WANG Chunlan,XIE Yanting,WANG Xingcan?,et al.Research Progress on the Interaction Between Cathodic Protection and Outer Coating of Pipeline[J].Plating & Finishing,2021,(8):59-62.[doi:10.3969/j.issn.1001-3849.2021.08.013]
管道阴极保护与外涂层相互影响的研究进展
- Title:
- Research Progress on the Interaction Between Cathodic Protection and Outer Coating of Pipeline
- 文献标志码:
- A
- 摘要:
- 阴极保护和外涂层是长输管道防腐蚀的必要措施,本文讨论了管道外涂层和阴极保护共存时相互作用、相互影响的因素。首先总结了管道外涂层种类、缺陷和环境对阴极保护电流渗透的影响,其次概述涂层的剥离、缝隙、破损和硫酸盐还原菌对阴极保护性能的影响,然后概括了管道钢阴极保护对涂层结合力、涂层剥离、涂层电阻和应力腐蚀断裂的影响。指出了研究管道外涂层和阴极保护相互作用的重点问题。
- Abstract:
- Cathodic protection and outer coating were the necessary measures to prevent corrosion of long-distance pipelines. In this paper, the interactional factors related to the coexist of cathodic protection and outer coating was discussed. Firstly, the influences of pipeline outer coating types, defects and environment on cathodic protection current penetration were introduced. Secondly, the effect of coating peeling, cracks, damage and sulfate-reducing bacteria on cathodic protection performance were summarized. Thirdly, the effects of pipeline steel cathodic protection on coating adhesion, peeling, the resistance and stress corrosion fracture were clarified. Finally, the key issues were pointed out in further studying the interaction between pipeline outer coating and pipeline cathodic protection.
参考文献/References:
[1] Saleem B, Ahmed F, Rafifiq M A, et al. Stress corrosion failure of an X52 grade gas pipeline[J]. Engineering Failure Analysis, 2014, 46, 157-165.
[2] Song F M. Predicting the chemistry, corrosion potential and corrosion rate in a crevice formed between substrate steel and a disbonded permeable coating with a mouth[J]. Corrosion science, 2012, 55, 107-115.
[3] Kuang D, Cheng Y F. Study of cathodic protection shielding under coating disbondment on pipelines[J]. Corrosion Science, 2015, 99, 249-257.
[4] 于利宝, 徐兆东, 孙海星, 等. 剥离PE防腐层破损点下钢质管线的阴极保护[J]. 全面腐蚀控制, 2016, 30(11): 41-44.
Yu L B, Xu Z D, Sun H X, et al. Cathodic protection of steel pipeline beneath disbonded polyethylene coating[J]. Total Corrosion Control, 2016, 30(11): 41-44 (in Chinese).
[5] Fu A Q, Cheng Y F. Characterization of the permeability of a high performance composite coating to cathodic protection and its implications on pipeline integrity[J]. Progress in Organic Coatings, 2011, 72, 423-428.
[6] Yin K, Yang Y, Cheng Y F. Permeability of coal tar enamel coating to cathodic protection current on pipelines[J]. Construction and Building Materials, 2018, 192, 20-27.
[7] 张曼曼. 埋地管道防腐层破损对阴极保护参数影响规律研究[D]. 天津: 中国民航大学机场学院, 2016.
[8] 刘波, 王树立, 杨燕, 等. 涂层孔隙率对钢质套管穿越段管道阴保电位影响规律的数值模拟[J]. 腐蚀与防护, 2016, 37(12): 961-965.
Liu B,Wang S L,Yang Y, et al. Numerical simulation of the influence rule of coating porosity on cathodic potential of pipeline in steel casing[J]. Corrosion & protection, 2016, 37(12): 961-965 (in Chinese).
[9] Kuang D, Cheng Y F. Effect of alternating current interference on coating disbondment and cathodic protection shielding on pipelines[J]. Corrosion Engineering, Science and Technology, 2015, 50(3): 211-217.
[10] Varela F, Tan M Y J, Forsyth M. Understanding the effectiveness of cathodic protection under disbonded coatings[J]. Electrochimica acta, 2015, 186, 377-390.
[11] Ashari R, Eslami A, Shamanian M. Corrosion and electrochemical conditions of pipeline steel under tape coating disbondments: effect of disbondment gap size and morphology[J]. Journal of?Pipeline?Systems Engineering and Practice, 2020, 11(1): 04019051.
