BAI Yuwei*,CHEN Rui.白玉伟*，陈锐[J].Plating & Finishing,2021,(3):1-5.[doi:10.3969/j.issn.1001-3849.2021.03.001]
封闭处理对工程车用件磷化膜形貌和耐蚀性的影响
- Title:
- 白玉伟*，陈锐
- 文献标志码:
- A
- 摘要:
- 使用以硅酸钠为主成分的封闭液对工程车用件表面的锌钙系磷化膜进行封闭处理。选取封闭液中硅酸钠的浓度、封闭时间和封闭液温度作为影响因素，并以电荷转移电阻和耐硫酸铜腐蚀时间作为评价指标，通过单因素实验考察了封闭处理工艺条件对封闭处理后的磷化膜耐蚀性的影响。结果表明：硅酸钠的浓度和封闭时间对封闭处理后的磷化膜耐蚀性都有较明显的影响，适当增加硅酸钠的浓度以及延长封闭时间有助于改善磷化膜的耐蚀性，而封闭液温度对封闭处理后的磷化膜耐蚀性的影响程度相对较小。当硅酸钠的浓度为12 g/L、封闭时间为16 min、封闭液温度约75 ℃，封闭处理后的磷化膜表面趋于平整，致密度较高，其耐蚀性较封闭处理前的磷化膜有明显改善。封闭处理可以进一步增强锌钙系磷化膜对基体的保护作用。
- Abstract:
- The zinc-calcium phosphating film on the surface of engineering vehicle parts was sealing treated with the sealing solution with sodium silicate as the main component. The concentration of sodium silicate in sealing solution, sealing time and temperature of sealing solution were selected as the influencing factors, and the charge transfer resistance and corrosion resistance time of copper sulfate were taken as the evaluation indexes. Through single factor experiment, the influence of sealing treatment process conditions on the corrosion resistance of the phosphating film after sealing treatment were investigated. The results showed that both the concentration of sodium silicate and sealing time have an obvious influence on the corrosion resistance of the phosphate film after sealing treatment. Appropriately increase of the concentration of sodium silicate and extension of sealing time were helpful to improve the corrosion resistance of phosphate film, while the temperature of sealing solution has a relatively small influence on the corrosion resistance of the phosphate film after sealing treatment. When the concentration of sodium silicate was 12 g/L, sealing time was 16 min and temperature of sealing solution was about 75 ℃, the phosphating film after sealing treatment has a flat surface and compact microstructure, its corrosion resistance was significantly improved compared with the phosphating film before sealing treatment. Sealing treatment can further improve the protective effect of zinc-calcium phosphating film to the substrate.
参考文献/References:
[1] 董蓓, 魏星, 刘渊媛, 等. 磷化工艺对电镀锌预磷化板磷化膜质量的影响[J]. 材料保护, 2018, 51（12）:72-76.
Dong B, Wei X, Liu Y Y, et al. Effect of phosphating process on the quality of phosphating film on electrogalvanized sheet[J]. Materials Protection, 2018, 51（12）:72-76（in Chinese）.
[2] Debnath N C. Importance of surface preparation for corrosion protection of automobiles[J]. Journal of Surface Engineered Materials and Advanced Technology, 2013, 3（1）:94-105.
[3] 牟世辉. 锌锰系磷化膜硅烷封闭工艺研究[J]. 电镀与精饰, 2012, 34（7）:41-43.
Mu S H. Study of silane sealing process for zinc-manganese phosphate coating[J]. Plating & Finishing, 2012, 34（7）:41-43（in Chinese）.
[4] Ishigure F, Inayoshi S. The anodized films characteristic analysis of before and after sealing treatment[J]. Journal of the Vacuum Society of Japan, 2015, 58（12）:437-441.
[5] 安成强, 刘新院, 陈梨, 等. 锌锰系磷化膜硅酸钠封闭工艺研究[J]. 表面技术, 2012, 41（3）:84-86.
An C Q, Liu X Y, Chen L, et al. The study on process of sodium silicate sealing for zinc-manganese phosphate coating[J]. Surface Technology, 2012, 41（3）:84-86（in Chinese）.
[6] Dechoup S, Thaiwatthana D, Chairaungstri T. Post-treatment by sodium silicate after zinc phosphating on cold-rolled steel. Chiang Mai Journal of Science, 2012, 39（1）:30-40.
[7] 张云霞, 李亚娟. 热水和硅酸钠封孔法对镁合金磷化膜耐蚀性的影响[J]. 电镀与环保, 2014, 34（2）:37-39.
