Shen Yechao*,Ge Yong. Analysis and research on coating performance based on remanufacture of drive axle housing half shaft sleeve [J].Plating & Finishing,2023,(3):26-31.[doi:10.3969/j.issn.1001-3849.2023.03.004]
基于驱动桥壳半轴套管再制造的镀层性能分析与研究
- Title:
-
Analysis and research on coating performance based on remanufacture of drive axle housing half shaft sleeve
- Keywords:
- drive axle housing ; half shaft sleeve ; coating deposition ; coating performance ; remanufacture
- 分类号:
- TQ153
- 文献标志码:
- A
- 摘要:
- 为了研究驱动桥壳再制造沉积镀层的工艺性能,在 40Mn 基材的半轴套管表面采用电刷镀方法形成再制造修复层,选用线切割技术制备镀层和基体试样,分别利用金相显微镜观测了镀层和基体的微观形貌、采用硬度测试计验证了镀层和基体的硬度分布、使用 X 射线衍射仪进行了试样的物相分析。结果表明:在再制造沉积层的最大可镀范围内,镀层和基体结合可靠、镀层硬度优于基体、沉积镀层中未引入过多其它杂质元素,镀层性能可以满足再制造的使用性能要求。
- Abstract:
- : In order to study the process performance of the remanufactured deposited coating of the drive axle housing , the remanufactured repair layer was formed by brush plating on the surface of the half shaft sleeve of 40Mn substrate. The coating and substrate samples were prepared by wire cutting technology. The micro- morphology of the coating and substrate samples were observed by metallographic microscope , the hardness distribution of the samples was verified by hardness tester , and the phase analysis of the samples was carried out by X-ray diffractometer. The results show that within the maximum plating range of the remanufactured deposition layer , the combination of the coating and the substrate is reliable , the hardness of the coating is better than that of the substrate , and there are not too many other impurities in the deposited coating. The performance of the coating can meet the performance requirements of remanufacture.
参考文献/References:
[1] 王雪梅 , 薛振国 , 刘玲玲 . 基于有限单元法重载车辆驱动桥壳优化设计 [J]. 机械设计与制造 , 2021(1): 240-244, 249.
[2] 李攀 , 罗建国 , 朱鑫锴 , 等 . 重型载重车半轴套管精确挤压成形过程参数优化 [J]. 塑性工程学报 , 2020, 27(7): 79-85.
[3] 金国 , 丁小龙 , 胡振峰 , 等 . 电刷镀 Ni- 石墨烯复合镀层的耐腐蚀性能 [J]. 稀有金属材料与工程 , 2019, 48(6): 2002-2008.
[4] 丁浩 , 李志宏 , 朱世根 . 电刷镀超厚镍 / 铜组合镀层及其组织结构 [J]. 电镀与涂饰 , 2020, 39(5): 245-248.
[5] 李长春 , 姜新华 , 肖祥定 , 等 . Ni-P-WC 和 Ni-P-SiC 复合镀层的耐磨和耐蚀性能比较 [J]. 材料保护 , 2021, 54(9): 59-62.
[6] Rastorguev D A, Semenov K O, Dema R R, et al. Influence of the hydrodynamics of electrolyte flow on the surface quality in electrochemical machining[J]. Russian Engineering Research, 2022, 41(12): 1169-1174.
[7] Wang D Y, Ren Z Y, Le H Y, et al. Improvement on the periodic dissolution behavior of titanium alloy in counter-rotating electrochemical machinin[J]. The International Journal of Advanced Manufacturing Technology, 2021, 116: 877-887.
[8] Sun G R, Ying Y, Dong J T, et al. Research on electrochemical machining technology of deep small hole using suction electrode[J]. Journal of Physics: Conference Series, 2021, 1948(1): 1-6.
[9] Daniel N R, Marcelo P S, José B C, et al. Kinetics of conversion of brushite coatings to hydroxyapatite in alkaline solution[J]. Journal of Materials Research and Technology, 2018, 7(4): 479-486.
[10] 孙垂康 , 贾卫平 , 周绍安 , 等 . 超声辅助脉冲电沉积 Ni - TiN 复合镀层的结合力和耐蚀性 [J]. 材料保护 , 2021, 54(4): 80-85.
[11] Kostruba A, Stetsyshyn Y, Mayevska S, et al. Composition, thickness and properties of grafted copolymer brush coatings determined by ellipsometry: calculation and prediction.[J]. Soft Matter, 2018, 14(6): 1016-1025.
[12] 张春杰 , 应丽霞 , 吴云龙 , 等 . 热处理温度对 Ni-P/Al 2 O 3 / 石墨烯复合刷镀层性能的影响 [J]. 材料热处理学报 , 2021, 42(4): 153-159.
[13] 杨惠良 . 硫酸盐镀液中紫铜电沉积 Ni-Co/WC 复合镀层的工艺条件优化 [J]. 电镀与精饰 , 2021, 43(6): 30-34.
[14] 詹中伟 , 葛玉麟 , 田礼熙 , 等 . 搅拌速度和颗粒尺寸对复合电沉积 Ni-cBN 复合量的影响及机理分析 [J]. 电镀与精饰 , 2022, 44(1): 1-5.
[15] 吕镖 , 胡振峰 , 汪笑鹤 , 等 . 相对运动速度对柔性摩擦辅助电沉积镍镀层结构的影响 [J]. 材料研究学报 , 2014, 28(4): 255-261.
[16] 李恒征 , 康敏 , 张银 , 等 . 喷射参数对 Ni-Co-BN(h) 纳米复合镀层结构及耐磨性的影响 [J]. 中国表面工程 , 2018, 31(2): 103-112.
[17] Hsue A W J, Huang Z Y. Deionized water electrochemical machining hybridized with alumina powder polishing for microcavity of m-333 mold steel[J]. Processes, 2022, 10(1): 152.
[18] Shen Z Y, Tsui H P. An investigation of ultrasonic-assisted electrochemical machining of micro-hole array [J]. Processes, 2021, 9(9): 1615.
[19] 钟强 , 钱炯 , 周宇宾 , 等 . 双环电化学动电位再活化法评价 UNS N08811 的晶间腐蚀敏感性 [J]. 材料保护 , 2021, 54(3): 23-27, 45.
[20] Kaewsaard P, Zhu H, Qi H, et al. Laser surface masking of stainless steel for electrochemical machining process[J]. The Inter national Journal of Advanced Manufacturing Technology, 2021, 116(3-4): 1141-1150.
备注/Memo
收稿日期: 2022-07-29 修回日期: 2022-09-03 作者简介: 沈晔超( 1987 ―),男,硕士,讲师,研究方向为机电产品绿色设计与制造、工业机器人技术, email : shenyechao2006@126.com 基金项目: 安徽省高校科学研究项目( KJ2020A1106 ),安徽省高等学校省级质量工程项目( 2020jyxm0306 );职业教育提质培优行动计划( 2020tzpy46-5 ),安徽省高校优秀青年人才支持计划项目( gxyq2022275 )