Anti-Corrosion Performance Researching on Zn-Ni Alloy Coating of Elastic Element
- 作者:
-
王林; 周同理; 邓建青; 李斌; 谢彦飞
-
株洲时代新材料科技股份有限公司
- 分类号:
-
TQ153.2
- 摘要:
-
主要研究并分析了不同工艺下的锌-镍合金镀层及不同厚度镀层的防腐性能。结果表明,不同工艺防腐性能优劣顺序为:电镀+钝化+封闭电镀+钝化电镀+封闭电镀,随厚度增加,镀层防腐性能提高,δ为812μm的锌-镍合金镀层在保证生产效率的前提下,具有良好的防腐性能,且产品具有良好的粘合性能。
- Abstract:
-
Anti-corrosion performance of different processes and thickness of Zn-Ni alloy coatings were researched and analyzed. Results showed that the anti-corrosion performances order of the different processes,in accordance with their pros and cons,was as following: electroplating + passivation + sealing electroplating + passivation electroplating + sealing electroplating,and the anti-corrosion performance would increase with the thickness increasing. On premise of ensuring production efficiency,the Zn-Ni alloy coating with 8 ~ 12 μm thickness had good anti-corrosion performance,and the product had good adhesion performance.