Wang Xinhui,Hao Jianjun*,Mu Shihui,et al.Effect of lanthanum nitrate on corrosion resistance of passivation film on zinc aluminum magnesium alloy[J].Plating & Finishing,2023,(1):23-27.[doi:10.3969/j.issn.1001-3849.2023.01.004]
硝酸镧对锌铝镁合金表面钝化膜耐蚀性的影响
- Title:
- Effect of lanthanum nitrate on corrosion resistance of passivation film on zinc aluminum magnesium alloy
- Keywords:
- passive film ; lanthanum nitrate ; corrosion resistance
- 分类号:
- TG174.45
- 文献标志码:
- A
- 摘要:
- 为解决锌铝镁钢板的耐蚀性问题,以硝酸镧作为稀土添加剂在其表面制备丙烯酸树脂 - 硅烷 - 稀土钝化膜层。采用扫描电子显微镜、 X 射线衍射光谱分析、电化学工作站、中性盐雾试验等方法,研究了不同硝酸镧添加量对钝化膜结构及耐蚀性的影响。结果表明,钝化膜以堆积方式沉积到基材表面,硝酸镧添加量为 0.5% 时,耐盐雾试验时间可达到 72 h ,腐蚀电流密度降低至 1.11×10 -6 A·cm -2 ,相较于基体降低了两个数量级,耐黑变性良好。
- Abstract:
- : In order to solve the problem of corrosion resistance of zinc-aluminum-magnesium steel sheet , an acrylic resin-silane-rare earth passivation film was prepared on its surface using lanthanum nitrate as a rare earth additive. The effects of different amounts of lanthanum nitrate on the structure and corrosion resistance of passive film were studied by means of scanning electron microscope , X-ray diffraction spectrum analysis , electrochemical workstation and neutral salt spray test. The results show that the passivation film is deposited on the surface of the substrate in a stacking manner. When the addition of lanthanum nitrate is 0.5% , the corrosion resistance can reach NSST/72 h , the corrosion current density reduced to 1.11×10 -6 A·cm -2 , which is two orders of magnitude lower than that of the matrix , and the blackening resistance is good.
参考文献/References:
[1] 小松 , 厚志 , 泉谷 , 等 . 溶融 Zn-Al-Mg 系合金 めっき 鋼板 の 促進腐食環境下 における 耐食性 と 防食機構 [J]. 鐵 と 鋼 : 日本鐡鋼協會 々 誌 , 2000, 86(8): 534-541.
[2] 吴晓晓 , 孔纲 , 车淳山 , 等 . 热浸镀锌 - 铝层表面镧盐转化工艺 [J]. 电镀与涂饰 , 2015, 34(11): 621-625.
[3] Hernández-Barrios C A, Saavedra J A, Higuera S L, et al. Effect of cerium on the physicochemical and anticorrosive features of TEOS-GPTMS sol-gel coatings deposited on the AZ31 magnesium alloy[J]. Surfaces and Interfaces, 2020, 21:100671.
[4] Rodic P, Milosev I. The influence of additional salts on corrosion inhibition by cerium(III) acetate in the protection of AA7075-T6 in chloride solution[J]. Corrosion Science, 2019, 149: 108-122.
[5] 李会芬 , 邹忠利 , 李春龙 . 镀锌层表面无铬钝化工艺的研究进展 [J]. 材料保护 , 2021, 54(3): 137-143.
[6] 单凤君 , 齐国超 , 王双红 , 等 . 热镀铝锌钢表面环氧树脂 - 硅烷复合涂层及其耐蚀性能 [J]. 材料保护 , 2013, 46(12): 7-9.
[7] Morimoto Y, Honda K, Nishimura K, et al. Excellent corrosion-resistant Zn-Al-Mg-Si alloy hot-dip galvanized steel sheet "SUPER DYMA"[J]. Nippon Steel Technical Report, 2003, 87(87): 22-24.
[8] 西村 , 一実 , 新頭 , 等 . 溶融 Zn-Mg めっき 鋼板 の 耐食性 [J]. 鐵 と 鋼 : 日本鐡鋼協會 々 誌 , 2003, 89(1): 174-179.
[9] 张世欢 . 锌铝镁镀层汽车板应用分析 [J]. 世界有色金属 , 2020(13): 167-168.
[10] 张海良 , 段武兵 , 汤亮 . 锌铝镁合金镀层高强度高耐腐蚀性能桥梁缆索技术应用研究 [J]. 金属制品 , 2020, 46(4):31-37.
[11] 李辛庚 , 赵芃 , 张晋梅 . 输变电工程钢构件热喷涂锌铝镁稀土合金防腐涂层技术经济性分析 [J]. 科技创新与应用 , 2016 (31): 36.
