[1]高继文*,高俊国,南 健.超音速火焰喷涂316L不锈钢涂层在零件尺寸修复中的应用[J].电镀与精饰,2020,(2):38-43.[doi:10.3969/j.issn.1001-3849.2020.02.008]
　GAO Jiwen*,GAO Junguo,NAN Jian.Application of HVOF 316L Stainless Steel Coating in Resizing of Parts[J].Plating & Finishing,2020,(2):38-43.[doi:10.3969/j.issn.1001-3849.2020.02.008]
点击复制

超音速火焰喷涂316L不锈钢涂层在零件尺寸修复中的应用()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2020年2
页码:
38-43
栏目:
出版日期:
2020-02-15

文章信息/Info

Title:
Application of HVOF 316L Stainless Steel Coating in Resizing of Parts
作者:
高继文1*; 高俊国2; 南 健1
1. 国营芜湖机械厂， 安徽 芜湖 241007； 2. 北京航空材料研究院，北京 100095
Author(s):
GAO Jiwen1*;  GAO Junguo2;  NAN Jian1
1. State-owned Wuhu Machinery Factory, Wuhu 241007, China;　2. Beijing Institute of Aeronautical Materials, Beijing 100095, China
关键词:
尺寸超差; 超音速火焰喷涂; 316L不锈钢涂层; 尺寸修复
Keywords:
dimension deviation;  high velocity oxygen fuel (HVOF);  316L stainless steel coating;  size repair
DOI:
10.3969/j.issn.1001-3849.2020.02.008
文献标志码:
A
摘要:
为了解决装备核心零部件因磨损、消除腐蚀等带来的尺寸超差问题，制作超音速火焰喷涂316L不锈钢涂层性能试样，对试样涂层的形貌、硬度、耐蚀性开展试验检测研究。结果表明，涂层具有与25Cr3MoA接近的硬度和比30CrMnSiNi2A更好的耐蚀性能。由此，提出采用超音速火焰喷涂316L不锈钢涂层进行零件尺寸修复，制定了可行的修理方案和技术路线，确定了修理工序和参数，形成了相关技术文件，用于指导零件尺寸修复，并在油泵轴和肩轴两类零件上成功应用和装机验证，其性能良好，质量安全。
Abstract:
In order to solve the problems of dimension deviation caused by wear and corrosion of core parts of equipment, the high velocity oxygen fuel (HVOF) 316L stainless steel coating performance samples were made, and the morphology, hardness and corrosion resistance of the coatings were tested. The results showed that the coating had a hardness close to that of 25Cr3MoA and better corrosion resistance than 30CrMnSiNi2A. Therefore, the HVOF 316L stainless steel coating was used for part size repair, a feasible repair plan and technical route were developed, the repair process and parameters were determined, and the relevant technical documents was formed to guide the part size repair which had been successfully applied and verified on oil pump shaft and shoulder shaft with good performance and safe quality.

参考文献/References:

[1] 张六泉.Inconel 690合金HVOF喷涂WC-10Co4Cr涂层高温微动磨损特性研究[D]. 成都:西南交通大学, 2017.
[2] 陈焕涛, 陈文龙, 张晓锋, 等.HVOF和APS喷涂WC-10Co-4Cr涂层性能研究[J]. 材料研究与应用, 2017, 11(1):30-33.
[3] Ding X, Cheng X D, Yu X, et al. Structure and cavitation erosion behavior of HVOF sprayed multi-dimensional WC-10Co4Cr coating[J]. Transactions of Nonferrous Metals Society of China, 2018, (28):487-494.
[4] 周夏凉, 陈小明, 吴燕明, 等.HVOF制备纳米WC-10Co4Cr涂层的微观组织及抗冲蚀性能[J]. 粉末冶金材料科学与工程, 2018, 23(2):124-129.
[5] 李洪波, 韩金成, 顾勇飞, 等.T10钢表面HVOF喷涂WC-10Co4Cr涂层的耐磨性研究[J]. 燕山大学学报, 2016, 40(1):22-28.
[6] 王大锋, 张波萍, 贾成厂, 等.WC粉末粒度对超音速火焰喷涂WC-CoCr涂层组织性能的影响[J]. 粉末冶金工业, 2017, 27(2):58-65.
[7] 王进春, 孔德军.超音速火焰喷涂WC-12Co涂层高温摩擦-磨损性能[J]. 中南大学学报(自然科学版), 2017, 48(3):608-616.
[8] 余俊.粉末冶金316L不锈钢的制备及性能研究[D]. 南京:南京航空航天大学, 2012.
[9] 郭孟秋, 张兴华, 阙民红, 等.超音速火焰喷涂316L不锈钢涂层性能研究[J]. 失效分析与预防, 2013, 8(4):216-221.
[10] 吴文恒, 吴凯琦, 肖逸凡, 等.气雾化压力对3D打印用316L不锈钢粉末性能的影响[J]. 粉末冶金技术, 2017, 35(2):83-88.
[11] 孔祥吉, 刘超, 况春江, 等.316L不锈钢粉末微注射成形的烧结过程有限元模拟研究[J]. 粉末冶金工业, 2017, 27(6):27-33.
[12] 翟敏, 安浩.超音速火焰喷涂与电镀铬的工艺研究[J]. 中国科技纵横, 2018, (2):81-83.
[13] 王升伟. 超声速火焰喷涂技术在航空修理领域的应用研究[C]//武哲.中国航空学会:航空装备维修技术及应用研讨会论文集, 北京:航空知识杂志社, 2015:596-604.
[14] 高继文, 刘洲. 镀铬活塞杆表层裂纹分析与解决[J]. 电镀与精饰, 2019, 41(5):43-48.

备注/Memo

备注/Memo:
收稿日期： 2019-09-15；修回日期： 2019-12-29
通信作者： 高继文（1970—）， 男， 安徽芜湖人， 高级工程师， 主要从事航空附件维修与工艺优化设计工作。
email: 690802818@qq.com
基金项目： 装备预研重点领域基金项目(61400040404)
更新日期/Last Update: 2020-02-10