XU Fangqiang*,ZOU Songhua,ZHANG Fu,et al.Research of Anodizing at Wide Temperature in Sulfuric Acid-Potassium Sodium Tartrate Bath System[J].Plating & Finishing,2019,(12):5-9.[doi:10.3969/j.issn.1001-3849.2019.12.002]
硫酸-酒石酸钾钠宽温阳极氧化槽液体系研究
- Title:
- Research of Anodizing at Wide Temperature in Sulfuric Acid-Potassium Sodium Tartrate Bath System
- Keywords:
- sulfuric acid; potassium sodium tartrate; wide temperatures; anodizing
- 文献标志码:
- A
- 摘要:
- 为解决传统阳极氧化温度范围偏窄的问题,本文介绍了一种宽温硫酸阳极氧化槽液体系,通过对2219、2A14、5A06三种材料在不同温度条件下的阳极氧化处理,对槽液体系中的硫酸含量和添加剂含量进行了优化,并通过系列试验研究得到了不同阳极氧化温度时适用的工艺参数。结果表明,以酒石酸钾钠含量为50 g/L,硫酸含量为160~200 g/L构成的宽温阳极氧化槽液体系,可以满足5~35 ℃槽液温度条件下,铝合金阳极氧化膜层耐腐蚀性能要求。
- Abstract:
- To solve the problem of narrow temperature range of traditional anodization, an anodizing bath system at wide temperature was introduced in this paper. The anodizing tests of three material including 2219, 2A14, 5A06 under various temperatures were completed, sulfuric and additive content in bath system were optimized, applicable process parameters at different anodizing temperatures were obtained through a series of experiments.The results show that wide-temperature anodizing tank liquid system with potassium sodium tartrate content of 50 g/L and sulfuric acid content of 160-200 g/L,it can meet the requirements of corrosion resistance of aluminium alloy anodic coating at 5-35 ℃ bath temperature.
参考文献/References:
[1] 王艳芝. 铝及其合金阳极氧化技术研究的进展[J]. 材料保护, 2001, 34(9): 23.
[2] 干建群, 张敏, 刘言平, 周统昌. 铝和铝合金宽温快速阳极氧化[J]. 航空制造技术, 2005, 1: 107-108.
相似文献/References:
[1]方 舒,何 欢,叶 涛,等.辅助络合剂对无氰电镀Cu-Zn合金的影响[J].电镀与精饰,2019,(6):18.[doi:10.3969/j.issn.1001-3849.2019.06.004]
FANG Shu,HE Huan,YE Tao,et al.Effect of Auxiliary Complexing Agent on Cyanide Free Electroplating Cu-Zn Alloy[J].Plating & Finishing,2019,(12):18.[doi:10.3969/j.issn.1001-3849.2019.06.004]
[2]胡素荣*,杨文茂.浸锌溶液组分含量的滴定分析方法对比[J].电镀与精饰,2019,(11):43.[doi:10.3969/j.issn.1001-3849.2019.11.009]
HU Surong*,YANG Wenmao.Comparison of Titration Analysis Methods for Component Content of Zinc Dipping Solution[J].Plating & Finishing,2019,(12):43.[doi:10.3969/j.issn.1001-3849.2019.11.009]
[3]徐 昕,李向红*.溴化十六烷基吡啶在硫酸溶液中对钢的缓蚀性能研究[J].电镀与精饰,2021,(10):1.[doi:10.3969/j.issn.1001-3849.2021.10.001]
XU Xin,LI Xianghong*.Study on the Inhibition Action of Hexadecylpyridinium Bromide on Steel in Sulfuric Acid Solution[J].Plating & Finishing,2021,(12):1.[doi:10.3969/j.issn.1001-3849.2021.10.001]
[4]乔东伟*,李朋喜,白佳凯,等.前处理对烧结多孔钛板镀铂包覆效果影响的研究[J].电镀与精饰,2024,(2):17.[doi:10.3969/j.issn.1001-3849.2024.02.003]
Qiao Dongwei*,Li Pengxi,Bai Jiakai,et al.Study on the effect of pretreatment for platinum plating coating on sintered porous titanium plate[J].Plating & Finishing,2024,(12):17.[doi:10.3969/j.issn.1001-3849.2024.02.003]
[5]徐方强*,邹松华,孙 靖,等.硫酸-酒石酸钾钠宽温阳极化工艺对铝合金焊接质量的影响[J].电镀与精饰,2019,(11):14.[doi:10.3969/j.issn.1001-3849.2019.11.004]
XU Fangqiang*,ZOU Songhua,SUN Jing,et al.Influence of Sulfuric Acid-Potassium Sodium Tartrate Wide Temperature Anodizing on Welding Quality of Aluminium Alloy[J].Plating & Finishing,2019,(12):14.[doi:10.3969/j.issn.1001-3849.2019.11.004]
备注/Memo
收稿日期: 2019-09-23;修回日期: 2019-10-12
通信作者: 徐方强,email:xufqtj@163.com