LUO Weihua,DING Yunhu*,MAO Zuguo,et al.Study on Water-Soluble Protective Agent for Nickel Plating of Battery Shell[J].Plating & Finishing,2020,(7):17-22.[doi:10.3969/j.issn.1001-3849.2020.07.0040]
水溶性电池壳镀镍层保护剂研究
- Title:
- Study on Water-Soluble Protective Agent for Nickel Plating of Battery Shell
- 文献标志码:
- A
- 摘要:
- 以水溶性油酸酯为电池壳镀镍层基础保护剂组分，分别研究了硫醇、MF缓蚀剂和葵二酸三乙醇胺酯等辅助保护剂对保护膜层性能的影响。采用正交试验对保护剂组分进行了优化，通过中性盐雾实验、高温高湿实验、SEM和EDS等研究了保护膜层的性能。结果表明，当硫醇添加量为1.0%，MF缓蚀剂添加量为1.0%，葵二酸三乙醇胺酯添加量为8.0%时，保护剂制备的膜层综合性能最好。
- Abstract:
- The effects of thiol, MF corrosion inhibitor and triethanolamine glycerate on the performance of the protective film layer were studied using water-soluble oleate as the basic protective agent component of the nickel plating layer of the battery case. The orthogonal test was adopted to optimize the composition of the protective agent, and the performance of the protective film layer was studied by neutral salt spray test, high temperature and high humidity test, SEM and EDS. The results showed that when the amount of thiol was 1.0%, the amount of MF corrosion inhibitor was 1.0%, and the amount of triethanolamine malate was 8.0%, the comprehensive performance of the film prepared by the protective agent was best.
参考文献/References:
[1] 王文忠. 金属防锈剂[J]. 电镀与环保, 2000, 20(2):33-34.
Wang W Z. Metal rust inhibitor [J]. Electroplating and Environmental Protection, 2000, 20 (2): 33-34(in Chinese).
[2] Eugenio A, Flores O O, Natalya V, et al. Sodium phthalamates as corrosion inhibitors for carbon steel in aqueous hydrochloric acid solution[J]. Corrosion Science, 2011, 53(12):3899-3913.
[3] 马聪. 新能源汽车动力电池组焊接工艺研究[D]. 长春:长春理工大学, 2014.
Ma C. Research on welding technology of new energy vehicle power battery pack[D]. Changchun: Changchun University of Science and Technology, 2014. (in Chinese)
[4] 周树云, 陈萍. 硫醇化合物在银盐CTP版材上的疏水作用[J]. 感光科学与光化学, 1998, 16(4):321-325.
Zhou S Y, Chen P. Hydrophobic effect of thiol compounds on silver salt CTP plates[J]. Photographic Science and Photochemistry, 1998, 16 (4): 321-325.(in Chinese)
[5] 冷静文, 尚云成, 刘伟, 等. 蓖麻油在化工领域的研究进展[J]. 农业科技通讯, 2019, 569(5):226-227+230.
Calm W, Shang Y C, Liu W, et al. Research progress of castor oil in chemical industry[J]. Agricultural Science and Technology Newsletter, 2019, 569 (5): 226-227 + 230.(in Chinese)
[6] 王昕, 张春丽, 王艳军. 钼酸钠和三乙醇胺对45#钢的缓蚀作用研究[J]. 沈阳理工大学学报, 2003, 22(4):89-91.
Wang X, Zhang C L, Wang Y J. Research on the corrosion inhibition effect of sodium molybdate and triethanolamine on 45 # steel[J]. Journal of Shenyang University of Science and Technology, 2003, 22 (4): 89-91.(in Chinese)
[7] 张允诚, 胡如南, 向荣. 电镀手册(第4版) [M]. 北京:国防工业出版社, 2011.
Zhang Y C, Hu R N, Xiang R. Electroplating Manual (4th Edition) [M]. Beijing:National Defense Industry Press, 2011. (in Chinese)
[8] 张宝根. 钢铁基体镀镍保护材料的研制[J]. 电镀与涂饰, 2002, 5:22-23.
Zhang B G. Development of nickel-plated protective material for steel substrate[J]. Electroplating and Finishing, 2002, 5: 22-23. (in Chinese)
相似文献/References:
[1]董 楹,王朝琳,文颖慧,等.doi: 10.3969/j.issn.1001-3849.2025.01.010飞机零部件原位修复用钝化膏的制备及性能评价[J].电镀与精饰,2025,(01):59.
Dai Xiaoliang,Liu Zhigang*.Preparation and performance evaluation of passivation paste for in-situ repair of aircraft components and parts Dong Ying1, Wang Zhaolin1, Wen Yinghui1, Song Bin1, Mi Nan 1,[J].Plating & Finishing,2025,(7):59.
备注/Memo
收稿日期： 2020-04-15；修回日期： 2020-05-19
通信作者：丁运虎，35184526@qq.com