[1]陈天丽. 处理时间对建筑用热镀锌板镧盐转化膜耐蚀性的影响 [J].电镀与精饰,2022,(7):24-29.[doi:10.3969/j.issn.1001-3849.2022.07.005]
　CHEN Tianli.Effect of Treatment Time on Corrosion Resistance of Lanthanum Salt Conversion Films on Hot Galvanized Plate Used in Construction[J].Plating & Finishing,2022,(7):24-29.[doi:10.3969/j.issn.1001-3849.2022.07.005]
点击复制

处理时间对建筑用热镀锌板镧盐转化膜耐蚀性的影响
()

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG]

卷:
期数:
2022年7
页码:
24-29
栏目:
出版日期:
2022-07-15

文章信息/Info

Title:
Effect of Treatment Time on Corrosion Resistance of Lanthanum Salt Conversion Films on Hot Galvanized Plate Used in Construction
作者:
陈天丽
（郑州升达经贸管理学院 建筑工程学院，河南 新郑 451191）
Author(s):
CHEN Tianli
（Department of Architectural Engineering，Shengda Trade Economics & Management College of Zhengzhou，Xinzheng 451191，China）
关键词:
镧盐转化膜; 热镀锌板; 处理时间; 耐醋酸铅点滴时间; 盐雾实验
Keywords:
lanthanum salt conversion film ;  hot galvanized plate ;  treatment time ;  lead acetate resistance time ;  salt spray test
分类号:
TG174.4
DOI:
10.3969/j.issn.1001-3849.2022.07.005
文献标志码:
A
摘要:
将热镀锌板浸入含有柠檬酸的处理液中制备镧盐转化膜，并研究处理时间对镧盐转化膜形貌、表面成分、物相及耐蚀性的影响。结果表明：镧盐转化膜含有 Zn 、 La 、 C 和 O 元素，主要由 ZnO 和 La 2 O 3 相组成。随着处理时间延长， La 元素质量分数呈增加趋势，伴随着 Zn 元素质量分数降低，镧盐转化膜的形貌先趋于致密而后表面龟裂出现脱落现象，导致耐蚀性先逐步提高而后下降。对热镀锌板化学转化处理 8 min 后，表面出现白锈的时间延长了约 30 h ，耐醋酸铅点滴时间延长了约 40 s ，膜层电阻和电荷转移电阻都提高约 2 倍，耐蚀性明显提高。
Abstract:
： Hot galvanized plate was immersed in a treatment solution containing citric acid to prepared lanthanum salt conversion films ， and the effect of treatment time on the morphology ， surface composition ， phase and corrosion resistance of lanthanum salt conversion films was studied. The results showed that lanthanum salt conversion film contains Zn ， La ， C and O elements ， and was composed of ZnO and La 2 O 3 phase. With the extension of treatment time ， the mass fraction of La element shows an increasing trend along with the decrease of the mass fraction of Zn element ， and the morphology of lanthanum salt conversion films tend to be dense at first and then the surface cracked and fell off ， leading to the corrosion resistance increased at first and then decreased. When chemical conversion treatment of hot galvanized plate for 8 min ， the time of white rust appeared on the surface was prolonged by about 30 h ， the lead acetate resistance time was prolonged by about 40 s ， and the film resistance and charge transfer resistance were increased by about two times ， indicating that the corrosion resistance of hot galvanized plate was significantly improved.

参考文献/References:



[1] 周婉秋 , 刘艳荣 , 王建 , 等 . 热镀锌板钼酸盐转化膜制备及耐腐蚀性能研究 [J]. 沈阳师范大学学报 ( 自然科学版 ), 2013, 31(2): 148-152.

[2] 黄婷婷 , 周婉秋 , 王宇玲 , 等 . 添加剂用量对钼酸盐失效转化液再生的影响 [J]. 沈阳师范大学学报 ( 自然科学版 ), 2016, 34(1): 6-9.

[3] 赵艳 . 热浸镀锌层表面钛盐转化处理研究 [D]. 西安 : 西安建筑科技大学 , 2012.

[4] 吴晓晓 . 热浸 Galfan 镀层表面镧盐转化膜的研究 [D]. 广州 : 华南理工大学 , 2016.

[5] 甘树坤 , 刘爽 . 吕雪飞 . 金属表面耐蚀性稀土转化膜的研究进展 [J]. 吉林化工学院学报 , 2017, 34(9): 79-83.

[6] 吴海江 , 徐国荣 , 许剑光 , 等 . 热镀锌钢铈盐 / 硅烷复合膜的制备及其耐蚀性能 [J]. 材料保护 , 2013, 46(1): 16-18.

[7] 孔纲 , 吴双 , 林德鑫 , 等 . 热镀锌层柠檬酸改进型铈盐转化膜的生长机理 [J]. 中国有色金属学报 , 2012, 22(5): 1390-1397

[8] 吴海江 , 卢锦堂 . 热镀锌钢表面铈转化膜的表征与腐蚀电化学行为 [J]. 中国有色金属学报 , 2011, 21(5): 1009-1015.

[9] 史立平 , 郭瑞光 . 镀锌钢铈盐转化膜硅酸钠封闭后的耐蚀性能 [J]. 材料保护 , 2013, 46(6): 15-17.

[10] 田飘飘 , 张振海 , 徐丽萍 , 等 . 钴盐对热镀锌板有机硅烷转化膜耐腐蚀性能的影响 [J]. 材料保护 , 2013, 46(7): 13-15.

[11] 李丽洁 , 房永超 , 蔡召兵 , 等 . 镁合金无水化学转化膜表面裂纹行为的计算机模拟 [J]. 稀有金属材料与工程 , 2018, 47(2): 431-435.

相似文献/References:

[1]韩晶晶,窦国涛*.建筑用热镀锌板表面不同镧盐转化膜的制备与性能[J].电镀与精饰,2022,(2):1.[doi:doi： 10.3969/j.issn.1001-3849.2022.02.001]
　HAN Jingjing,DOU Guotao *.Preparation and Properties of Different Lanthanum Salt Conversion Films on Hot Galvanized Plate for Construction[J].Plating & Finishing,2022,(7):1.[doi:doi： 10.3969/j.issn.1001-3849.2022.02.001]

备注/Memo

备注/Memo:
收稿日期： 2021-08-05 修回日期： 2021-11-06 作者简介： 陈天丽（ 1984 －），硕士，讲师， Email ： huajing0000@126.com 基金项目： 河南省科技攻关项目（ 212102310972 ）、河南省高等学校重点科研项目（ 20B560016 ）
更新日期/Last Update: 2022-07-09