):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
[6]刘奋照*.几种铝合金材料在汽车防冻液中的腐蚀行为[J].电镀与精饰,2021,(9):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
LIU Fenzhao*.Corrosion Behavior of Several Aluminum Alloy in Automobile Antifreeze[J].Plating & Finishing,2021,(7):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
[7]刘 静,马小昭,王帅星.绝缘保护用铬酸阳极氧化工艺研究[J].电镀与精饰,2022,(6):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
LIU Jing,MA Xiaozhao,WANG Shuaixing.Research on Chromic Acid Anodizing Technique for Insulation Protection[J].Plating & Finishing,2022,(7):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
[8]李志强,魏红阳,陈东初*,等.电源参数对铝合金表面复合氧化膜的多彩电解着色的影响规律研究[J].电镀与精饰,2022,(6):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
LI Zhiqiang,WEI Hongyang,CHEN Dongchu*,et al.Effects of Power Parameters on Electrolytic Colouring of Colorful Composite Oxide Film on Aluminum Alloy Surface[J].Plating & Finishing,2022,(7):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
[9]李廷取 *,刘祥玲,刘文异. 不同占空比对6061铝合金微弧氧化着色及性能的影响研究 [J].电镀与精饰,2022,(9):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
LI Tingqu *,LIU Xiangling,LIU Wenyi.Study on Microarc Oxidation Coloring and Properties of 6061 Aluminum Alloy with Different Duty Ratios[J].Plating & Finishing,2022,(7):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
[10]刘巧娣*,邓国军. 硫酸阳极化膜层出现白色粉末问题原因分析 [J].电镀与精饰,2022,(10):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
LIU Qiaodi*,DENG Guojun.Cause Analysis of White Powder in Sulfuric Acid Anodized Film[J].Plating & Finishing,2022,(7):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
备注/Memo
收稿日期: 2018-11-30;修回日期: 2019-03-09