DU Yongtao*,WANG Jiejie,YANG Miao,et al.Effect of ZrO2 Particles Concentration on Corrosion Resistance of Ni-P/ZrO2 Composite Coatings on NdFeB[J].Plating & Finishing,2021,(5):30-35.[doi:10.3969/j.issn.1001-3849.2021.05.005]
ZrO2颗粒浓度对钕铁硼Ni-P/ZrO2复合镀层耐蚀性的影响
- Title:
- Effect of ZrO2 Particles Concentration on Corrosion Resistance of Ni-P/ZrO2 Composite Coatings on NdFeB
- 关键词:
- 耐蚀性; Ni-P/ZrO2复合镀层; ZrO2颗粒浓度; 钕铁硼
- 文献标志码:
- A
- 摘要:
- 采用化学镀技术在钕铁硼表面制备出Ni-P/ZrO2复合镀层,并研究了ZrO2颗粒浓度对复合镀层中ZrO2颗粒含量、复合镀层的形貌、孔隙率和耐蚀性的影响。结果表明,ZrO2颗粒浓度在0.5~4.0 g/L范围内时,复合镀层的耐蚀性随着ZrO2颗粒浓度增加逐步改善,在不同腐蚀介质中的平均腐蚀速率都呈现减小的趋势,主要归因于复合镀层中ZrO2颗粒含量升高以及复合镀层表面趋于光滑平整,且孔隙率明显降低。但ZrO2颗粒浓度超过一定限度后,复合镀层中ZrO2颗粒含量下降,加之孔隙率升高和表面平整度有所下降,导致耐蚀性变差。ZrO2颗粒浓度为4.0 g/L制备的复合镀层具有良好的耐蚀性,但在不同腐蚀介质中其耐蚀性存在一定的差异。该复合镀层腐蚀前后的形貌差异不太明显,而钕铁硼腐蚀前后的形貌有明显的差异,表明该复合镀层在不同腐蚀介质中的耐蚀性明显好于钕铁硼。
- Abstract:
- Ni-P/ZrO2 composite coatings were prepared on the surface of NdFeb by electroless plating, and the effect of ZrO2 particles concentration on the content of ZrO2 particles in composite coatings, the morphology, porosity and corrosion resistance of composite coatings were studied. The results showed that when ZrO2 particle concentration was in the range of 0.5~4.0 g/L, the corrosion resistance of composite coatings was gradually improved with the increase of ZrO2 particle concentration, and the average corrosion rate in different corrosive media presents a trend of decrease, which was mainly attributed to the increase of the content of ZrO2 particles in composite coatings, more uniform surface and significantly reduced porosity. However, when the ZrO2 particles concentration exceeds a certain limit, the content of ZrO2 particles in composite coatings decreased, along with the increase of porosity and the decrease of surface roughness, resulting in the deterioration of corrosion resistance. The composite coating prepared with 4.0 g/L ZrO2 particles exhibited good corrosion resistance, but its corrosion resistance varies in different corrosive media. The morphology difference of the composite coating before and after corrosion was not very significant, while the morphology difference of NdFeB before and after corrosion was significantly different, indicating that the corrosion resistance of this composite coating in different corrosive media was obviously better than that of NdFeB.
参考文献/References:
[1] 周巧英, 陈仁杰, 郭帅. 钕铁硼磁体表面高耐蚀性锌铝涂层的制备及性能研究[J]. 电镀与涂饰, 2020, 39(3): 165-170.
Zhou Q Y, Chen R J, Guo S. Preparation of highly corrosion-resistant ZnAl coating on NdFeB magnet and study on its properties[J]. Electroplating & Finishing, 2020, 39(3): 165-170 (in Chinese).
[2] 叶陈清, 游东宏, 丘翠英, 等. 钕铁硼表面镍铜磷镀层的制备及其防腐蚀性能研究[J]. 广东化工, 2019, 46(8): 44-45.
Ye C Q, You D H, Qiu C Y, et al. The preparation and corrosion resistance of electroless Ni-Cu-P coating on Nd-Fe-B permanent magnet[J]. Guangdong Chemical Industry, 2019, 46(8): 44-45 (in Chinese).
