WANG Hong*,LIU Jichao.Effect of Sealing Treatment on Corrosion Resistance of Electroless Ni-Co-P Coating on NdFeB Permanent Magnetic Material[J].Plating & Finishing,2020,(11):5-9.[doi:10.3969/j.issn.1001-3849.2020.11.0020]
封孔处理对钕铁硼永磁材料化学镀Ni-Zn-P镀层耐蚀性的影响
- Title:
- Effect of Sealing Treatment on Corrosion Resistance of Electroless Ni-Co-P Coating on NdFeB Permanent Magnetic Material
- 关键词:
- 封孔处理; 化学镀Ni-Zn-P镀层; 钕铁硼永磁材料; 耐蚀性
- Keywords:
- sealing treatment electroless Ni-Zn-P coating NdFeB permanent magnet material corrosion resistance
- 文献标志码:
- A
- 摘要:
- 在钕铁硼永磁材料表面化学镀Ni-Zn-P镀层，为了进一步提高镀层耐蚀性，镀后进行封孔处理。在封孔过程中，采用不同方式搅拌封孔液，表征了封孔处理前后镀层的表面形貌和孔隙率，并测量了封孔处理前后镀层的极化曲线和阻抗谱。结果表明：采用磁力和超声波搅拌封孔液，封孔处理后镀层与未封孔镀层相比表面的微孔数量明显减少，孔隙率降低，对腐蚀介质的敏感性和腐蚀倾向性减弱，耐蚀性明显提高。相比之下，在封孔过程中采用超声波搅拌封孔液能实现更好的封孔效果，封孔处理后镀层的孔隙率最低，约为1.04%，其耐蚀性更好。
- Abstract:
- Electroless Ni-Zn-P coating was deposited on the surface of NdFeB permanent magnet material, and sealing treatment was carried out in order to further improve the corrosion resistance of the coating. Different methods were used to stir the sealing solution in the process of coating sealing. The surface morphology and porosity of the coating before and after sealing treatment were characterized, and the polarization curve and impedance spectrum of the coating before and after sealing treatment were measured. The results showed that when the sealing solution was stirred by magnetic force and ultrasonic wave, the number of micropores on the surface of the coating and the porosity of the coating after sealing treatment were significantly reduced compared with that of the coating before sealing treatment. The sensitivity and corrosion tendency to corrosive medium were weakened, indicating that the corrosion resistance of the coating after sealing treatment was obviously improved. In contrast, using ultrasonic to stir the sealing solution can achieve better sealing treatment effect, the coating after sealing treatment possessed the lowest porosity about 1.04% and much better corrosion resistance.
参考文献/References:
[1] 宋振纶, 李卫. 钕铁硼永磁材料表面防护技术:特点·应用·问题[J]. 磁性材料及器件, 2008, 39（1）:1-6.
Song Z L, Li W. Protection technology of NdFeB magnet materials:characteristics, applications and problems[J]. Journal of Magnetic Materials and Devices, 2008, 39（1）:1-6（in Chinese）.
[2] 张鹏杰. 用于烧结钕铁硼（NdFeB）表面防护的新型涂层的制备及其性能研究[D]. 合肥:合肥工业大学, 2016.
[3] Cao R, Zhu L Q, Chen H N, et al. The Influence of alumina-silica sol addition on microstructure and protective properties of electrodeposited zinc coatings on NdFeB magnet[J]. Journal of The Electrochemical Society, 2018, 165（2）:D64-D75.
[4] 刘伟, 侯进. 钕铁硼电镀技术生产现状与展望[J]. 电镀与精饰, 2012, 34（4）:20-25.
Liu W, Hou J. Production status and prospect of NdFeB magnet electroplating[J]. Plating & Finishing, 2012, 34（4）:20-25（in Chinese）.
[5] Chen H M, Wang Q, Dong H B, et al. Electroless plating of Ni-P-W coatings containing scattered Nb2O5 on sintered NdFeB substrate[J]. Materials Research, 2015, 18（5）:1089-1096.
[6] Chen E, Peng K, Zhu J J, et al. Corrosion resistance of sintered NdFeB magnets with various surface coatings[J]. Applied Mechanics and Materials, 2014, 492:263-267.
[7] 卢旭东, 邵忠财. 化学镀Ni-P合金镀层孔隙率的影响因素[J]. 电镀与精饰, 2007, 29（6）:1-3.
Lu X D, Shao Z C. Factors affecting porosity of the electroless Ni-P alloy coating[J]. Plating & Finishing, 2007, 29（6）:1-3（in Chinese）.
[8] 张峻巍, 苏建铭, 王一雍, 等. 超声波对Ni-Co-Al2O3镀层性能的影响[J]. 有色金属（冶炼部分）, 2015, 4:59-62.
Zhang J W, Su J M, Wang Y Y, et al. Effect of ultrasonic on property of Ni-Co-Al2O3 coatings[J]. Nonferrous Metals（Extractive Metallurgy）, 2015, 4:59-62（in Chinese）.
[9] Graves J E, Sugden M, Litchfield R E, et al. Ultrasound assisted dispersal of a copper nanopowder for electroless copper activation[J]. Ultrasonics Sonochemistry, 2016, 29:428-438.
[10] 罗婵媛, 纪秀林, 李泽. 电沉积非晶态Fe-Co-Ni-P镀层的制备及性能[J]. 中国表面工程, 2017, 30（2）:92-97.
Luo C Y, Ji X L, Li Z. Preparation and properties of electrodeposited amorphous Fe-Co-Ni-P coatings[J]. China Surface Engineering, 2017, 30（2）:92-97（in Chinese）.
相似文献/References:
[1]成张佳宁,黄坤坤.建筑铝合金表面制备耐久性超疏水阳极氧化膜[J].电镀与精饰,2022,(6):16.[doi:10.3969/j.issn.1001-3849.2022.06.004]
CHENG Zhangjianing,HUANG Kunkun.Preparation of Durable Super-Hydrophobic Anodic Oxide Film on Aluminum Alloy for Construction[J].Plating & Finishing,2022,(11):16.[doi:10.3969/j.issn.1001-3849.2022.06.004]
备注/Memo
收稿日期： 2020-05-27；修回日期： 2020-07-04
通信作者： 王宏，wanghong0607@126.com
基金项目： 河北省青年