SUN Wei,ZHANG Weihua,DU Xiuli.Investigation on Zinc-Calcium Phosphating Treatment of 16Mn Steel Used for Architectural Structure[J].Plating & Finishing,2021,(4):11-15.[doi:10.3969/j.issn.1001-3849.2021.04.003]
建筑结构用16Mn钢锌钙系磷化处理研究
- Title:
- Investigation on Zinc-Calcium Phosphating Treatment of 16Mn Steel Used for Architectural Structure
- 关键词:
- 锌钙系磷化处理; 建筑结构用16Mn钢; 耐蚀性; 稀土; 超声波
- 文献标志码:
- A
- 摘要:
- 以建筑结构用16Mn钢作为基体,在稀土、超声波单独及复合作用下进行锌钙系磷化处理,旨在改善磷化工艺条件从而进一步提高锌钙系磷化膜的耐蚀性。研究了稀土、超声波单独及复合作用下获得的磷化膜的形貌、成分、厚度和耐蚀性,结果表明:稀土、超声波单独及复合作用不会对磷化膜成分产生影响,但会影响磷化膜的形貌、厚度和耐蚀性。超声波单独作用对改善磷化膜的致密度效果不明显,获得的磷化膜厚度与无超声波时相差不大,磷化膜的耐蚀性也未表现出明显的提高。稀土单独作用能有效促进磷化成膜,获得了晶粒细小、比较致密的磷化膜,虽然磷化膜的厚度下降,但耐蚀性明显提高。稀土和超声波复合作用获得的磷化膜表面也比较平整致密,其耐蚀性与无超声波和超声波单独作用获得的磷化膜相比要好,但与稀土单独作用获得的磷化膜相比稍差。
- Abstract:
- Zinc-calcium phosphating treatment of 16Mn steel used for architectural structure under the action of rare earth and ultrasonic alone and in combination was carried out aiming to improve the phosphating process conditions and then further improve the performance of zinc-calcium phosphating film. The morphology, composition, thickness and corrosion resistance of the phosphating film obtained under the action of rare earth and ultrasonic alone and in combination were studied, and the results showed that the action of rare earth and ultrasonic alone and in combination do not affect the composition of phosphating film, but can affect the morphology, thickness and corrosion resistance of phosphating film. The effect of ultrasonic alone on improving the density of phosphating film was not obvious, the thickness of phosphating film was close to that of the phosphating film obtained without ultrasonic, and the corrosion resistance of phosphating film does not show an obvious improvement. The action of rare earth alone can effectively promote phosphating film formation, and a phosphating film with fine grains and compact structure was obtained. Although the thickness of phosphating film decreased, the corrosion resistance increased obviously. The surface of phosphating film obtained by the combined action of rare earth and ultrasonic was relatively flat and dense, and its corrosion resistance was better than that of the phosphating film obtained with or without ultrasonic, but it was slightly worse than that of the phosphating film obtained by the action of rare earth alone.
参考文献/References:
[1] 张辉.火灾条件下16Mn钢的力学性能试验研究[J]. 理化检验-物理分册,2006,42(6):282-284.
Zhang H. Mechanical performance of 16Mn steel under fire condition[J]. Physical and Chemical Examination-Physical Section, 2006, 42(6): 282-284(in Chinese).
[2] 郎丰军,杨奕,黄先球,等.表面处理对免酸洗钢磷化膜耐蚀性影响[J]. 钢铁研究,2015,43(6):41-43.
Lang F J, Yang Y, Huang X Q, et al. Influence of surface treatment on corrosion resistance of phosphate coating of a free-pickled steel[J]. Research on Iron and Steel, 2015, 43(6): 41-43(in Chinese).
[3] Kuang J. Phosphatization coating-forming mechanism based on green phosphating accelerator rare earth nitrate[J]. Advanced Materials Research, 2013(838-841): 2806-2810.
[4] Kuang J C, Huang Y. Effect of rare earth on the coating-forming and mechanism of phosphatization[J]. Journal of Rare Earths, 2010(S1): 132-135.
[5] 胡贵芳,胡秀英,宋皖杰,等.超声波作用下钢铁常温磷化影响因素研究[J]. 电镀与精饰,2019,41(5):9-15.
Hu G F, Hu X Y, Song W J, et al. Study on the influencing factors of phosphating for iron and steel under the action of ultrasound at room temperature[J]. Plating & Finishing, 2019, 41(5): 9-15(in Chinese).
[6] Diaz B, Freire L, Mojio M. at al. Optimization of conversion coatings based on zinc phosphate on high strength steels, with enhanced barrier properties[J]. Journal of Electroanalytical Chemistry, 2015, 737: 174-183.
[7] 冯晨萁.超声波辅助镍基金属镀层的制备及其性能研究[D]. 上海:上海应用技术大学,2017.
[8] 李红玲,付小宁.铝合金表面无铬磷酸盐稀土转化膜的成膜机理及耐蚀性研究[J]. 表面技术,2011,40(2):8-11.
Li H L, Fu X N. Study on the film forming mechanism and corrosion resistance of non-chromium phosphate rare earth Conversion coating on Al alloy[J]. Surface Technology, 2011, 40(2): 8-11(in Chinese).
[9] 李帅.AZ91镁合金磁控溅射氮化铝膜的制备工艺及其性能研究[D]. 呼和浩特:内蒙古工业大学,2018.
[10] 赖德林.锌层表面疏水膜的构筑及膜层耐腐蚀行为研究[D]. 广州:华南理工大学,2018.
备注/Memo
收稿日期:2020-06-20;修回日期: 2020-07-12
通讯作者: 孙伟(1981—),女,硕士,副教授,主要研究方向:建筑结构材料,表面改性技术等。Email:sun_huang0619@
126.com
基金项目: 青岛黄海学院校级科研项目(2019KJ04)