CAI Jianfeng *.Quality Process Control for Medium Temperature Phosphating of Ship Piping Zinc-Calcium System[J].Plating & Finishing,2022,(2):30-35.[doi:10.3969/j.issn.1001-3849.2022.02.007]
船舶管系锌钙系中温磷化质量过程控制
- Title:
- Quality Process Control for Medium Temperature Phosphating of Ship Piping Zinc-Calcium System
- 分类号:
- TB43
- 文献标志码:
- A
- 摘要:
- 对适用于船舶管系的不同磷化液成分进行选型和比较,选用了锌钙系 HY-3 磷化液及其相关工艺,并优化了其质量过程控制。结果表明: HY-3 锌钙系中温磷化工艺能有效地提升磷化前处理质量,满足磷酸转化膜内壁防腐、外壁增强涂装结合力的工艺要求,为船舶建造提供了保障。
- Abstract:
- The different phosphating liquid components suitable for ship piping were selected and compared , HY-3 phosphating solution of zinc-calcium system and its related process were selected , and its quality control process was also optimized. The results showed that the HY-3 medium temperature phosphating process could effectively improve the pre-treatment quality of phosphating , meet the technological requirements of phosphoric acid conversion film for inner wall anticorrosion and outer wall enhancement for coating binding force , and provide a guarantee for ship construction.
参考文献/References:
[1] CB/Z 94 -19 68, 黑色金属磷化技术条件 [S].
[2] 蒋文军 . 锌钙系防锈磷化工艺 [J]. 合肥学院学报 ( 自然科学版 ), 2006, (B10): 30-32.
Jiang W J. The zinc calcium guards against rust the phosphorization craft [J]. Journal of Hefei University (Natural Sciences), 2006, (B10): 30-32 (in Chinese).
[3] 曹学增 , 陈爱英 . 影响锌钙系磷化液性能的几个因素 [J]. 常熟高专学报 , 2002, (2): 32-35.
Cao X Z, Chen A Y. The factors that influence property of phosphatating liquid in middle temperature zinc-calcium series [J]. Journal of Changshu College, 2002, (2): 32-35 (in Chinese).
[4] GB/T 5936 - 1986, 轻工产品黑色金属化学保护层的测试方法—浸渍点滴法 [S].
[5] GB/T 10125 - 2012/ISO 9227: 2006, 人造气氛腐蚀试验—盐雾试验 [S].
[6] GB/T 9286 - 1998, 色漆和清漆—漆膜的划格试验 [S].
[7] 文斯雄 . 锌钙系中温磷化 [J]. 电镀与精饰 , 2002, 24(1): 18-19.
Wen S X. Zinc-calcium system medium temperature phosphating [J]. Plating & Finishing, 2002, 24(1): 18-19 (in Chinese).
[8] 杨占伟 , 孙涛 . 中温锌系磷化质量控制与工艺维护 [J]. 电镀与涂饰 , 2003, (4): 48-50.
Yang Z W, Sun T. Quality control and process maintenance of zinc phosphating at medium temperature [J]. Electroplating & Finishing, 2003, (4): 48-50 (in Chinese).
[9] 傅敏 , 吴四维 . 中温锌钙系磷化液研究 [J]. 渝州大学学报 , 1999, (2): 62-65.
Fu M, Wu S W. Study on mid-temperature Ca-Zn phosphating solution [J]. Journal of Yuzhou University, 1999, (2): 62-65 (in Chinese).
[10] GB/T 11376 - 1997, 金属的磷酸盐转化膜 [S].
[11] GB/T 6807 - 2001, 钢铁工件涂漆前磷化处理技术条件 [S].
备注/Memo
收稿日期: 2021-01-31 修回日期: 2021-02-06 作者简介: 蔡建峰( 1979 —),男,助理工程师,经济师, email : caijianfeng@smmail.cn