TAN Yue,CHEN Yan*.Surface Finishing of GH4169 Tube by Electrolytic Composite Magnetic Grinding[J].Plating & Finishing,2020,(1):27-32.[doi:10.3969/j.issn.1001-3849.2020.01.006]
电解复合磁力研磨GH4169管内表面的光整研究
- Title:
- Surface Finishing of GH4169 Tube by Electrolytic Composite Magnetic Grinding
- Keywords:
- nickel?based alloy; electrolytic composite magnetic grinding; surface roughness; residual stress; passivation
- 文献标志码:
- A
- 摘要:
- 为解决GH4169合金管内表面质量问题，降低其表面粗糙度，本文采用电解复合磁力研磨光整加工方法进行了试验，研究了在电解复合磁力研磨条件下，磁粒粒径、电解液温度、电解电压对管内壁表面质量的影响，寻求了最优的工艺参数组合。结果表明，在磁粒粒径为185 μm，电解液温度为35 ℃，电解电压为9 V的条件下，采用电解复合磁力研磨法对GH4169合金管内表面加工25 min，管内表面粗糙度Ra可由原始的1.8 μm降至0.11 μm。表面缺陷得到有效去除，表面质量得到了明显的改善。管内表面残余应力由＋92 MPa转变为－68 MPa，获得了更好的应力状态，提高了表面抗疲劳强度。
- Abstract:
- In this paper, in order to improve the surface quality and reduce the surface roughness of GH4169 alloy tube, the electrolytic composite magnetic abrasive finishing method was carried out in the experiment. The effects of magnetic particle size, electrolyte temperature and electrolyte voltage on the inner surface quality of tube under electrolytic composite magnetic abrasion were studied and the optimum combination of process parameters was sought. The results show that the surface roughness of GH4169 alloy tube is reduced from 1.8 μm to 0.11 μm after electrolytic composite magnetic grinding for 25 min under the following conditions: magnetic particle size of 185 μm, electrolyte temperature of 35 ℃ and electrolytic voltage of 9 V. The surface defects were effectively removed and the surface quality was obviously improved. The residual stress on the inner surface of the tube is changed from ＋92 MPa to －68 MPa, a better stress state is obtained and the surface fatigue strength is increased.
参考文献/References:
[1] 陈燕, 曾加恒, 胡玉刚, 等. 超声复合磁力研磨加工镍基合金GH4169异形管[J]. 中国表面工程, 2018, 31(6): 118-124.
[2] Liu G, He N, Li L, et al. Cutting forces during the high speed machining of inconel 718[J]. Key Engineering Materials, 2004, 259-260: 824-828.
[3] 廖明, 韩冰, 陈燕, 等. 钛合金管内表面的电化学磁力研磨复合光整试验[J]. 中国表面工程, 2016, 29 (3): 123-131.
[4] 谭悦, 陈燕, 曾加恒, 等. 电解-磁力复合研磨对TA18内表面光整加工[J]. 电镀与涂饰, 2017, 36(5): 248-252
[5] 黄新春, 张定华, 姚倡锋, 等. 镍基高温合金GH4169 削参数对表面完整性影响[J]. 航空动力学报, 2013, 28(3): 621-628.
[6] 韩冰, 邓超, 陈燕. 球形磁极在弯管内表面磁力研磨中的应用[J]. 摩擦学学报, 2013, 33(6): 565-570.
[7] 白阿香, 魏刚, 乔宁. 表面处理对镍基合金加热管腐蚀行为影响[J]. 腐蚀科学与防护技术, 2012, 24(3): 228-231.
[8] 谭悦, 于克强, 陈燕, 等.电解-磁力复合研磨镍基高温合金实验研究[J]. 电镀与精饰, 2017, 39(12): 1-4.
[9] 许召宽, 韩冰, 陈燕, 等. 基于电解-磁力复合研磨法的表面光整加工[J]. 电镀与精饰, 2018, 40(12): 7-10.
[10] 吴昊, 张桂香, 赵文聪. 磁力研磨对440C不锈钢表面形貌的影响[J]. 电镀与精饰, 2015, 37(3): 16-19.
[11] 孙超, 张国军, 尹佳超. GH4169镍基高温合金砂带磨削表面完整性分析[J]. 金刚石与磨料磨具工程, 2016, 36(1): 74-78.
[12] 罗玉梅, 任凤章, 张伟, 等. X射线法测量多晶体材料残余应力[J]. 材料导报, 2014, 28(6): 112-114.
备注/Memo
收稿日期： 2019-06-09；修回日期： 2019-07-06
通信作者： 陈燕， email： 1336852522@qq.com
基金项目： 国家自然科学基金项目（51775258）