工艺参数对电镀镍钴合金及其性能的影响
- Title:
- Effect of Process Parameters on Electrodepositing Ni-Co Alloy and Its Properties
- 文献标志码:
- A
- 摘要:
- 在氨基磺酸盐镀液体系中,采用电沉积法制备Ni-Co合金镀层,采用SEM、XRD与维氏硬度仪分析镀层相结构、微观形貌及显微硬度,并研究了沉积电流密度、氨基磺酸钴浓度及电镀液温度对镀层微观结构与显微硬度的影响。结果表明:阴极电流密度对镀层的择优取向无显著影响,但对各衍射峰强度影响较大。氨基磺酸钴浓度对择优取向有明显影响,当浓度从6 g/L提高至18 g/L时,择优取向由双择优取向(111)与(220)转至单择优取向(111),且金属晶粒更为细化。钴盐浓度提升还有利于提高镀层的显微硬度,钴盐浓度为18 g/L时比浓度为6 g/L时的显微硬度提高约44.56 %。溶液温度35~45 ℃,电流密度2 A/dm2时,可获得具有良好的表面质量与显微硬度合金镀层。
- Abstract:
- Ni-Co alloy coating was electrodeposited on the surface of the stainless steel 304 in the sulfamate plating system. The phase structure, microstructure and microhardness of the coating were analyzed by SEM, XRD and vickers hardness tester. The effects of deposition current density, cobalt sulfamate concentration and electrodepositing temperature on the microstructure and microhardness of the coating were investigated. The results show that the cathode current density had no significant effect on the phase structure of the coating, but a great influence on the peak strength. The concentration of cobalt sulfamate had a significant effect on the preferred orientation, which was changed from double preferred orientations (111) and (220) to a single preferred orientation (111) with the concentration increased from 6 g/L to 18 g/L. In addition, the metal grains became refined with the concentration increased. Increasing the concentration of cobalt salt was also conducive to improve the microhardness of the coating, which was increased by about 44.56% when the cobalt salt concentration increased from 6 g/L to 18 g/L. The alloy coating with good surface quality and microhardness could obtain when the solution temperature of 35~45 °C and deposition current density of 2 A/dm2.
参考文献/References:
[1] 王伊卿,赵文轸,唐一平,等.Ni-Co合金电铸工艺及性能研究[J]. 兵器材料科学与工程, 2000, 3:39-43.
Wang Y Q, Zhao W Z, Tang Y P, et al. Study on electroforming processing and properties of Ni-Co alloy [J]. Ordnance Material Science and Engineering, 2000, 3:39-43 (in Chinese).
[2] 刘学武.高频脉冲电镀镍钴合金内应力、形貌和结构及耐磨性的研究[D]. 北京:北京交通大学,2014.
[3] Karpuz A, Kockar H, Alper M, et al. Electrodeposited Ni-Co films from electrolytes with different Co contents [J]. Applied Surface Science, 2012, 258(8): 4005-4010.
[4] Tian L, Xu J, Xiao S. The influence of pH and bath composition on the properties of Ni-Co coatings synthesized by electrodeposition [J]. Vacuum, 2011, 86(1): 27-33.
[5] 许伟长,戴品强,郑耀东.钴含量对电沉积纳米晶镍钴合金组织与力学性能的影响[J]. 中国有色金属学报,2010,20(1):92-99.
Xu W C, Dai P Q, Zheng Y D. Effect of Co content on structures and mechanical properties of electrodeposited nanocrystalline Ni-Co alloys [J]. The Chinese Journal of Nonferrous Metals, 2010, 20(1):92-99 (in Chinese).
[6] 马军.电沉积法制备纳米晶Ni-Co合金镀层[J]. 电镀与精饰,2019,41(6):1-4.
Ma J. Preparation of nanocrystalline Ni-Co alloy coatings by electrodeposition [J]. Plating & Finishing, 2019, 41(6):1-4 (in Chinese).
[7] Li Y, Zhang X, Hu A, et al. Morphological variation of electrodeposited nanostructured Ni-Co alloy electrodes and their property for hydrogen evolution reaction [J]. International Journal of Hydrogen Energy, 2018, 43(49): 22012-22020.
[8] Vazquez-Arenas J, Treeratanaphitak T, Pritzker M. Formation of Co-Ni alloy coatings under direct current, pulse current and pulse-reverse plating conditions [J]. Electrochimica Acta, 2012, 62: 63-72.
[9] 兰新武. Ni-Co合金镀层的制备及其应用于汽车缸套的可行性分析[J]. 电镀与环保, 2017, 37(1):25-28.
