CHAO Yaojie*,LIU Jifei,JU Min,et al.Influence of Electroless Nickel Plating Times on the Fatigue Properties of TC2 Titanium Alloy[J].Plating & Finishing,2022,(7):19-23.[doi:10.3969/j.issn.1001-3849.2022.07.004]
化学镀镍次数对TC2钛合金疲劳性能影响
- Title:
- Influence of Electroless Nickel Plating Times on the Fatigue Properties of TC2 Titanium Alloy
- 分类号:
- TG174.4
- 文献标志码:
- A
- 摘要:
- 为研究化学镀镍次数对钛合金疲劳性能的影响,选取 TC2 钛合金作为代表材料,采用疲劳试验机和扫描电子显微镜对其空白试样与 3 次和 5 次化学镀镍返修试样的疲劳寿命和疲劳断口形貌进行了测试分析。旋转弯曲疲劳试验结果表明:化学镀镍返修次数越多, TC2 试样在高载荷条件下的疲劳寿命越低;疲劳载荷越低,化学镀镍返修次数对 TC2 的疲劳寿命影响越小;当疲劳载荷接近疲劳极限时, 5 次以内的化学镀镍次数对疲劳极限数值无影响。疲劳断口观察结果表明:随着镀镍次数的增多,疲劳断口的疲劳源数量增多,疲劳扩展区和瞬断区形貌无差别。
- Abstract:
- : In order to study the influence of the number of electroless nickel plating on the fatigue properties of titanium alloys , TC2 titanium alloy was selected as the representative material. The fatigue properties of the blank specimens , three and five electroless nickel plating rework specimens were tested with a fatigue testing machine. The fatigue fracture morphology was tested and analyzed by a scanning electron microscope. The results of the rotating bending fatigue test show that the more the number of electroless nickel plating rework , the lower the fatigue life of the TC2 specimen under high load conditions. The lower the fatigue load , the less the number of electroless nickel plating rework will affect the fatigue life of TC2.When the load is close to the fatigue limit , the number of electroless nickel plating has little effect on the fatigue life value. Fatigue fracture observation results show that the number of fatigue sources of fatigue fracture increases , with the increase of nickel plating times. There is no difference in the morphology of fatigue expansion zone and instantaneous fracture zone.
参考文献/References:
[1] Rajakumaran R, Anupriya J, Chen S M. 2D-Titanium carbide MXene/RGO composite modified electrode for selective detection of carcinogenic residue furazolidone in food and biological samples[J]. Materials Letters, 2021, 297: 129979.
[2] Hjk A, Mh B, Ssp C, et al. Microstructures and biological properties of 3D-printed titanium intervertebral spacer with the tri-calcium phosphate loaded demineralized bone matrix hydrogel[J]. Materials Letters, 2021, 303: 130519.
[3] Meng Q K,Xu J D,Li H,et al. Phase transformations and mechanical properties of a Ti36Nb5Zr alloy subjected to thermomechanical treatments[J]. Rare Met, 2022, 41: 209-217.
[4] 陈君 , 阎逢元 , 王建章 . 海水环境下 TC4 钛合金腐蚀磨损性能的研究 [J]. 摩擦学学报 , 2012, 32(1): 1-6.
[5] 林翠 , 梁静 , 赵晴 , 等 . TA15 钛合金腐蚀加工工艺研究 [J]. 材料工程 , 2010, 8: 51-55.
[6] Pruett J P, Clement D J, Carnes D L. Cyclic fatigue testing of nickel-titanium endodontic instruments[J]. Journal of Endodontics, 1997, 23(2): 77-85.
[7] Naydenkin E V, Soldatenkov A P, Mishin I P, et al. Very high cycle fatigue failure of near β titanium alloy[J]. Physical Mesome chanics, 2021, 24(3): 326-334.
[8] Hui L, Xie L Y, Liu J Z, et al. Study on microstructure and fatigue fracture properties of TC2 titanium alloy welded joints[J]. Journal of Aeronautical Materials, 2004, 24(3): 48-51.
[9] 宁铮 , 赵晴 , 陈庆龙 , 等 . 钛合金化学镀镍层结合力影响因素探讨 [J]. 材料保护 ,2010, 2: 33-35.
[10] 胡水莲 , 陈云鹏 , 程宗辉 , 等 . 化学镀镍次数对 TC6 钛合金性能的影响 [J]. 电镀与精饰 , 2019, 41(4): 10-13.
[11] 程琳 , 李丽 , 蒋金海 , 等 . 前处理工艺对钛合金化学镀镍性能的影响 [J]. 电镀与精饰 , 2019, 41(2): 10-14.
[12] 陈学成 , 程德 , 佟晓波 , 等 . 航天器用钛合金表面镀覆技术 [J]. 宇航材料工艺 , 2019, 49(5): 58-62.
[13] 钟群鹏 , 赵子华 . 断口学 [M]. 北京 : 高等教育出版社 , 2006.
[14] 束德林 . 工程材料力学性能 [M]. 北京 : 机械工业出版社 , 2004.
备注/Memo
收稿日期: 2021-10-06 修回日期: 2022-03-11 作者简介: 晁耀杰( 1988 — ),男,硕士,工程师,主要从事航空装备修理相关的技术及研究工作。 Email : chaoyaojie@163.com 基金项目: 大连市高层次人才创新支持计划项目( 2020RQ094 ),大连市揭榜挂帅科技攻关项目( 2021JB12GX007 ) .