[12] Liu J, Wang D, Gao L, et al. Synergism between cerium nitrate and sodium dodecylbenzenesulfonate on corrosion of AA5052 aluminium alloy in 3 wt.% NaCl solution[J]. Applied Surface Science, 2016, 389: 369-377.
[13] Dan Z, Jie S, Zhang L, et al. Corrosion behavior of rare earth cerium based conversion coating on aluminum alloy[J]. Journal of Rare Earths, 2010, 28: 371-374.
[14] Aballe A, Bethencourt M, Botana F J, et al. CeCl 3 and LaCl 3 binary solutions as environment-friendly corrosion inhibitors of AA5083 Al-Mg alloy in NaCl solutions[J]. Journal of Alloys and Compounds, 2001, 323: 855-858.
[15] Milosev I, Rodic P. Cerium chloride and acetate salts as corrosion inhibitors for aluminum alloy AA7075-T6 in sodium chloride solution[J]. Corrosion, 2016, 72(8): 1021-1034.
[16] Milosev I, Volaric B. Conversion coatings based on rare earth nitrates and chlorides for corrosion protection of aluminum alloy 7075-T6[J]. Corrosion, 2017, 73(7): 822-843.
[17] Zhou B, Wei X, Wang Y, et al. Effect of lanthanum addition on microstructures and corrosion behavior of ZnAl-LDHs film of 6061 aluminum alloys[J]. Surface and Coatings Technology, 2019, 379: 125056.
[18] Toorani M, Aliofkhazraei M, Golabadi M, et al. Effect of lanthanum nitrate on the microstructure and electrochemical behavior of PEO coatings on AZ31 Mg alloy[J]. Journal of Alloys and Compounds, 2017, 719: 242-255.
[19] 袁美蓉 , 卢锦堂 , 孔纲 , 等 . 热镀锌层上硅酸盐膜的耐蚀性和自愈性 [J]. 材料工程 , 2012(6): 48-53.
[20] 许满足 , 邹忠利 . 成膜温度对镁合金镧盐转化膜耐蚀性的影响 [J]. 材料保护 , 2021, 54(4): 90-93.
[21] 甘树坤 , 吕雪飞 . 铜合金表面硝酸镧稀土钝化膜的性能研究 [J]. 材料保护 , 2008, 41(8): 35-37.
[22] 孔纲 , 刘仁彬 , 卢锦堂 , 等 . 热镀锌表面镧盐转化膜生长机理的研究 [J]. 金属学报 , 2010, 46(4): 487-493.
相似文献/References:
[1]黎恒君,郝建军*. 硅烷偶联剂对热镀锌铝镁板钝化膜耐蚀性的影响 [J].电镀与精饰,2023,(5):90.[doi:10.3969/j.issn.1001-3849.2023.05.013]
Li Hengjun,Hao Jianjun*.Effect of silane coupling agent on corrosion resistance of passivation film on hot dip galvanized aluminum magnesium sheet[J].Plating & Finishing,2023,(1):90.[doi:10.3969/j.issn.1001-3849.2023.05.013]
[2]郭 蓓,王利华,王宁涛,等. 2系铝合金三价铬钝化法研究进展 [J].电镀与精饰,2023,(6):48.[doi:10.3969/j.issn.1001-3849.2023.06.008]
Guo Bei,Wang Lihua,Wang Ningtao,et al.Research progress of trivalent chromium passivating method for 2 series aluminum alloys[J].Plating & Finishing,2023,(1):48.[doi:10.3969/j.issn.1001-3849.2023.06.008]
[3]宋乙峰,王悦鼎,岳重祥*,等.表面膜层对镀锡板表面张力及印铁缩孔的影响[J].电镀与精饰,2023,(12):8.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.002]
Song Yifeng,Wang Yueding,Yue Chongxiang*,et al.Effect of surface films on surface tension of tinplate and shrinkage hole during printing?/html>[J].Plating & Finishing,2023,(1):8.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.002]
[4]李积鹏,姚 莹*,刘小华,等.无铬耐指纹热镀铝锌钢板黑斑缺陷研究[J].电镀与精饰,2024,(2):87.[doi:10.3969/j.issn.1001-3849.2024.02.012]
Li Jipeng,Yao Ying*,Liu Xiaohua,et al.Study on black spot defect of chromium-free fingerprint-resistant hot-dip aluminized zinc steel plate[J].Plating & Finishing,2024,(1):87.[doi:10.3969/j.issn.1001-3849.2024.02.012]
备注/Memo
收稿日期: 2022-03-23 修回日期: 2022-04-12 作者简介: 王薪惠( 1994 ―),女,硕士研究生, email : 2023397746@qq.com * 通信作者: 郝建军, email : hjj68881@163.com?/html>