ZHU Zijun,HAN Bing*,LI Kui,et al.Experimental Study on Ultrasonic-Assisted Magnetic Particle Grinding of TC4 Plane[J].Plating & Finishing,2020,(10):6-11.[doi:10.3969/j.issn.1001-3849.2020.10.0020]
超声辅助磁粒研磨TC4平面的光整试验研究
- Title:
- Experimental Study on Ultrasonic-Assisted Magnetic Particle Grinding of TC4 Plane
- Keywords:
- ultrasonic titanium alloy TC4 plane slotted pole magnetic field gradient surface roughness
- 文献标志码:
- A
- 摘要:
- 为了提高钛合金TC4表面质量，采用超声辅助磁粒研磨技术对TC4平面进行光整试验研究，研究了磁极开槽宽度与深度在不同比例下的磁场强度大小，及不同超声波振动幅度和磨粒粒径条件下对TC4表面粗糙度值的影响。结果表明：在磁极开槽宽度与深度比为1∶1，超声波振动幅度为10 μm，磨粒粒径为200 μm时，研磨加工60 min，钛合金TC4平面研磨前后的表面粗糙度值Ra由原始3.00 μm下降到0.12 μm，表面纹理去除，形貌得到明显改善，TC4平板表面材料力学属性加强，表面摩擦系数降低。
- Abstract:
- In order to improve the surface quality of titanium alloy TC4, the TC4 plane was subjected to the skin finishing test by ultrasonic assisted magnetic particle grinding technology. The effects of the magnetic field strength of the magnetic pole slot width and depth at different ratios, the different ultrasonic vibration amplitude and abrasive grains, on the surface roughness of TC4 were studied. The results showed that the surface roughness value Ra of the titanium alloy TC4 before and after planar grinding was decreased from the original 3.00 μm to 0.12 μm when the magnetic pole slot width to depth ratio was 1∶1, the ultrasonic vibration amplitude was 10 μm, the abrasive grain size was 200 μm, and the grinding process was 60 min. The surface texture was removed and the morphology was significantly improved. The mechanical properties of the TC4 flat surface material were strengthened and the surface friction coefficient was reduced.
参考文献/References:
[1] 黄旭, 李臻熙, 高帆, 等. 航空发动机用新型高温钛合金研究进展[J]. 航空制造技术, 2014, 57（7）:70-75.
Huang X, Li Z X, Gao F, et al. Recent development of high-temperature titanium alloys for aeroengine [J]. Aeronautical Manufacturing Technology, 2014, 57（7）: 70-75 （in Chinese）.
[2] 杨海吉, 邓祥伟, 韩冰, 等. 超声波辅助磁力研磨TC4薄壁细长管内表面研究[J]. 组合机床与自动化加工技术, 2018, 60（2）: 30-33.
Yang H J, Deng X W, Han B, et al. Study on the inner surface of TC4 thin-walled tube by ultrasonic vibration assisted MAF [J]. Modular Machine Tool & Automatic Manufacturing Technique, 2018, 60（2）: 30-33 （in Chinese）.
[3] 曾加恒, 陈燕, 张科丙, 等. 旋转超声辅助磁力研磨镍基合金试验研究[J]. 硬质合金, 2018, 35（3）:180-185.
Zeng J H, Chen Y, Zhang K B, et al. Experimental research on rotary ultrasonic assisted magnetic abrasive finishing of nickel based alloy[J]. Cemented Carbide, 2018, 35（3）: 180-185 （in Chinese）.
[4] 廖明, 韩冰, 陈燕, 等. 钛合金管内表面的电化学磁力研磨复合光整试验[J]. 中国表面工程, 2016, 29（3）:123-131.
Liao M, Han B, Chen Y, et al. Inner surface of titanium alloy tube by electrochemical magnetic abrasive compound finishing[J]. China Surface Engineering, 2016, 29（3）:123-131 （in Chinese）.
[5] 康璐, 陈燕, 赵杨, 等. 超声振动辅助磁力研磨协同增效机制与试验研究[J]. 航空制造技术, 2018, 61（21）: 57-62+68.
Kang L, Chen Y, Zhao Y, et al. Synergistic mechanism and experimental study of ultrasonic vibration assisted magnetic grinding [J]. Aeronautical Manufacturing Technology, 2018, 61（21）: 57-62+68 （in Chinese）.
[6] 叶恒宇, 梁存真, 覃寿同. 磁极开槽情况对磁力研磨的影响[J]. 机械设计与制造, 2018, 56（4）: 101-103+107.
Ye H Y, Liang C Z, Tan S T. Effect of magnetic pole groove on magnetic abrasive finishing [J]. Machinery Design & Manufacture, 2018, 56（4）: 101-103+107 （in Chinese）.
[7] 赵文聪, 张桂香, 陈春增. 磁力光整加工永磁极结构参数设计及仿真[J]. 机械设计与研究, 2016, 32（6）:106-109.
Zhao W C, Zhang G X, Chen C Z. Design and simulation research of the magnetic poles structure parameters on magnetic abrasive finishing system [J]. Machine Design & Research, 2016, 32（6）: 106-109 （in Chinese）.
