WEI Yaping*,LV Peng,LV Chengbin,et al.魏亚平1*，吕 鹏1，吕成斌1，于喜彬2，蒋 杰3，齐凤垣1[J].Plating & Finishing,2021,(2):44-46.[doi:10.3969/j.issn.1001-3849.2021.02.0090]
硫酸盐镀锌光亮剂的研究
- Title:
- 魏亚平1*，吕 鹏1，吕成斌1，于喜彬2，蒋 杰3，齐凤垣1
- 文献标志码:
- A
- 摘要:
- 对ZL-94型宽温全光亮硫酸盐镀锌光亮剂的性能及其对镀层质量的影响进行了研究，并与其他光亮剂进行了比较。结果表明：该光亮剂耐盐性、耐温性较好，光亮剂不易被析出，光亮剂消耗量低，电镀电流密度范围宽，镀层光亮且均匀，结晶细致，结合力、脆性和延展性好，能满足产品质量要求，可应用于线材、带材和板材镀锌等。
- Abstract:
- The properties of ZL-94 zinc plating brightener with wide temperature and full brightness and its effect on coating quality were studied and compared with other brighteners. The results showed that the brightener was not easy to precipitate and had many advantages, such as good salt resistance and temperature resistance, low consumption of brightener, wide range of electroplating current density, bright and uniform coating, fine crystallization, good adhesion, brittleness and ductility, which can meet the requirements of product quality, and can be applied to galvanizing wire, strip and sheet.
参考文献/References:
[1] 王孝殚, 邹常诗, 郭振良, 等. 一种新的硫酸盐镀锌光亮剂的研制[J]. 表面技术, 2003, 32(1): 46-48.
Wang X R, Zou C S , Guo Z L, et al. Study on a new brightener for sulfate Zn-plating[J]. Surface Technology, 2003, 32(1): 46-48 (in Chinese).
[2] 张骐, 詹中伟, 孙志华, 等. 以烷基糖苷为载体的复合光亮剂对硫酸盐镀锌的影响[J]. 电镀与涂饰, 2018, 37(13): 561-565.
Zhang Q, Zhan Z W, Sun Z H, et al. Effect of a composite brightener containing alkyl glycoside as carrier on zinc electroplating in sulfate bath [J]. Electroplating & Finishing, 2018, 37(13): 561-565 (in Chinese).
[3] 张体群, 陆萍, 周宁雅, 等. 光亮添加剂在硫酸盐电镀锌钢丝生产中的应用[J]. 金属制品, 2011, (1): 45-48.
Zhang T Q, Lu P, Zhou N Y, et al. Application of bright additive to sulfate bethanizing[J]. Steel Wire Products, 2011, (1): 45-48 (in Chinese).
[4] 肖鑫, 郭贤烙, 易翔, 等. 光亮硫酸盐镀锌工艺研究[J]. 腐蚀与防护, 2000, 21(11): 498-501.
Xiao X, Guo X L, Yi X, et al. Study on the technology of bright zinc electroplating in sulfate solution [J]. Corrosion & Protection, 2000, 21(11): 498-501 (in Chinese).
相似文献/References:
[1]焦 莎,等.doi: 10.3969/j.issn.1001-3849.2025.01.005 氯化钾镀锌层表面不同颜色钝化膜的结构及耐蚀性分析[J].电镀与精饰,2025,(01):29.
Wang Shuaixing*,Du Nan.Microstructure and corrosion resistance analysis of different colored passive films on the surface of zinc coating obtained from potassium chloride system Jiao Sha1, 2, Liu Yan1, 2, Zhang Xiaobin1, 2, Zhang Tao3, Zhao Chao3,[J].Plating & Finishing,2025,(2):29.
备注/Memo
收稿日期：2020-09-20；修回日期：2020-10-15
通信作者：魏亚平，email：845716810@qq.com