[1]吴 敏*,黎 聪.汽车电池负极镁基合金Mg-Ni-Y-Gd的组织与性能[J].电镀与精饰,2020,(2):11-14.[doi:10.3969/j.issn.1001-3849.2020.02.003]
　WU Min*,LI Cong.Microstructure and Properties of Mg-Based Alloy Mg-Ni-Y-Gd for Automotive Battery Anode[J].Plating & Finishing,2020,(2):11-14.[doi:10.3969/j.issn.1001-3849.2020.02.003]
点击复制

汽车电池负极镁基合金Mg-Ni-Y-Gd的组织与性能

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG] 卷: 期数: 2020年2 页码: 11-14 栏目: 出版日期: 2020-02-15
Title:
Microstructure and Properties of Mg-Based Alloy Mg-Ni-Y-Gd for Automotive Battery Anode
作者:
吴 敏1*; 黎 聪2
1.浙江工业职业技术学院，浙江 绍兴，312000； 2.东风汽车集团有限公司技术中心，湖北 武汉，430056
Author(s):
WU Min1*;  LI Cong2
1. Zhejiang Industry Polytechnic College, Shaoxing 312000, China;　2. Technique Center of Dongfeng Motor Corporation, Wuhan 430056, China
关键词:
汽车电池负极材料; 球磨; 镁基合金Mg-Ni-Y-Gd; 放电性能; 耐腐蚀性能
Keywords:
anode material of automotive battery;  ball milling;  Mg-based alloy Mg-Ni-Y-Gd;  discharge performance;  corrosion resistance
DOI:
10.3969/j.issn.1001-3849.2020.02.003
文献标志码:
A
摘要:
针对目前汽车电池存在续航不足、放电不稳定等问题，采用不同的球磨工艺制备了Mg-Ni-Y-Gd和Mg2Ni汽车电池负极镁基合金，并对其组织、放电性能和耐腐蚀性能进行了测试与分析。结果表明：在500 r/min下球磨48 h后两种合金都是非晶合金。与Mg2Ni相比，Mg-Ni-Y-Gd合金腐蚀电位正移53 mV，充放电循环25次后放电容量减小13.5 %，合金的耐腐蚀性能和放电性能得到明显提高。
Abstract:
In view of the current problems of insufficient battery life and unstable discharge, Mg-based alloys for anode of automotive batteries such as Mg-Ni-Y-Gd and Mg2Ni were prepared by different ball milling process and the microstructure, discharge performance and corrosion resistance were tested and analyzed. The results showed that the two alloys were amorphous alloys after 500 r/min ball milling for 48 h. Compared with Mg2Ni alloy, the corrosion potential of Mg-Ni-Y-Gd alloy was shifted by 53 mV positively, and the discharge capacity was decreased by 13.5 % after 25 cycles of charge-discharge. The corrosion resistance and discharge performance of Mg-Ni-Y-Gd alloy were obviously improved.

参考文献/References:

[1] 张腾飞, 张娅, 夏邢燕, 等. Mg-Zn-Cu系合金作为镁电池负极材料的性能[J]. 腐蚀与防护, 2017, 38(9):705-709.
[2] 吴瑞峰, 叶金云, 胡启山, 等. 镁掺杂对正极材料尖晶石LiMn2O4电化学性能的影响[J]. 化工新型材料, 2017, (5):164-166.
[3] 华政, 梁风, 姚耀春, 等. 电动汽车电池的发展现状与趋势[J]. 化工进展, 2017, 36(8): 2874-2881.
[4] 石春梅, 曾小勤, 常建卫, 等. AZ31合金用于镁二次电池负极材料的电化学性能[J]. 中国有色金属学报, 2010, 20(5): 885-890.
[5] 周惦武, 刘金水, 卢远志, 等. 镁基储氢材料的吸放氢性能[J]. 机械工程材料, 2008, 32(4):5-9+37.
[6] 李振玲, 商国华. 21世纪电动车用电池的发展与展望[J]. 摩托车技术, 2001, (1): 21-24.
[7] 尧玉芬, 陈昌国, 刘渝萍, 等. 镁电池的研究进展[J]. 材料导报, 2009, 23(19):119-121.
[8] 韩树民, 李媛, 张忠, 等. Ni/MH电池负极用高容量稀土-镁-镍基储氢合金[J]. 西安交通大学学报, 2008, 42(3): 377-380.

备注/Memo

收稿日期： 2019-05-10；修回日期： 2019-09-26
通信作者： 吴敏（1988—）， 男， 安徽池州人， 讲师， 主要从事精密仪器及机械、汽车材料结构研究。
email： wumin_1234@sina.cn
基金项目： 国家自然科学基金项目（50875070）

更新日期/Last Update: 2020-02-10