[8] 王兰. 钛合金磨损行为及磨损机理的研究[D]. 镇江:江苏大学材料学, 2014.
[9] 彭约钧. 表面微结构在大气和水环境下的摩擦学特性研究[D]. 南京: 南京航空航天大学研究生院机电学院, 2011.
[10] 吴红艳, 张跃文, 黄珂, 等. TC4钛合金表面渗锆层的显微组织与摩擦磨损性能[J]. 机械工程材料, 2016, 40（5）: 77-80.
Wu H Y, Zhang Y W , Hang K, et al. Microstructure and friction and wear properties of Zr-alloyed layer on TC4 titanium alloy surface [J]. Materials for Mechanical Engineering, 2016, 40（5）: 77-80 （in Chinese）.
[11] Hitomi Y, Anil K S, Michael T, et al. Magnetic abrasive finishing of cutting tools for high-speed machining of titanium alloys [J]. CIRP Journal of Manufacturing Science and Technology, 2014, 7（4）: 299-304.
[12] 马付建, 栾诗宇, 罗奇超, 等. 超声辅助磁性磨料光整加工工艺对钛合金表面完整性的影响[J]. 中国表面工程, 2019, 32（2）: 128-136.
Ma F J, Luan S Y , Luo Q C, et al. Effects of ultrasonic assisted magnetic abrasive finishing on surface integrity of titanium alloy [J]. China Surface Engineering, 2019, 32（2）: 28-136 （in Chinese）.
[13] 姜海涛, 邵忠财, 魏守强. 钛合金表面处理技术的研究进展[J]. 电镀与精饰, 2010, 32（10）:15-20.
Jiang H T, Shao Z C, Wei S Q. Research progress of surface treatment techniques for titanium alloys [J]. Plating & Finishing, 2010, 32（10）: 15-20 （in Chinese）.
相似文献/References:
[1]姚知深,牛宗伟*,刘 斌,等.超声振动对65钢电解磷化膜表面形貌与耐蚀性的影响[J].电镀与精饰,2019,(9):24.[doi:10.3969/j.issn.1001-3849.2019.09.005]
YAO Zhishen,NIU Zongwei*,LIU Bin,et al.Effect of Ultrasonic Vibration on Surface Morphology and Corrosion Resistance of 65 Steel Electrolytic Phosphating Film[J].Plating & Finishing,2019,(10):24.[doi:10.3969/j.issn.1001-3849.2019.09.005]
[2]贾启华.超声波辅助化学镀工艺及性能研究[J].电镀与精饰,2020,(3):24.[doi:10.3969/j.issn.1001-3849.2020.03.005]
JIA Qihua.Study on Ultrasound-assisted Electroless Plating Technology and Properties[J].Plating & Finishing,2020,(10):24.[doi:10.3969/j.issn.1001-3849.2020.03.005]
[3]于克强*,周 锟,陈 燕.超声波辅助磁力研磨整体叶盘试验研究[J].电镀与精饰,2020,(7):42.[doi:10.3969/j.issn.1001-3849.2020.07.0090]
YU Keqiang*,ZHOU Kun,CHEN Yan.Experimental Study on Blisk by Ultrasonic Vibration Assisted MAF[J].Plating & Finishing,2020,(10):42.[doi:10.3969/j.issn.1001-3849.2020.07.0090]
[4]孙 伟,张伟华,杜秀丽.建筑结构用16Mn钢锌钙系磷化处理研究[J].电镀与精饰,2021,(4):11.[doi:10.3969/j.issn.1001-3849.2021.04.003]
SUN Wei,ZHANG Weihua,DU Xiuli.Investigation on Zinc-Calcium Phosphating Treatment of 16Mn Steel Used for Architectural Structure[J].Plating & Finishing,2021,(10):11.[doi:10.3969/j.issn.1001-3849.2021.04.003]
[5]马露,张鹏,肖棱*,等.超声波/紫外光-纳米Fe0类芬顿法处理络合态重金属废水[J].电镀与精饰,2023,(4):57.[doi:10.3969/j.issn.1001-3849.2023.04.010]
Ma Lu,Zhang Peng,Xiao Ling*,et al.Treatment of complex heavy metal wastewater by ultrasonic/ultraviolet nano-Fe 0 Fenton-like process[J].Plating & Finishing,2023,(10):57.[doi:10.3969/j.issn.1001-3849.2023.04.010]
[6]王利艳*,咸庆军.建筑结构用Q235钢超声波辅助锌-锰系磷化处理及耐蚀性研究[J].电镀与精饰,2023,(8):26.[doi:10.3969/j.issn.1001-3849.2023.08.005]
Wang Liyan*,Xian Qingjun.Study on zinc-manganese phosphating treatment and corrosion resistance of Q235 steel for construction structure[J].Plating & Finishing,2023,(10):26.[doi:10.3969/j.issn.1001-3849.2023.08.005]
备注/Memo
收稿日期： 2019-12-07；修回日期： 2020-03-10
作者简介： 朱子俊（1995—），女，硕士研究生，email: 1332624941@qq.com
通信作者： 韩冰，email：Hanb75@126.com
基金项目： 国家自然科学