[3] Nan H C, Zhu L Q, Liu H C, et al. Protection of NdFeB magnets by corrosion resistance phytic acid conversion film[J]. Applied Surface Science, 2015(355): 126-132.
[4] 黎翻, 曾阳庆, 甘家毅, 等. 钕铁硼永磁材料腐蚀机理及表面防护技术现状[J]. 湖南有色金属, 2018, 34(1): 46-50.
Li F, Zeng Y Q, Gan J Y, et al. The corrosion mechanism and protection research status of electroless plating electroplating on NdFeB permanent magnetic materials[J]. Hunan Nonferrous Metals, 2018, 34(1): 46-50 (in Chinese).
[5] 王勇, 张祖军. 钕铁硼磁体表面化学镀 Ni-Cu-P 合金工艺及性能研究[J]. 机械工程与自动化, 2013(3): 90-91.
Wang Y, Zhang Z J. Process and performance study on electroless plating Ni-Cu-P alloy on Nd-Fe-B magnet[J]. Mechanical Engineering & Automation, 2013(3): 90-91 (in Chinese).
[6] Ma T Y, Ying H G, Yan M, et al. Electroless Ni-Co-P coatings on sintered Nd-Fe-B magnets with improved corrosion resistance[J]. Advanced Materials Research, 2009(75): 53-56.
[7] 王憨鹰, 刘炜. NdFeB磁性材料表面化学镀Ni-W-P实验研究[J]. 兵器材料科学与工程, 2010, 33(5): 91-93.
Wang H Y, Liu W. Electroless Ni-W-P alloy plating on NdFeB magnets[J]. Ordnance Material Science and Engineering, 2010, 33(5): 91-93 (in Chinese).
[8] 涂承君. 耐高温AgAl-Al2O3金属陶瓷薄膜制备、热稳定性及其光学特性研究[D]. 南京: 南京理工大学, 2015.
[9] Sassi W, Dhouibi L, Hihn J Y, et al. Corrosion protection of Cu eElectrical cable by W-Ni composite coatings doped with TiO2 nanoparticles: influence of pulse currents[J]. Journal of Materials Engineering and Performance, 2019(9): 5639-5648.
[10] Belhamra N, Boulebtina A R, Belassadi K. Effect of doping of nanoparticles on the properties of Zn-Ni composite coatings[J]. Diffusion Foundations, 2018(18): 19-26.
[11] 孟昭光. PCB镀镍金孔隙率探讨[J]. 印制电路信息, 2013(1): 53-58.
Meng Z G. PCB plating nickel gold porosity study[J]. Printed Circuit Information, 2013(1): 53-58 (in Chinese).
[12] 胡静, 王斌, 胡金铜, 等. 纳米SiO2对Ni-W-P镀层耐高温高压腐蚀性能的影响[J]. 表面技术, 2018, 47(6): 68-74.
Hu J, Wang B, Hu J T, et al. Effect of nSiO2 on corrosion resistance of Ni-W-P coating in high temperature and high pressure environment[J]. Surface Technology, 2018, 47(6): 68-74 (in Chinese).
[13] Deng S J, Jiang C, Liu T W, et al. Corrosion resistance of Al2O3-Y2O3-SiC coating on depleted uranium prepared by cathode plasma electrolytic deposition[J]. Journal of the American Ceramic Society, 2019, 102(3): 1362-1372.
[14] 马蓓蕾, 王瑞红. 镁合金表面镍钨合金镀层的制备及性能[J]. 腐蚀与防护, 2019, 40(2): 116-120.
Ma B L, Wang R H. Preparation and properties of Ni-W alloy coating on surface of magnesium alloy[J]. Corrosion & Protection, 2019, 40(2): 116-120 (in Chinese).
