CHEN Yajun* SUN Licheng WANG Hansen REN Kaixu SONG Xiaoxiao WANG Xin.Corrosion Behavior of Two Kinds of Polyurethane Coated Cold Colled Plates in Cyclic Salt Spray Test[J].Plating & Finishing,2022,(1):11-21.[doi:10.3969/j.issn.1001-3849.2022.01.003]
循环盐雾中两种聚氨酯涂层冷轧板腐蚀行为
- Title:
- Corrosion Behavior of Two Kinds of Polyurethane Coated Cold Colled Plates in Cyclic Salt Spray Test
- Keywords:
- polyurethane coating; cold rolled plate; electrophoresis; powder spraying; cyclic salt spray test; corrosion behavior
- 分类号:
- V261.93+3
- 文献标志码:
- A
- 摘要:
- 为了解决冷轧板耐蚀性差的问题，常在其表面制备聚氨酯涂层。本文以电泳聚氨脂涂层冷轧板（ESPCC）和粉末喷涂聚氨脂涂层冷轧板（PSPCC）为研究对象，进行42 d的循环盐雾试验后，通过扫描电镜、X射线衍射分析和电化学测试来考察其在循环盐雾试验环境中的腐蚀形貌、腐蚀产物组成和电化学行为。结果表明，ESPCC和PSPCC经过42 d循环盐雾腐蚀后的单边扩蚀宽度分别为0.45 mm和0.25 mm。ESPCC比PSPCC的腐蚀颗粒更大，二者的腐蚀产物都是Fe 3O4、α-FeOOH、γ-FeOOH和β-FeOOH，但是ESPCC的腐蚀产物的峰值强度高于PSPCC。ESPCC的腐蚀电流密度最大为1.08×10-5 A·cm -2，大于PSPCC的最大腐蚀电流密度1.34×10-9 A·cm -2；且其腐蚀42 d后电荷转移电阻只有2.88×104 Ω ?cm2，小于PSPCC腐蚀42 d后的电荷转移电阻1.35×1010 Ω ?cm2。
- Abstract:
- In order to solve the problem of poor corrosion resisitance of cold rolled plate， the polyurethane coating is often prepared on the surface. In this paper， the cold rolled plate with electrophoresis polyurethane coating （ESPCC） and the cold rolled plate with powder spraying polyurethane coating （PSPCC） were used as research objects. After 42 days of cyclic salt spray test， the corrosion morphology， corrosion product composition and electrochemical behavior in cyclic salt spray test environment were investigated by scanning electron microscope， X-ray diffraction and electrochemical test. The results show that the single side erosion width of ESPCC and PSPCC after 42 d cyclic salt spray corrosion is 0.45 mm and 0.25 mm， respectively. ESPCC has larger corrosion particles than PSPCC. The corrosion products of both are Fe3O4， α-FeOOH， γ-FeOOH and β-FeOOH， but the peak strength of the corrosion products of ESPCC is higher than that of PSPCC. The maximum corrosion current density of ESPCC reached 1.08×10-5 A·cm -2， which is greater than 1.34×10-9 A·cm -2 of PSPCC. The charge transfer resistance of PSPCC is only 2.88×10 4 Ω ·cm2， which is less than 1.35×1010 Ω ·cm2 of ESPCC after 42 d cyclic salt spray corrosion
参考文献/References:
[1] 刘艳辉, 邓爱民. 聚氨酯-聚丙烯酸互穿网络聚合物乳液的合成[J]. 电镀与精饰, 2009, 30(1): 34-37.
Liu Y H, Deng A M. Synthesis of polyurethane-polyacrylic acid interpenetrating network polymer emulsion[J]. Plating &Finishing, 2009, 30(1): 34-37 (in Chinese).
[2] 万亭. 提高聚氨酯磁漆涂层的结合力和外观质量[J]. 电镀与精饰, 2013(2): 29-31.
Wan T. Improve the adhesion and appearance quality of polyurethane enamel coatings[J]. Plating &Finishing, 2013(2): 29-31 (in Chinese).
[3] Ramde T, Ecco L G, Rossi S. Visual appearance durability as function of natural and accelerated ageing of electrophoretic styrene-acrylic coatings: influence of yellow pigment concentration[J]. Progress in Organic Coatings, 2017, 103: 23-32.
[4] 卢琳, 胡建文, 李晓刚, 等. 光老化对丙烯酸聚氨酯/钢板界面附着力的影响[J]. 复合材料学报, 2011, 28(2): 94-99.
Lu L, Hu J W, Li X G, et al. Effect of light aging on interface adhesion of acrylic polyurethane/steel sheet[J]. Journal of Composite Materials, 2011, 28(2): 94-99 (in Chinese).
[5] Merlatti C, Perrin F X, Aragon E, et al. Natural and artificial weathering characteristics of stabilized acrylic-urethane paints[J]. Polymer Degradation & Stability, 2008, 93(5): 896-903.
[6] 杨晓然, 袁艺, 李迪凡, 等. 高加速自然环境试验系统的研制[J]. 腐蚀科学与防护技术, 2012, 24(6): 489-493.
