SUN Haijing,XU Jiaxin,YAO Yuxuan,et al.Preparation and Study on Water-based Silicone Modified Epoxy-Acrylate Resin[J].Plating & Finishing,2020,(3):18-23.[doi:10.3969/j.issn.1001-3849.2020.03.004]
水性有机硅改性环氧丙烯酸树脂的制备及性能研究
- Title:
- Preparation and Study on Water-based Silicone Modified Epoxy-Acrylate Resin
- Keywords:
- acrylic resin; organsilicone; epoxy resin; waterborne paint; water absorption
- 文献标志码:
- A
- 摘要:
- 针对涂料漆膜吸水率偏高的问题,采用种子乳液、单体滴加的方法进行聚合,研究了丙烯酸用量、E-44用量、A151与D4的配比、乳化剂总量、引发剂用量、电解质种类对乳液以及漆膜性能的影响。结果表明:采用正交优化方法,可以改性涂料漆膜的吸水率,制得的乳液稳定性高。其最优配方为:AA含量为2%,E-44含量为5%,有硅单体为6.04g且A151:D4为1∶2,复合乳化剂为2.5%且OP-10:SLS为2∶1,电解质稳定剂NaHCO3为0.45%,引发剂APS为0.8%,其各项性能均满足GB/T20623-2006《建筑涂料用乳液》标准的要求。
- Abstract:
- The research was carried out aiming at the problem of high water absorption rate of acrylic resin. In this study, waterborne silicone modified epoxy acrylic resin was prepared by seed emulsion and monomer dropping polymerization. The influences of the acrylic acid dosage, E-44 dosage, A151/D4 ratio, emulsifier dosage, initiator dosage and electrolyte type on the properties of emulsion and film were respectively studied. The result showed that the prepared coating had lower water absorption rate and higher stability. With orthogonal experiment, the optimum formula of water-based silicone modified epoxy-acrylate resin was obtained, which was: AA 2 wt%, E-44 5wt%, organsilicone monomer 6.04 g, A151/D4 1∶2, compound emulsifer 2.5 wt%, OP-10:SLS 2∶1, NaHCO3 0.45 wt%, APS 0.8 wt%. And the properties all met the standard of GB/T 20623-2006 for architectural coating.
参考文献/References:
[1] 江河, 曾和平, 黎常成等. 环氧树脂改性硅丙乳液的制备及水性涂料的研究[J]. 广东化工, 2014, 41(6):3-6.
[2] 张东阳, 朱东, 王木立等. 水性涂料用丙烯酸酯乳液的研究进展[J]. 中国涂料, 2011, 26(9):14-17.
[3] 赵维, 邓宇凌, 李玉红. 甲基硅油改性丙烯酸树脂乳液的合成与性能研究[J]. 化学工程师, 2018, 271(4):5-8.
[4] 张爱黎, 田坤, 常彩彩. 改性环氧丙烯酸水性防腐涂料制备研究[J]. 电镀与精饰, 2015, 37(11):15-19.
[5] 刘海, 张爱黎, 吴松浩. 有机硅改性环氧-丙烯酸酯乳液的合成与性能研究[J]. 沈阳理工大学学报, 2011, 30(4):67-71.
[6] 侯光宇, 聂俊, 谭征兵, 等. 环氧有机硅油改性丙烯酸树脂的合成及性能[J]. 热固性树脂, 2007, 22(6):56-58.
[7] 张超灿, 李曦, 庞金兴, 等. 有机硅-丙烯酸甲酯的乳液聚合[J]. 武汉理工大学报, 2001, 23(4):29-32.
[8] 毛晶晶, 张良均, 童身毅. 有机硅改性水性环氧树脂的合成研究[J]. 广东化工, 2009, 36(1):10-12.
[9] 徐彦. 有机硅丙烯酸脂共聚乳液的合成及性能研究[D]. 苏州:热固性树脂, 2008.
[10] 殷锦捷, 周华利. 有机硅和环氧树脂复合改性聚氨酯涂料的研制[J]. 表面技术, 2010, 39(6):93-96.
[11] Rath S K, Chavan J G, Sasane S, et al. Two component silicone modified epoxy foul release coatings: Effect of modulus surface energy and surface restructuring on pseudobarnacle and macrofoulingbehavior[J]. Applied Surface Science, 2010, 256:2400-2446.
[12] Rath S K, Chavan J G, Sasane S, et al. Coatings of silicone modified epoxy via urethane linkage: segmental correlation length phase morphology thermomechanical and surface behavior[J]. Progress in Organic Coatings, 2009, 65:366-374.
[13] 卢招弟, 张爱黎, 邢文男. 有机硅改性环氧丙烯酸乳液的制备研究[J]. 沈阳理工大学学报, 2016, 35(1):98-101.
[14] 王艳姣, 强西怀, 张辉. 引发剂用量对丙烯酸树脂乳液及膜性能的影响[J]. 西部皮革, 2011, 33(22):10-15.
相似文献/References:
[1]赵荣兴,郝建军*,尹鸿鹍,等.磷酸二氢铵对水性耐腐蚀涂层的性能影响[J].电镀与精饰,2021,(1):7.[doi:10.3969/j.issn.1001-3849.2021.01.0020]
ZHAO Rongxing,HAO Jianjun*,YIN Hongkun,et al.Effect of Ammonium Dihydrogen Phosphate on the Performance of Waterborne Corrosion Resistant Coatings[J].Plating & Finishing,2021,(3):7.[doi:10.3969/j.issn.1001-3849.2021.01.0020]
[2]李 琼,李旭勇,吴 宁,等.磷化膜无铬封闭工艺研究[J].电镀与精饰,2024,(1):91.[doi:10.3969/j.issn.1001-3849.2024.01.014]
Li Qiong,Li Xuyong,Wu Ning,et al.Study on chromium-free sealing process of phosphating film[J].Plating & Finishing,2024,(3):91.[doi:10.3969/j.issn.1001-3849.2024.01.014]
备注/Memo
收稿日期: 2019-12-11;修回日期: 2020-1-12
通信作者: 张爱黎,1169674033@qq.com
基金项目: 辽宁省教育厅青年科技人才“育苗”项目(LG201928);辽宁省博士启动基金(201601181);沈阳理工大学大学生创新创业计划项目(201810144053)