相似文献/References:
[1]宿 辉,栾柏瑞.AZ91D镁合金表面无铬无氟前处理工艺研究[J].电镀与精饰,2019,(1):10.[doi:10.3969/j.issn.1001-3849.2019.01.003]
XU Hui,LUAN Bairui.Study on Chromium?Free and Fluorine?Free PretreatmentProcess of AZ91D Magnesium Alloy[J].Plating & Finishing,2019,(5):10.[doi:10.3969/j.issn.1001-3849.2019.01.003]
[2]徐美玲,亢淑梅,陈婷婷,等.添加氯化铈对镁合金Ni?P化学镀镀层性能影响[J].电镀与精饰,2019,(1):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
XU Meiling,KANG Shumei,CHEN Tingting,et al.Properties of Electroless Plating Ni?P on Magnesium AlloySubstrate by Adding CeCl3[J].Plating & Finishing,2019,(5):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
[3]刘军松,刘定富,苏 琪,等.有机添加剂对电镀Zn-Ni-P合金的影响[J].电镀与精饰,2019,(7):6.[doi:10.3969/j.issn.1001-3849.2019.07.002]
LIU Junsong,LIU Dingfu,SU Qi,et al.Effect of Organic Additives on Zn-Ni-P Alloy Electroplating[J].Plating & Finishing,2019,(5):6.[doi:10.3969/j.issn.1001-3849.2019.07.002]
[4]颜晨曦,宋娟娟,曹建平,等.全氢聚硅氮烷涂层制备及其性能[J].电镀与精饰,2019,(7):14.[doi:10.3969/j.issn.1001-3849.2019.07.004]
YAN Chenxi,SONG Juanjuan,CAO Jianping,et al.Preparation and Properties of Perhydropolysilazane Coating[J].Plating & Finishing,2019,(5):14.[doi:10.3969/j.issn.1001-3849.2019.07.004]
[5]姚知深,牛宗伟*,刘 斌,等.超声振动对65钢电解磷化膜表面形貌与耐蚀性的影响[J].电镀与精饰,2019,(9):24.[doi:10.3969/j.issn.1001-3849.2019.09.005]
YAO Zhishen,NIU Zongwei*,LIU Bin,et al.Effect of Ultrasonic Vibration on Surface Morphology and Corrosion Resistance of 65 Steel Electrolytic Phosphating Film[J].Plating & Finishing,2019,(5):24.[doi:10.3969/j.issn.1001-3849.2019.09.005]
[6]李佳霖,郝建军,牟世辉.Fe2+对镁合金电化学磷化改性研究[J].电镀与精饰,2019,(10):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
LI Jialin,HAO Jianjun,MOU Shihui.Study on Electrochemical Phosphating Modification of Magnesium Alloy by Fe2+[J].Plating & Finishing,2019,(5):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
[7]雷同鑫,鞠 辉,张长科,等.电镀Ni-W-P合金在钻杆接头上的应用[J].电镀与精饰,2019,(10):38.[doi:10.3969/j.issn.1001-3849.2019.10.009]
LEI Tongxin,JU Hui,ZHANG Changke,et al.Application of Ni-W-P Alloy Prepared by Electroplating to Tool Joints[J].Plating & Finishing,2019,(5):38.[doi:10.3969/j.issn.1001-3849.2019.10.009]
[8]贾启华,许晓娟*.沉积时间对镁合金化学镀镍的影响[J].电镀与精饰,2019,(12):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
JIA Qihua,XU Xiaojuan*.Effect of Deposition Time on Direct Electroless Plating of Magnesium Alloys[J].Plating & Finishing,2019,(5):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
[9]李 博*,赵金航,肖细军.电镀锌-镍合金替代镀镉、镀镉-钛工艺研究[J].电镀与精饰,2020,(3):43.[doi:10.3969/j.issn.1001-3849.2020.03.009]
LI Bo*,ZHAO Jinhang,XIAO Xijun.Process Research on Electroplating of Zinc-Nickel Alloy Instead of Cadmium Plating and Cadmium-Titanium Plating[J].Plating & Finishing,2020,(5):43.[doi:10.3969/j.issn.1001-3849.2020.03.009]
[10]黄章崎,石海明,朱惠文,等.可溶性镍阳极对电镀镍性能的影响[J].电镀与精饰,2020,(6):1.[doi:10.3969/j.issn.1001-3849.2020.06.0010]
HUANG Zhangqi,SHI Haiming,ZHU Huiwen,et al.Effect of Soluble Nickel Anode on the Performance of Electroplated Nickel[J].Plating & Finishing,2020,(5):1.[doi:10.3969/j.issn.1001-3849.2020.06.0010]
备注/Memo
收稿日期: 2020-08-01;修回日期: 2020-09-04
通信作者: 杜涌涛,Email:du_education00@163.com
河北省青年基金项目(QN2019328