CAO Xinshuai,CHEN Yunrui,BAI Yahui,et al.Effect of Sealing Process on Corrosion Resistance of Thin Nickel[J].Plating & Finishing,2021,(10):36-40.[doi:10.3969/j.issn.1001-3849.2021.10.007]
封闭工艺对薄镍耐蚀性的影响
- Title:
- Effect of Sealing Process on Corrosion Resistance of Thin Nickel
- 文献标志码:
- A
- 摘要:
- 为提高薄镍耐腐蚀性能，研制了一种由成膜物质、辅助成膜物质及表面活性剂复配而成的水溶性封闭剂，对碳钢表面3 ?m镍层进行封闭处理。结果表明，以硬脂酸钠、三乙醇胺、钼酸钠和十二烷基磺酸钠等成分复配的封闭剂使薄镍具有良好的耐蚀性；经过封闭处理以后，腐蚀电位由208 mV上升为300 mV，腐蚀电流由16.78 μA·cm-2下降至11.40 μA·cm-2，镍表面接触角由92.99 °增大到104.99 °，耐中性盐雾试验时间由0.5 h增加到5.0 h。
- Abstract:
- In order to improve the corrosion resistance of thin nickel, a water-soluble sealant consisting of film-forming substance, auxiliary film-forming substance and surfactant was developed to seal the 3 ?m nickel layer on the surface of carbon steel. The experimental results showed that the sealing agent compounded with sodium stearate, triethanolamine, sodium molybdate and sodium dodecyl sulfonate made the thin nickel with good corrosion resistance. After sealing treatment, the corrosion potential increased from 208 mV to 300 mV, the corrosion current decreased from 16.78 μA·cm-2 to 11.40 μA·cm-2, the contact angle of the nickel surface increased from 92.99 ° to 104.99 °, and the neutral salt spray resistance test time increased from 0.5 h to 5.0 h.
参考文献/References:
[1] Mao S D, Yang H X, Song Z L, et al. Corrosion behaviour of sintered NdFeB deposited with an aluminium coating[J]. Corrosion Science, 2011, 53(5): 1887-1894.
[2] 张东洋, 邵阳阳, 靳惠明. 电镀镍层表面封孔工艺的研究[J]. 化学工程与装备, 2017, (1): 17-18.
Zhang D Y, Shao Y Y, Jin H M. Research on surface sealing process of electroplated nickel layer[J]. Chemical Engineering and Equipment, 2017, (1):17-18 (in Chinese).
[3] 王宗雄, 彭海泉, 王超, 等. 多层镀镍工艺及相关配方[J]. 电镀与涂饰, 2015, 34(16): 940-952.
Wang Z X, Peng H Q, Wang C, et al. Multi-layer nickel plating process and related formulations[J]. Electroplating & Coating, 2015, 34(16): 940-952 (in Chinese).
[4] 李红玲, 刘双枝. 金属表面无铬替代处理技术的研究进展[J]. 表面技术, 2013, 42(2): 112-115.
Li H L, Liu S Z. Research progress of chromium-free alternative treatment technology on metal surface[J]. Surface Technology, 2013, 42(2): 112-115 (in Chinese).
[5] Mrdak M R. Characterization of nickel graphite sealing coatings in the system with the nickel-aluminum bonding coating[J]. Vojnotehni?ki Glasnik, 2013, 61(1): 69-88.
[6] 石海明, 黄章崎, 王春霞, 等. 镍阳极溶解的工艺优化与性能调控[J]. 电镀与精饰, 2020, 42(327): 1-7.
Shi H M, Huang Z Q, Wang C X, et al. Process optimization and performance control of nickel anode dissolution[J]. Plating and Finishing, 2020, 42(327): 1-7 (in Chinese).
[7] 惠建科. 滚镀钢壳钝化剂及钝化工艺的开发[D]. 湘潭: 湘潭大学, 2012.
[8] 李晶, 李红, 于化东, 等. 碳钢超疏水表面制备及其耐腐蚀性研究[J]. 中国机械工程, 2016, (23): 3241-3246.
Li J, Li H, Yu H Det al. Preparation and corrosion resistance of carbon steel super-hydrophobic surface[J]. China Mechanical Engineering, 2016, (23): 3241-3246 (in Chinese).
[9] 刘晓辉, 欧阳贵, 李鑫庆, 等. 阳极氧化化学染色膜封孔工艺的研究[J]. 电镀与环保, 2016, 36(5): 37-39.
Liu X H, Ouyang G, Li X Q, et al. Research on the sealing technology of anodized chemical dyeing film[J]. Plating & Environmental Protection, 2016, 36(5): 37-39 (in Chinese).
相似文献/References:
[1]黎小阳,郭崇武*.铸铁件氯化钾镀锌与石墨烯封闭工艺[J].电镀与精饰,2022,(8):58.[doi:10.3969/j.issn.1001-3849.2022.08.010]
LI Xiaoyang,GUO Chongwu*.Process for Potassium Chloride Zinc Plating and Graphene Sealing on Cast Iron Parts[J].Plating & Finishing,2022,(10):58.[doi:10.3969/j.issn.1001-3849.2022.08.010]
备注/Memo
收稿日期： 2020-06-02；修回日期： 2020-09-29
作者简介： 曹鑫帅（1996—），男，硕士，email：1059840549@qq.com
通信作者： 王春霞，email：wcx95@163.com