Zhang Y X, Li Y J. Effects of hot water and Na2SiO3 sealing on corrosion resistance of phosphate film for magnesium alloy[J]. Electroplating & Pollution Control, 2014, 34（2）:37-39（in Chinese）.
[8] Nam N D. Role of zinc in enhancing the corrosion resistance of Mg-5Ca alloys[J]. Journal of The Electrochemical Society, 2016, 163（3）:76-84.
[9] 王雷, 袁琳, 许育东, 等. 碳钢的电解磷化工艺探究[J]. 金属功能材料, 2015, 22（3）:35-40.
Wang L, Yuan L, Xu Y D, et al. Study on the process parameters of electrolytic phosphating. Metallic Functional Materials, 2015, 22（3）:35-40（in Chinese）.
[10] 刘志海, 李瑞萍. 硅酸钠水玻璃制作技术方法大全[M]. 北京:化学工业出版社, 2014.
相似文献/References:
[1]于海青*,丁春燕.中温锌钙系磷化工艺在Q345钢防腐蚀中的应用[J].电镀与精饰,2020,(5):44.[doi:10.3969/j.issn.1001-3849.2020.05.0070]
YU Haiqing*,DING Chunyan.Application of Medium Temperature Zn-Ca Phosphating Process in Corrosion Protection of Q345 Steel[J].Plating & Finishing,2020,(3):44.[doi:10.3969/j.issn.1001-3849.2020.05.0070]
[2]师 辉*,王树臣.稀土硝酸铈对油管锌钙系磷化膜形貌和性能的影响[J].电镀与精饰,2021,(2):22.[doi:10.3969/j.issn.1001-3849.2021.02.0050]
SHI Hui*,WANG Shuchen.师 辉1*，王树臣2[J].Plating & Finishing,2021,(3):22.[doi:10.3969/j.issn.1001-3849.2021.02.0050]
[3]于海青*,王金涛,王 东.Q345钢表面SiC颗粒掺杂锌钙系磷化膜的制备与性能[J].电镀与精饰,2021,(7):20.[doi:10.3969/j.issn.1001-3849.2021.07.004]
YU Haiqing*,WANG Jintao,WANG Dong.Preparation and Properties of Zinc-Calcium Phosphate Film Doped with SiC Particles on Q345 Steel[J].Plating & Finishing,2021,(3):20.[doi:10.3969/j.issn.1001-3849.2021.07.004]
[4]孙 伟*,许 霞,张伟华.建筑结构钢锌钙系磷化膜的结构与耐蚀性研究[J].电镀与精饰,2022,(10):60.[doi:10.3969/j.issn.1001-3849.2022.10.010]
SUN Wei*,XU Xia,ZHANG Weihua.Investigation on Structure and Corrosion Resistance of Zinc-Calcium Phosphating Films on Building Structural Steel[J].Plating & Finishing,2022,(3):60.[doi:10.3969/j.issn.1001-3849.2022.10.010]
[5]孙伟*,杨辉,徐秀凤,等.促进剂对建筑结构钢锌钙系磷化膜形貌和耐蚀性的影响[J].电镀与精饰,2023,(4):8.[doi:10.3969/j.issn.1001-3849.2023.04.002]
Sun Wei*,Yang Hui,Xu Xiufeng,et al.Effects of accelerating agents on morphology and corrosion resistance of zinc-calcium phosphating films on building structural steel[J].Plating & Finishing,2023,(3):8.[doi:10.3969/j.issn.1001-3849.2023.04.002]
[6]冉 黎,李 杰*.封闭处理对钢筋磷化膜耐蚀性的影响[J].电镀与精饰,2023,(5):34.[doi:10.3969/j.issn.1001-3849.2023.05.005]
Ran Li,Li Jie*.Effect of sealing treatment on corrosion resistance of phosphating film on rebar[J].Plating & Finishing,2023,(3):34.[doi:10.3969/j.issn.1001-3849.2023.05.005]
[7]苏 奥*,苏运娟.Ti-6Al-4V钛合金环保型阳极氧化及封闭处理研究[J].电镀与精饰,2024,(3):66.[doi:10.3969/j.issn.1001-3849.2024.03.010]
Su Ao *,Su Yunjuan.Study on environmentally friendly anodizing and sealing treatment of Ti-6Al-4V titanium alloy[J].Plating & Finishing,2024,(3):66.[doi:10.3969/j.issn.1001-3849.2024.03.010]
备注/Memo
收稿日期： 2020-08-02；修回日期： 2020-09-07
通信作者： 白玉伟，cangzhou_139@163.com
基金项目： 河北省科学技术研究与发展计划项目（09201812E）