Lan X W. Preparation of Ni-Co alloy coating and feasibility analysis of Ni-Co alloy coating applied on automobile cylinder liner [J]. Electroplating & Pollution Control, 2017, 37(1):25-28 (in Chinese).
[10] 宫晓静. 高频脉冲电镀镍钴合金机械性能的研究[D]. 北京:北京交通大学,2007.
[11] 王丹,高吉成,张骥群, 等.沉积参数对Ni-Co镀层成分及微观结构影响研究[J]. 四川大学学报(自然科学版),2013,50(1):118-124.
Wang D, Gao J C, Zhang J Q, et al. Effect of deposition parameters on the composition and microstructure of electrodeposited Ni-Co films [J]. Journal of Sichuan University (Natural Science Edition), 2013, 50(1):118-124 (in Chinese).
[12] Rafailovi? L D, Karnthaler H P, Tri?ovi? T, et al. Microstructure and mechanical properties of disperse Ni-Co alloys electrodeposited on Cu substrates [J]. Materials Chemistry and Physics, 2010, 120(2): 409-416.
[13] 裴和中.镍钴合金电铸成形精密器件应用与机理的研究[D]. 昆明:昆明理工大学,2013.
相似文献/References:
[1]王晓丽,顾 海,周昭昌,等.铜镀层工艺参数优化的正交实验研究[J].电镀与精饰,2018,(12):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
WANG Xiaoli,GU Hai,ZHOU Zhaochang,et al.Orthogonal Experimental Research on Optimization of Process Parameters of Copper Electroplating[J].Plating & Finishing,2018,(4):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
[2]王 秀.电镀智能监控系统设计[J].电镀与精饰,2018,(12):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
WANG Xiu.Design of Intelligent Electroplating Monitoring System[J].Plating & Finishing,2018,(4):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
[3]马 军.电沉积法制备纳米晶Ni-Co合金镀层[J].电镀与精饰,2019,(6):1.[doi:10.3969/j.issn.1001-3849.2019.06.001]
MA Jun.Preparation of Nanocrystalline Ni-Co Alloy Coatings by Electrodeposition[J].Plating & Finishing,2019,(4):1.[doi:10.3969/j.issn.1001-3849.2019.06.001]
[4]王明亮,杨海燕,李 明,等.电镀硬金的研究现状[J].电镀与精饰,2019,(11):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
WANG Mingliang,YANG Haiyan,LI Ming,et al.Research Progress on Hard Gold Electrodeposition[J].Plating & Finishing,2019,(4):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
[5]刘 光*,文 桦,徐启杰.基于TIA和PLC的全自动ABS塑料电镀控制系统设计[J].电镀与精饰,2020,(2):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
LIU Guang*,WEN Hua,XU Qijie.Design of Automatic Control System for ABS Plastics Electroplating Line Based on TIA and PLC[J].Plating & Finishing,2020,(4):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
[6]宋青员,何荣祥,陈朝会,等.高度梯度微纳结构的自动化电镀制备方法[J].电镀与精饰,2020,(7):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
SONG Qingyuan,HE Rongxiang,CHEN Chaohui,et al.Automated Electroplating for Gradient Height Micro-nano Structures Fabricating[J].Plating & Finishing,2020,(4):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
[7]雷翔霄?,徐立娟,唐春霞.基于神经网络PID算法的镀液温度控制系统[J].电镀与精饰,2020,(8):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
LEI Xiangxiao,XU Lijuan,et al.Bath Temperature Control System Based on Neural Network PID[J].Plating & Finishing,2020,(4):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
[8]范文俊,崔红兵,王 萌,等.从三价铬溶液电沉积非晶Cr-C镀层及其性能研究[J].电镀与精饰,2020,(12):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
FAN Wenjun,CUI Hongbing,WANG Meng,et al.Preparation and Performance Study of Amorphous Cr-C Coating Electrodeposited from Trivalent Chromium Solution[J].Plating & Finishing,2020,(4):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
[9]薛迪杰*,陈 军,陈景召.基于ZigBee的电镀生产线温度集中监控系统[J].电镀与精饰,2021,(1):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
XUE Dijie*,CHEN Jun,CHEN Jingzhao,et al.Temperature Centralized Monitoring System of Electroplating Production Line Based on ZigBee[J].Plating & Finishing,2021,(4):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
[10]王昱开*.不锈钢工具电镀金刚石工艺研究[J].电镀与精饰,2021,(3):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
WANG Yukai*.王昱开*[J].Plating & Finishing,2021,(4):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
备注/Memo
收稿日期:2019-08-05;修回日期:2019-10-24
作者简介:杨航城,女,硕士,Email:838429676@qq.com