航空发动机用离子镀银紧固件的耐酸性盐雾性能研究

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG] 卷: 期数: 2022年11 页码: 12-17 栏目: 出版日期: 2022-11-15
Title:
Study on Acid Salt Spray Corrosion Resistance of Fasteners with Vacuum ion Plated Silver Coating used on Aero Engine
作者:
（1.贵州航天精工制造有限公司，贵州 遵义 563000； 2.天津市紧固连接技术企业重点实验室，天津 300300； 3.四川轻化工大学材料学院，四川 自贡 643000）
Author(s):
（1.Guizhou Aerospace Precision Manufacturing Co.， Ltd.， Zunyi 563000， China； 2.Tianjin Key Laboratory of Fastening Technology， Tianjin 300300， China； 3.College of Materials， Sichuan University of Light Chemical Technology， Zigong 643000， China）
关键词:
酸性盐雾性能; 真空离子镀银; 紧固件; 镀镍; 航空发动机
Keywords:
acid salt spray corrosion resistance ;  vacuum ion plated silver coating ;  fasteners ;  nickel plating ;  aero engine
分类号:
TB79
DOI:
10.3969/j.issn.1001-3849.2022.11.003
文献标志码:
A
摘要:
航空发动机面向海洋环境服役，对配套用紧固件提出了耐酸性盐雾性能要求。本文从真空离子镀银不同打底层工艺及后处理方法，开展了发动机用高温合金紧固件产品的耐酸性盐雾性能研究。结果表明， GH738 、 GH4169 、 GH2132 紧固件采用预镀镍工艺，涂覆 HTAg-2000 防变色剂后可以满足 192 h 酸性盐雾性能要求。采用氯化物镀镍 + 氨基磺酸盐镀镍的预镀镍工艺对紧固件酸性盐雾性能的改善效果优于氯化物镀镍 + 化学镀镍工艺。涂覆保护剂能有效提升紧固件的耐酸性盐雾性能，效果优劣排序为： HTAg-2000 ＞ BK 保护剂＞ LD-4310 保护剂。
Abstract:
： The acid corrosion resistance of fasteners is demanded when the aero engine services in ocean environment. The acid corrosion resistance of superalloy fasteners was investigated using different pre-plating nickel coats and protection coatings. The results show that GH738 、 GH4169 、 GH2132 fasteners prepared with two types of nickel coatings ， then coated with HTAg-2000 anti-discoloration film can meet the requirement of 192 h acid salt spray test. The nickel plating plus aminosulfonate nickel plating is better than chloride nickel plating plus chemical nickel plating process. The protection coatings can improve the acid salt spray corrosion resistance of fasteners ， and the effects sequence is HTAg-2000 coating ＞ BK coating ＞ LD-4310 coating.

参考文献/References:



[1] Asseya E, Abderrahim S, Hicham H, et al. Detection of corrosion depth in bolts by thermographic model[J]. Procedia Structural Integrity, 2017, 5: 1065-1071.

[2] 刘燕 , 许彦伟 , 殷小健 , 等 . 紧固件真空镀铝层耐腐蚀性能评价 [J]. 电镀与精饰 , 2020, 42(10): 12-16.

[3] Michael R I, Joshua M, Lee J K, et al. Irradiation-assisted stress corrosion cracking of type 347 316 steels irradiated in commercial pressurized water reactors[J]. Journal of Nuclear Materials, 2020, 536: 152182-152201.

[4] Osoba L O, Oladoye A M, Ogbonna V E. Corrosion evaluation of superalloys Haynes282 and Inconel718 in hydrochloric acid[J]. Journal of Alloys and Compounds, 2019, 804: 376-384.

[5] Liu L, Li Y, Wang F H. Influence of grain size on the corrosion behavior of a Ni-based superalloy nanocrystalline coating in NaCl acidic solution[J]. Electrochimica Acta, 2008, 23(5): 2453-2462.

[6] 邱星瀚 , 陈亚军 , 杨雅婷 , 等 . V2500 发动机燃烧室紧固件银镀层失效机理 [J]. 电镀与精饰 , 2021, 43(7): 1-9.

[7] Kolbinger E, Wagner S, Gollhardt A, et al. Corrosion behaviour of sintered silver under maritime environmental conditions[J]. Microelectronics Reliability, 2018, 88-90: 715-720.

[8] Perrenot P, Pairis S, Bourgault D, et al. Sulphur corrosion effect on the electrical performance of silver films elaborated by physical vapor deposition[J]. Vacuum, 2019, 163: 26-30.

[9] April M J, Tara N, Laura T, et al. Corrosion of novel reactive silver ink and commercial silver-based metallizations in diluted acetic acid[J]. Solar Energy Materials and Solar Cells, 2021, 223: 110900-110908.

[10] 高晓明 , 孙嘉奕 , 胡明 , 等 . 沉积温度及膜厚对离子镀银膜结构及摩擦学性能的影响 [J]. 机械工程材料 , 2007, 31(7): 11-14.

[11] Lidan Y, Kui X, Pan Y, et al. Surface analysis of silver-plated circuit boards in a salt-spray environment[J]. Journal of Alloys and Compounds, 2016, 688: 301-312.

[12] Manal A S, Nahla T E, Malek G, et al. Nanocrystalline silver coatings on steel by electrodeposition from non-polluting aqueous baths and its antibacterial activity[J]. Journal of the Taiwan Institute of Chemical Engineers, 2022, 132: 104212-104216.

[13] 张瑞 , 李夯 , 阮臣良 , 等 . 元素 S 对镍基合金 718 在含 H 2 S 和 CO 2 盐溶液中腐蚀行为的影响 [J]. 材料保护 , 2020, 53(3): 61-65, 77.

[14] 郭绕龙 . 提高合金钢镀银高温结合力的工艺研究 [J]. 电镀与涂饰 . 2017, 36(15): 823-826.

[15] 徐亚莉 , 张勇强 . 电接触镀银保护剂抗硫化变色机制和能力研究 [J]. 机电元件 , 2021, 41(6): 20-26.

[16] 申柯娅 . 分子自组装技术在防银表面变色中的研究与应用前景 [J]. 腐蚀与防护 , 2010, 31(1): 882-885.

[17] 罗维华 , 丁运虎 , 宣立强 , 等 . 经不同保护剂处理后的镀镍层电化学性能测试 [J]. 材料保护 , 2020, 53(2): 70-73.

[18] 代文彪 , 袁光生 , 罗元凯 , 等 . 一种真空离子镀银工艺 [P], CN201811511983.X. 2018.

[19] 胡隆伟 , 胡娅 , 杨兵 , 等 . 一种真空离子 Ag 纳米复合涂层紧固件及制备方法 [P], CN201810584163.7, 2018.

[20] 詹兴刚 , 杨兵 , 沈丽娟 , 等 . T/CSEA 15 ― 2021 真空磁控溅射镀银工艺及质量检验标准 [S]. 2021.

备注/Memo

收稿日期： 2022-03-08 修回日期： 2022-05-11 作者简介： 詹兴刚（ 1968 ―），男，高级工程师，研究方向为表面工程技术， email ： zxg0114@126.com 通信作者： 刘燕，女，高级工程师，研究方向为表面工程技术， email ： aliya0719@163.com 基金项目： 高温、高强度、高抗疲劳性发动机紧固件标准研究与验证（ Y2019-VII-0012-0173 ）

更新日期/Last Update: 2022-11-12