- Title:
- Corrosion failure analysis on the welding line of gas compressor inlet pipeline flange
- Keywords:
- pipeline flange ; corrosion failure ; electrochemical corrosion
- 分类号:
- TG172.2
- 文献标志码:
- A
- 摘要:
- 对失效部位试样的化学成分、金相组织和显微硬度进行研究,通过扫描电镜、能谱分析和 X 射线衍射分析失效工件的腐蚀产物形貌和腐蚀产物组成,选用 S 2- 溶液和 S 2- 、 Cl - 混合溶液对试样进行电化学腐蚀对比实验。结果表明:气压机管线法兰焊缝腐蚀原因是法兰材质不符合标准,法兰与短接管的焊缝属于异种金属不等壁厚焊接,导致焊缝耐腐蚀性下降,在潮湿环境中与硫化物、氯化物等腐蚀介质发生综合作用,焊缝发生快速腐蚀,导致气压机管线法兰焊缝腐蚀、失效。
- Abstract:
- : The chemical composition , metallographic structure and microhardness of the failure parts samples were studied and the morphology and composition of corrosion products were analyzed by scanning electron microscope , energy spectrum analysis and X-ray diffraction test. The electrochemical behavior of the samples in different electrolyte was used to carry out the electrochemical corrosion comparison test , and the electrolyte was S 2- solution and S 2- , Cl - mixed solution , respectively. The results show that the reason for the corrosion of the flange weld is that the material of the flange does not meet the standard , and the weld of the flange and short pipe is dissimilar materials and unequal wall welding , which leads to the decrease of the corrosion resistance of the weld. Under the humid environ ment , the comprehensive interaction of weld with sulfide , chloride and other corrosive media , the corrosion of weld occurs rapidly , which resulting in the corrosion and failure of pneumatic pipeline flange.
参考文献/References:
[1] 胡章枝 , 周学杰 , 吴军 . Q235 碳钢在石化大气环境中初期腐蚀行为 [J]. 装备环境工程 , 2011, 8(3): 30-33.
[2] 杜存臣 , 林慧珠 . 天燃气管道的腐蚀与防护 [J]. 化工装备技术 , 2004, 25(2): 63-65.
[3] Feliu S, Morcillo M, Feliu S J. The prediction of atmospheric corrosion from meteorological and pollution parameters-I. annual corrosion[J]. Corrosion Science, 1993, 34(3): 403-414.
[4] Bhaumik M, Raju K, Arunachellan I, et al. High-performance supercapacitors based on doped polyaniline nanotubes decorated with Ni(OH) 2 nano sponge and on ion-like carbons derived from used car tyres [J]. Electrochimica Acta, 2020, 342: 136111.
[5] 于利宝 , 徐兆东 , 孙海星 , 等 . 剥离 PE 防腐层破损点下钢质管线的阴极保护 [J]. 全面腐蚀控制 , 2016, 30(11): 41-44.
[6] Wang C Y, Qi Z F. Chemical composition and property of atmospheric corrosion resistant steel[J]. Special Steel, 1997, 18(1): 13-19.
备注/Memo
收稿日期: 2022-02-07 修回日期: 2022-03-24 * 通信作者: 付亮( 1983 —),男,硕士研究生,讲师, email : 289494984@qq.com 基金项目: 2021 年度吉林省职业教育与成人教育教学改革研究课题:产教融合背景下吉林省高职院校双师型师资队伍建设研究( 2021ZCY108 )?/html>