[1]毛 喆*,尹中秋,胡剑锋,等.漆膜颗粒的产生原因及控制措施[J].电镀与精饰,2022,(1):35-39.[doi:10.3969/j.issn.1001-3849.2022.01.006]
　MAO Zhe*,YIN Zhongqiu,HU Jianfeng,et al.Causes and Control Measures of Paint Film Particles[J].Plating & Finishing,2022,(1):35-39.[doi:10.3969/j.issn.1001-3849.2022.01.006]
点击复制

漆膜颗粒的产生原因及控制措施()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2022年1
页码:
35-39
栏目:
出版日期:
2022-01-09

文章信息/Info

Title:
Causes and Control Measures of Paint Film Particles
作者:
毛 喆1*; 尹中秋2; 胡剑锋2; 黄红武1; 黄天勇1
(1.航空工业郑飞公司热表处理厂, 河南 郑州 450005; 2.空军装备部驻郑州地区军事代表室,河南 郑州 450005)
Author(s):
MAO Zhe1*； YIN Zhongqiu2； HU Jianfeng2； HUANG Hongwu1； HUANG Tianyong1
(1.Heat Treatment and Surface Treatment Plant of Zheng Fei Company of Aviation Industry Zhengzhou 450005 China；2.Military Representative Office of Air Force Equipment Department in Zhengzhou Zhengzhou 450005 China)
关键词:
漆膜; 颗粒; 系统; 控制措施
Keywords:
paint film;  particle;  system;  control measures
分类号:
TQ639.8
DOI:
10.3969/j.issn.1001-3849.2022.01.006
文献标志码:
B
摘要:
本文针对漆膜颗粒问题，从材料基体、环境、油漆以及施工四个方面对漆膜颗粒的来源进行了分析，阐述了漆膜颗粒对产品质量的影响，并对制件的前处理、周转、喷漆环境以及操作提出了系统的控制措施，有效避免了涂膜颗粒的产生。
Abstract:
In this paper， aiming at the problem of paint film particles， the sources of paint film particles from four aspects of material matrix， environment， paint and construction were analyzed. The influence of paint film particles on product quality was expounded. Systematic control measures for the pretreatment， turnover， painting environment and operation of parts were put forward， and the coating particles could be effectively avoided

参考文献/References:

[1] 毛喆, 胡剑锋, 黄红武. 涂装过程多余物的类型及控制[J]. 现代涂料与涂装, 2019, 22(6): 19-21+24.

Mao Z, Hu J F, Huang H W. Types and control of excess in painting process[J]. Modern Paint and Finishing, 2019, 22(6): 19-21+24 (in Chinese).

[2] 何晓敏. 铸造铝合金中的针孔及其防止[J]. 金属加工, 2009, 3: 58-60.

He X M. Pinholes in cast aluminum alloys and their prevention[J]. Metal Working, 2009, 3: 58-60 (in Chinese).

[3] 毛喆, 胡剑锋, 黄红武. 涂装表面颗粒产生的原因与预防[J]. 现代涂料与涂装, 2017, 20(6): 42-43.

Mao Z, Hu J F, Huang H W. Cause and prevention of particles on the surface coating[J]. Modern Paint and Finishing, 2017,20(6): 42-43 (in Chinese).

[4] 周强, 金祝年. 涂料化学[M]. 北京: 化学工业出版社, 2007: 109.

[5] 陈治良. 现代涂装手册[M]. 北京: 化学工业出版社, 2010: 234.

[6] 潘继民. 涂装技术1000问[M]. 北京: 机械工业出版社, 2013: 154.

[7] 毛喆, 黄红武, 胡剑锋. 漆层湿热试验中起泡原因分析及控制措施[J]. 材料保护, 2017, 50(9): 99-102.

Mao Z, Huang H W, Hu J F. Causes analysis and control measures of paint layer foaming in humid heat test[J]. Material Protection, 2017, 50(9): 99-102 (in Chinese).

[8] 李永训, 白桦, 汤克勤, 等. GJB4439—2002军用飞机喷漆通用要求[S]. 北京: 总装备部军标发行部, 2003: 5.

[9] 傅新广, 张慧珍, 徐永明, 等. HB/Z102—2000机载设备"三防"涂层涂漆工艺[S]. 北京: 中国航空工业总公司三〇一研究所, 2001: 2.

[10] 徐滨士, 刘世参. 中国材料工程大典(第16卷)[M]. 北京: 化工工业出版社, 2005: 194.

[11] 徐美刚, 郑金芝. 涂装工艺学[M]. 北京: 中国劳动社会保障出版社, 2010: 82.

备注/Memo

备注/Memo:
收稿日期： 2021-03-03 修回日期： 2021-05-10
更新日期/Last Update: 2022-01-07