YU Xibin,CHEN Jin*,MENG Dan,et al.于喜彬1,陈锦1*,孟丹2,许长庆3,吕成斌4,魏亚平4,吕鹏4[J].Plating & Finishing,2021,(3):52-54.[doi:10.3969/j.issn.1001-3849.2021.03.011]
书钉生产过程中钢丝变色问题分析
- Title:
- 于喜彬1,陈锦1*,孟丹2,许长庆3,吕成斌4,魏亚平4,吕鹏4
- 文献标志码:
- A
- 摘要:
- 本文分析了书钉过程中,电镀锌改拔钢丝轧制成型前表面变色的问题。研究发现,钢丝变色是由于钢丝电镀锌前表面除锈不彻底引起的。如果钢丝表面有氧化物,钢丝在的电镀锌后的镀锌层内有氧化物存在。钢丝电镀后放置一段时间,钢丝表面将变色。采用湿热试验对钢丝的防锈性能能进行了测试,证实了表面存在氧化物的镀锌该拔丝有较差的防锈性能。
- Abstract:
- This paper analyzes the problem of discoloration of the surface of the galvanized drawn wire during the production of staples. It is found that the discoloration of steel wire is directly related to the incomplete removal of rust from the surface of the steel wire. If the surface of the wire has oxides, some oxides are found in the galvanized zinc layer of the product. After some time, the steel wire will change the color. The damp heat test was used to test the anti-rust performance of the steel wire, the results were showed that the galvanized drawn wire with some oxides on the surface has a relatively low anti-rust ability.
参考文献/References:
[1] 安茂忠.电镀锌及锌合金发展现状[J]. 电镀与精饰, 2003, 22(6):35-40.
An M Z. Current development of zinc and zinc alloy electroplating[J]. Electroplating & Finishing, 2003, 22(6):35-40(in Chinese).
[2] 董蓓,杨成志,蔡捷,等.电镀锌钢板表面白色线状缺陷的形成机理[J]. 钢铁研究学报, 2015, 27(7):56-61,72.
Dong B, Yang C Z, Cai J, et al. Formation mechanism for white line defect on surface of electro-galvanized sheet[J]. Journal of Iron and Steel Research, 2015, 27(7):56-61,72(in Chinese).
[3] 张伦,刘红芳,蔡文祥,等. 电镀锌制绳钢丝锌层质量的改善[J]. 金属制品, 2012, 38(5):33-36,61.
Zhang L, Liu H F, Cai W X, et al. Improvement of electrogalvanizing steel wire for rope zinc coating mass[J]. Steel Wire Products, 2012 38(5):33-36,6(in Chinese).
[4] 苗青林,张丽君. 氯化物镀锌层表面粗糙度的影响因素及其控制[J]. 电镀与环保, 2012, 32(4):7-9.
Miao Q L,Zhang L J. Influence factors and control of coating surface roughness in chloride zinc plating[J]. Electroplating & Pollution Control, 2012, 32(4):7-9(in Chinese).
[5] 常秋,田华. 拉丝模工作锥角度对镀锌钢丝拉拔后锌层质量影响[J]. 金属制品, 2014, 40(3):35-37.
Chang Q, Tian H. Wire drawing die work cone angles effect on zinc layer quality after drawing galvanized steel wire[J]. Steel Wire Products, 2014, 40(3):35-37(in Chinese).
[6] 顾勤勇. 拉丝模工作锥角度对钢丝镀锌层质量的影响[J]. 金属制品, 2005, 31(2):38-42.
Gu Q Y. Effect of wire drawing dies work cone angle on zinc coat mass of steel wire[J]. Steel Wire Products, 2005, 31(2):38-42(in Chinese).
[7] 韩红芳,李小红. 氯化钾镀锌常见故障分析[J]. 电镀与环保, 2002, 22(6):5-6.
Han H F, Li X H. An analysis of the common troubles in potassium chloride zinc plating[J]. Electroplating & Pollution Control, 2002, 22(6):5-6(in Chinese).
[8] 谢洪波,张来祥. 浅谈氯化物镀锌生产中的几个问题[J]. 电镀与精饰, 2000, 19(5):59-61.
Xie H B, Zhang L X. Some problems in acid chloride zinc plating process[J]. Electroplating & Finishing, 2000, 19(5):59-61(in Chinese).
备注/Memo
收稿日期:2020-11-19
修回日期:2020-12-30
通信作者:陈锦,chen1161629293@163.com