Jin Yongqing*,Yin Hongguo,Cun Haihong,et al.Study and control of white bar defects in hot-dip galvanized coating[J].Plating & Finishing,2024,(4):106-110.[doi:10.3969/j.issn.1001-3849.2024.04.015]
热镀锌镀层白条缺陷研究及控制
- Title:
- Study and control of white bar defects in hot-dip galvanized coating
- Keywords:
- hot dip galvanizing ; furnace nose ; white bar defect ; zinc ash ; dew point ; temperature
- 分类号:
- TG174.4
- 文献标志码:
- A
- 摘要:
- 针对热镀锌产品镀层白条缺陷，研究了其形成机理、影响因素和控制措施。结果表明，白条缺陷由炉鼻子内锌灰黏附于带钢表面而形成，其成分是 Zn 和 ZnO 。白条缺陷影响因素主要有炉鼻子密封性、露点、带钢入锌锅温度、锌锅温度和排锌灰效果。通过对上述因素进行控制及优化，有效地消除白条缺陷，达到家电用钢表面质量需求。
- Abstract:
- ： The formation mechanism ， influencing factors ， and control measures of white bar defects in hot-dip galvanized products were studied. The results indicate that the white bar defect is formed by the adhesion of zinc ash inside the furnace nose to the surface of the steel strip ， and its components are Zn and ZnO. The main factors affecting the white bar defect are sealing of the furnace nose ， dew point ， temperature of the steel strip entering the zinc pot ， zinc pot temperature ， and zinc ash removal effect. By controlling and optimizing the above factors ， the white bar defect can be effectively eliminated to meet the surface quality requirements of steel for household appliances.
参考文献/References:
[1] 吴价宝 , 张雨泉 . 控制热镀锌汽车外板锌渣缺陷的工艺创新方法 [C]// 第十二届中国钢铁年会论文集 , 北京 : 中国金属学会 , 2019: 123-128.
[2] 夏丹葵 , 戴永年 . 纯锌蒸发规律研究 [J]. 有色金属 , 1992, 44(4): 52-55.
[3] 李九岭 . 带钢连续热镀锌 ( 第 4 版 )[M]. 北京 : 冶金工业出版社 , 2019: 246-247.
[4] 崔凤伟 . 热镀锌生产中锌灰对产品表面质量的影响和解决方法 [J]. 辽宁科技学院学报 , 2010, 12(2): 13-14.
[5] 孙宁 . 连续热镀锌线在线清理锌灰应用 [J]. 山东工业技术 , 2018, 36(12): 18.
[6] 安伊宁 . 热镀锌机组锌灰产生机理及控制技术研究 [J]. 技术与市场 , 2019, 26(10): 170.
[7] 翟立刚 . 冷轧热镀锌带钢表面锌灰缺陷形成原因分析及控制 [J]. 科技资讯 ,2015, 13(9): 99.
[8] 谭运刚 , 文伟 . 热镀锌板表面锌灰缺陷的控制 [J]. 武钢技术 , 2010, 48(3): 31-33.
[9] 朱砚刚 , 彭俭 . 热镀锌板表面锌灰缺陷的形成机理及控制机制 [C]// 第十一届中国钢铁年会论文集 , 北京 : 中国金属学会 , 2017: 174-176.
[10] 刘力恒 , 车淳山 , 孔纲 , 等 . 热镀 Zn-0.2wt.%Al 镀层中 Fe-Al 抑制层失稳机理及其热力学评估 [J]. 金属学报 , 2016, 52(5): 614-624.
相似文献/References:
[1]李永迪,宫明江,于茂来,等.环保高效热镀锌合金钢丝技术研究[J].电镀与精饰,2021,(12):52.[doi:10.3969/j.issn.1001-3849.2021.12.011]
LI Yongdi,GONG Mingjiang,YU Maolai,et al.Environmental Protection and High-Efficiency Hot-Dip Zinc Alloy Steel Wire Technology Research[J].Plating & Finishing,2021,(4):52.[doi:10.3969/j.issn.1001-3849.2021.12.011]
[2]孙国庆,马永涛,冉成进,等.热镀锌中锌浮渣浸出毒性分析及探讨[J].电镀与精饰,2022,(6):37.[doi:10.3969/j.issn.1001-3849.2022.06.008]
SUN Guoqing,MA Yongtao,RAN Chengjin,et al.Analysis and Discussion on Leaching Toxicity of Zinc Scum from Hot Dip Galvanizing[J].Plating & Finishing,2022,(4):37.[doi:10.3969/j.issn.1001-3849.2022.06.008]
[3]姚金刚,徐 曦*,张会杰,等. GIS气动机构储气罐内壁防腐质量提升 [J].电镀与精饰,2022,(9):44.[doi:10.3969/j.issn.1001-3849.2022.09.008]
YAO Jingang,XU Xi*,ZHANG Huijie,et al.Improvement of Anti-Corrosion Quality of Inner Wall of Gas Storage Tank of GIS Pneumatic Mechanism[J].Plating & Finishing,2022,(4):44.[doi:10.3969/j.issn.1001-3849.2022.09.008]
[4]金永清*,李 响,蒋英箴,等.热镀锌锌液有效铝控制技术研究[J].电镀与精饰,2023,(6):73.[doi:10.3969/j.issn.1001-3849.2023.06.012]
Jin Yongqing*,Li Xiang,Jiang Yingzhen,et al.Study on effective Al control technology of hot-dip galvanizing bath[J].Plating & Finishing,2023,(4):73.[doi:10.3969/j.issn.1001-3849.2023.06.012]
[5]邓凌峰,黄 超,韩 靓 *,等. 浅谈船舶热镀锌表面处理的质量控制 [J].电镀与精饰,2023,(10):68.[doi:10.3969/j.issn.1001-3849.2023.10.011]
Deng Lingfeng,Huang Chao,Han Liang *,et al.Quality control of hot-dip galvanized surface treatment of ships[J].Plating & Finishing,2023,(4):68.[doi:10.3969/j.issn.1001-3849.2023.10.011]
备注/Memo
收稿日期： 2024-01-02 修回日期： 2024-02-06 作者简介： 金永清（ 1974 —），男，工程硕士，高级工程师， email ： 980227506@qq.com?/html>