Yang X R, Yuan Y, Li D F, et al. Development of a highly accelerated natural environment test system[J]. Corrosion Science and Protection Technology, 2012, 24(6): 489-493 (in Chinese).
[7] 胡明涛, 鞠鹏飞, 赵旭辉, 等. 不同加速试验对环氧/聚氨酯涂层失效机制的影响[J]. 化工学报, 2018, 69(8): 3548-3556.
Hu M T, Ju P F, Zhao X H, et al. Effect of different accelerated tests on failure mechanism of epoxy/polyurethane coatings[J]. Journal of Chemical Industry, 2018, 69(8): 3548-3556 (in Chinese).
[8] 卢浩. 纳米改性聚氨酯复合涂层的制备及其防腐蚀性能的研究[D]. 天津: 中国民航大学, 2015.
[9] 卢海艳. 碳钢表面聚氨酯/石墨烯复合防腐涂层的制备及性能研究[D]. 马鞍山: 安徽工业大学, 2019.
[10] Gaurav V. Weathering, salt spray corrosion and mar resistance mechanism of clay (nano-platelet) reinforced polyurethane nanocomposite coatings[J]. Progress in Organic Coatings, 2019, 129: 260-270.
[11] Nguyen T D, Tran B A, Phan T T, et al. Corrosion protection of carbon steel by polyurethane coatings containing graphene oxide[J]. Vietnam Journal of Chemistry, 2020, 58(1): 108-112.
[12] Palimi M, Ramezanzadeh B, Mahdavian M, et al. The corrosion protection performance of the polyurethane coatings containing surface modified Fe2O3 nanoparticles[J]. Corrosion, 2015, 71(8): 1012-1026.
[13] 纪红, 张文梅, 樊志罡, 等. 循环盐雾标准方法[J]. 环境技术, 2016, 34(1): 53-56+60.
Ji H, Zhang W M, Fan Z G, et al. Standard method for circulating salt spray[J]. Environmental Technology, 2016, 34(1): 53-56+60 (in Chinese).
[14] 刘鹏洋, 周和荣, 但佳永, 等. 中性盐雾腐蚀环境中B340LA钢板的腐蚀周期性研究[J]. 材料保护, 2018, 51(12): 28-32+67.
Liu P Y, Zhou H R, Dan J Y, et al. Periodic study on corrosion of B340LA steel plate in neutral salt spray corrosion environment[J]. Materials Protection, 2018, 51(12): 28-32+67 (in Chinese).
[15] Caia Q, Li S X, Pu J B, et al. Corrosion resistance and antifouling activities of silver-doped CrN coatings deposited by magnetron sputtering[J]. Surface and Coatings Technology, 2018, 453:194-202.
[16] 李俊. 新型聚苯胺环氧树脂复合防腐涂料的制备及其涂覆体系防腐性能的研究[D]. 杭州: 浙江大学, 2016.
[17] 聂铭, 岳楹超, 梁永纯, 等. 模拟酸雨环境下镀锌钢的阻抗谱解析[J]. 全面腐蚀控制, 2018, 32(10): 16-18+38.
Nie M, Qiu Y C, Liang Y C, et al. Impedance spectrum analysis of galvanized steel under simulated acid rain[J]. Total Corrosion Control, 2018, 32(10): 16-18+38 (in Chinese).
[18] 朱晓春. 合金元素Sb对Mg-5Al-2Sr合金组织和性能的影响[D]. 南京: 南京航空航天大学, 2012.
[19] Zhang J Q, Cao C N. Studyand evaluation on organic coatings by electrochemical impedance spectroscopy[J]. Corrosion and Protection, 1998, 3: 99-104.
[20] 庞然, 左禹, 唐聿明, 等. 环氧/聚氨酯涂层在4种环境中失效行为的EIS[J]. 化工学报, 2010, 61(10): 2656-2661.
Pang R, Zuo Y, Tang Y M, et al. EIS of epoxy/polyurethane coating failure behavior in 4 environments[J]. Journal of Chemical Industry, 2010, 61(10): 2656-2661 (in Chinese).
[21] 孔纲, 卢锦堂, 车淳山, 等. 热镀锌钢白锈产生原因分析及预防[J]. 腐蚀与防护, 2005, 26(10): 450-452.
相似文献/References:
[1]杨维宇,刘 妍,刘恩泽,等.影响冷轧板表面转化膜形成质量因素研究[J].电镀与精饰,2024,(9):76.[doi:doi: 10.3969/j.issn.1001-3849.2024.09.011]
Yang Weiyu*,Liu Yan,Liu Enze,et al.Analysis of factors influencing the quality of surface conversion film formation on cold rolled sheet[J].Plating & Finishing,2024,(1):76.[doi:doi: 10.3969/j.issn.1001-3849.2024.09.011]
备注/Memo
收稿日期： 2021-01-23 修回日期： 2021-03-05 通信作者： 陈亚军，email：yjchen@cauc.edu.cn