电镀镀层对帘线黏合剥离性能影响

《电镀与精饰》[ISSN:1001-3849/CN:12-1096/TG] 卷: 期数: 2024年2 页码: 30-36 栏目: 出版日期: 2024-02-15
Title:
Effect of electroplating coating on adhesion and peeling property of steel cord
作者:
（1.江苏兴达钢帘线股份有限公司，江苏 泰州 225721； 2.江苏省结构与功能金属复合材料
重点实验室；江苏 泰州 225721）
Author(s):
（1.Jiangsu Xingda Steel Tyre Cord Co.， Ltd.， Taizhou 225721， China； 2.Jiangsu Key Laboratory for Structural and Functional Metal Materials Composites， Taizhou 225721， China）
关键词:
电镀; 黄铜钢丝; 钢帘线; 黏合性能; 剥离性能
Keywords:
plating ;  brass steel wire ;  steel cord ;  adhesive property ;  peeling property
分类号:
TQ153.2
DOI:
10.3969/j.issn.1001-3849.2024.02.005
文献标志码:
A
摘要:
为研究电镀钢丝镀层对帘线黏合和剥离性能的影响，分别生产不同镀层重量、镀层铜含量和镀层表层铜含量的 Φ 1.72 mm 电镀黄铜钢丝，以相同工艺拉拔捻制为 2×0.30 HT 钢帘线，用以帘线和橡胶黏合和剥离性能测试。结果发现：当帘线镀层重量在 2.47~4.34 g?span>?/span> kg -1 、镀层铜含量在 61.30 %~66.36 % 时，帘线和橡胶建立了良好的黏合强度和黏附效果，即帘线和橡胶在此范围具有较好的黏合和剥离性能，钢丝表层铜含量在 57.82 %~62.22 % 时，帘线与橡胶的黏合和剥离性能均良好，说明此范围内表层铜含量的变化未对帘线黏合和剥离性能造成明显的或不利的影响。同时，当钢丝铜含量或表层铜含量偏低，均使得拉拔损失增加，不利于钢丝拉拔。
Abstract:
： In order to study the effect of electroplating steel wire coating on the adhesion and peeling property of steel cord ， the electroplating brass steel wire of 1.72 mm diameter was produced with different coating weight ， copper content of coating and copper content of coating surface. The 2×0.30 HT steel cord was drawn and twisted with the same technology to test the adhesion and peeling property of steel cord and rubber. The study found that when the coating weight of steel cord was in 2.47~4.34 g?/span>?g -1 ， the copper content of the coating was in 61.30 %?66.36 % ， and the adhesion strength and adhesion effect of steel cord and rubber were well established. It also meant that the steel cord and rubber had better bonding and peeling property under these conditions. The adhesion and peeling property of steel cord and rubber was good when the copper content of steel wire coating surface was in 57.82 %~62.22 % ， indicating that the change of copper content of steel wire coating surface had no obvious or adverse effect on the adhesion and peeling property of steel cord. At the same time ， when the copper percentage content or surface copper content was lower ， the steel wire drawing loss increased ， which was not conducive to steel wire drawing.

参考文献/References:



[1] 来永彪 , 赵阳 , 左锦中 , 等 . 钢帘线生产断丝原因分析 [J]. 金属制品 , 2023, 49(1): 52-55.

[2] 马海俊 , 王宝星 , 刘磊 . 不同镀层钢丝帘线黏合力在相应黏合体系中的测试、表征和分析 [J]. 轮胎工业 , 2018, 38(2): 117-120.

[3] 郜宪杰 , 陈龙 , 车树新 , 等 . 不同产地 2×0.30ST 钢丝帘线在轮胎中的应用对比 [J]. 轮胎工业 , 2023, 43(1): 43-45.

[4] Tashiro H, Tarui T. State of the art for high tensile strength steel cord[J]. Nippon Steel Technical Report, 2003(88): 87-91.

[5] 寇首鹏 , 周志嵩 , 张喜泽 , 等 . 1+6+12 与 1 +18 钢帘线微动磨损研究 [J]. 金属制品 , 2022, 48(2): 6-9.

[6] Hananto A L, Sulaiman S, Widiyanto S, et al. Evaluation comparison of wave amount measurement results in brass-plated tire steel cord using RMSE and cosine similarity[J]. Indonesian Journal of Electrical Engineering and Computer Science, 2021, 22(1): 207-214.

[7] 俞志高 , 罗奕文 , 王宝星 , 等 . 贝泰威镀层钢丝帘线在轮胎中的应用 [J]. 轮胎工业 , 2018, 38(11): 684-688.

[8] Jeon G S. Adhesion between rubber compounds and ternary-alloy-coated steel cords, Part I: Effect of cobalt plating amount in ternary-alloy-coated steel cords[J]. Journal of Adhesion Science and Technology, 2005, 19(6): 445-465.

[9] 王佳莉 , 张越 , 王宝星 , 等 . 改性硫黄对无钴天然橡胶的性能及与镀钴钢丝帘线黏合的影响 [J]. 合成橡胶工业 , 2017, 40(6): 473-476.

[10] 张宁 , 龙飞飞 , 郑涛 , 等 . 镀钴钢丝帘线在子午线轮胎带束层中的应用 [J]. 橡胶科技 , 2017(12): 32-35.

[11] 黄元昌 . 铜 - 锌 - 钴三元合金涂层钢丝帘线与橡胶的最佳黏合 [J]. 橡塑技术与装备 , 2018, 44(3): 37-41.