[12] Wang W H, Shen K L, Yi J, et al. A mathematical model of crevice corrosion for buried pipeline with disbonded coatings under cathodic protection[J]. Journal of Loss Prevention in the Process Industries, 2016, 41, 270-281.
[13] 刘杰, 李相波, 王佳, 等. 阴极极化对人为破损907A涂层钢腐蚀行为的影响[J]. 装备环境工程, 2010, 7(3): 1-5.
Liu J, Li X B, Wang J, et al. Effect of cathodic polarization on corrosion behavior of 907A steel with coating of artificial defect[J]. Equipment Environmental Engineering, 2010, 7(3): 1-5 (in Chinese).
[14] Wei B, Mustafin F M, Bykov L I. Experimental study of changes in contact resistance of underground pipeline coatings[J]. Oil & Gas Business, 2015, 2, 156-178.
[15] Narozny M, Zakowski K, Darowicki K. Application of electrochemical impedance spectroscopy to evaluate cathodically protected coated steel in seawater[J]. Construction and Building Materials, 2018, 181, 721-726.
[16] Shi W, Lyon S B. Investigation using localised SVET into protection at defects in epoxy coated mild steel under intermittent cathodic protection simulating intertidal and splash zones[J]. Progress in Organic Coatings, 2017, 102, 66-70.
[17] Mahdavi F, Forsyth M, Mike Y J T. Understanding the effects of applied cathodic protection potential and environmetal conditions on the rate of cathodic disbondment of coatings by means of local electrochemical measurements on a multi-electrode array[J]. Progress in Organic Coatings, 2017, 103,: 83-92.
[18] 王远志, 许海波, 王廷勇. 土壤环境中阴极保护电位对涂层的影响[J]. 材料开发与应用, 2005, 20(1): 43-46.
Wang Y Z, Xu H B, Wang T Y. Influence of cathodic voltage on the coat of steel samples in soil[J]. Material Development and Application, 2005, 20(1): 43-46 (in Chinese).
[19] 曾冬冬. 阴极保护条件下3PE防腐层埋地管道补口腐蚀行为研究[D]. 长沙: 湖南大学化学化工学院, 2014.
[20] Belec L, Joliff Y. Numerical study on the evaluation of thermal and mechanical stresses during the welding of coated pipelines[J]. Progress in Organic Coatings, 2017, 111, 336-342.
[21] 张丽. 外加电流阴极极化下环氧富锌涂层的失效行为研究[D]. 北京: 北京化工大学材料科学与工程学院, 2013.
[22] Nakache M, Aragon E, Belec L, et al. Degradation of rubber to metals bonds during its cathodic delamination, validation of an artificial ageing test[J]. Progress in Organic Coatings, 2011, 72(3), 279-286.
[23] Ma H C, Zhao B, Liu Z Y, et al. Local chemistry-electrochemistry and stress corrosion susceptibility of X80 steel below disbonded coating in acidic soil environment under cathodic protection [J]. Construction and Building Materials, 2020, 243, 118203.
[24] Fu A Q, Cheng Y F. Electrochemical polarization behavior of X70 steel in thin carbonate/bicarbonate solution layers trapped under a disbonded coating and its implication on pipeline SCC[J]. Corrosion Science, 2010, 52, 2511-2518.
[25] Yan M, Wang J, Han E, et al. Local environment under simulated disbonded coating on steel pipelines in soil solution[J]. Corrosion Science, 2008, 50(5): 1331-1339.
相似文献/References:
[1]杨 超 *,韩 庆,王安泉,等. 交流干扰下近中性环境中涂层失效机制研究 [J].电镀与精饰,2022,(10):9.[doi:10.3969/j.issn.1001-3849.2022.10.002]
YANG Chao *,HAN Qing,WANG Anquan,et al.Effect of AC Interference on Failure Mechanism of Coatings in Near-Neutral Solution[J].Plating & Finishing,2022,(8):9.[doi:10.3969/j.issn.1001-3849.2022.10.002]
备注/Memo
收稿日期: 2021-01-11;修回日期: 2021-03-29
作者简介: 王春兰(1980—),女,硕士,工程师, Email:15266732@qq.com