[12] 姚利丽 , 李呐 , 倪自飞 , 等 . 一步法替代热扩散电镀工艺对钢帘线性能影响 [J]. 电镀与精饰 , 2023, 45(4): 100-105.

[13] Buytaert G, Wang B X, Luo Y W. Superior adhesion of rubber and steel cord coated with Cu-Zn-Co ternary alloy[J]. Rubber World, 2015, 252(6): 20-24, 32.

[14] 张兰波 , 刘春芳 . 铜 - 锌 - 钴三相合金镀层钢丝帘线与无钴橡胶胶料的黏合 [J]. 世界橡胶工业 , 2016, 43(11): 29-34.

[15] 宋为 . 国产电镀黄铜生产线技术研发 [J]. 金属制品 , 2011, 37(1): 41-44, 60.

[16] Nah C, Sohn B Y, Park S-J. Adhesion of brass/cobalt/copper-plated steel cord to a typical rubber compound[J]. Journal of Adhesion Science and Technology, 2002, 16(6): 653-667.

[17] Buytaert G, Luo Y W. Study of Cu-Zn-Co ternary alloy-coated steel cord in cobalt-free skim compound[J]. Journal of Adhesion Science and Technology, 2014, 28(16): 1545-1555.

[18] Abou-Kandil A I, Awad A, Darwish N, et al. Adhesion of brass plated steel cords to natural rubber: Dynamic and statistical study of adhesion failure[J]. International Journal of Adhesion & Adhesives, 2013(44): 26-35.

[19] Vanooij W J, Harakuni P B, Buytaert G. Adhesion of steel tire cord to rubber[J]. Rubber Chemistry and Technology, 2009, 82(3): 315-339.

[20] Jeon G S, Kang U I, Jeong S W, et al. Adhesion between rubber compounds and ternary-alloy-coated steel cords. Part II: Effects of sulfur and cobalt salt in rubber compounds[J]. Journal of Adhesion Science and Technology, 2005, 19(15): 1325-1348.

相似文献/References:

[1]王晓丽,顾 海,周昭昌,等.铜镀层工艺参数优化的正交实验研究[J].电镀与精饰,2018,(12):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
　WANG Xiaoli,GU Hai,ZHOU Zhaochang,et al.Orthogonal Experimental Research on Optimization of Process Parameters of Copper Electroplating[J].Plating & Finishing,2018,(2):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
[2]王 秀.电镀智能监控系统设计[J].电镀与精饰,2018,(12):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
　WANG Xiu.Design of Intelligent Electroplating Monitoring System[J].Plating & Finishing,2018,(2):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
[3]王明亮,杨海燕,李 明,等.电镀硬金的研究现状[J].电镀与精饰,2019,(11):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
　WANG Mingliang,YANG Haiyan,LI Ming,et al.Research Progress on Hard Gold Electrodeposition[J].Plating & Finishing,2019,(2):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
[4]刘 光*,文 桦,徐启杰.基于TIA和PLC的全自动ABS塑料电镀控制系统设计[J].电镀与精饰,2020,(2):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
　LIU Guang*,WEN Hua,XU Qijie.Design of Automatic Control System for ABS Plastics Electroplating Line Based on TIA and PLC[J].Plating & Finishing,2020,(2):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
[5]宋青员,何荣祥,陈朝会,等.高度梯度微纳结构的自动化电镀制备方法[J].电镀与精饰,2020,(7):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
　SONG Qingyuan,HE Rongxiang,CHEN Chaohui,et al.Automated Electroplating for Gradient Height Micro-nano Structures Fabricating[J].Plating & Finishing,2020,(2):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
[6]雷翔霄?,徐立娟,唐春霞.基于神经网络PID算法的镀液温度控制系统[J].电镀与精饰,2020,(8):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
　LEI Xiangxiao,XU Lijuan,et al.Bath Temperature Control System Based on Neural Network PID[J].Plating & Finishing,2020,(2):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
[7]范文俊,崔红兵,王 萌,等.从三价铬溶液电沉积非晶Cr-C镀层及其性能研究[J].电镀与精饰,2020,(12):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
　FAN Wenjun,CUI Hongbing,WANG Meng,et al.Preparation and Performance Study of Amorphous Cr-C Coating Electrodeposited from Trivalent Chromium Solution[J].Plating & Finishing,2020,(2):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
[8]薛迪杰*,陈 军,陈景召.基于ZigBee的电镀生产线温度集中监控系统[J].电镀与精饰,2021,(1):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
　XUE Dijie*,CHEN Jun,CHEN Jingzhao,et al.Temperature Centralized Monitoring System of Electroplating Production Line Based on ZigBee[J].Plating & Finishing,2021,(2):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
[9]王昱开*.不锈钢工具电镀金刚石工艺研究[J].电镀与精饰,2021,(3):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
　WANG Yukai*.王昱开*[J].Plating & Finishing,2021,(2):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
[10]杨航城,田海燕.工艺参数对电镀镍钴合金及其性能的影响[J].电镀与精饰,2021,(4):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]
　YANG Hangcheng,TIAN Haiyan.Effect of Process Parameters on Electrodepositing Ni-Co Alloy and Its Properties[J].Plating & Finishing,2021,(2):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]

备注/Memo

收稿日期： 2023-05-25 修回日期： 2023-07-05 * 通信作者： 李呐（ 1991 —），硕士，工程师，主要研究方向：表面处理， email ： 13852645371@163.com?/html>

更新日期/Last Update: 2024-02-05