YUAN Hewei,WANG Pei,YUAN Li.Influence of Different Sealing Methods on Propertiese of Oxalic Acid Oxidation Film on 2036 Aluminum Alloy Used in Automobile[J].Plating & Finishing,2021,(8):11-15.[doi:10.3969/j.issn.1001-3849.2021.08.003]
不同封孔方法对汽车用2036铝合金草酸氧化膜性能的影响
- Title:
- Influence of Different Sealing Methods on Propertiese of Oxalic Acid Oxidation Film on 2036 Aluminum Alloy Used in Automobile
- 文献标志码:
- A
- 摘要:
- 选取汽车用2036铝合金作基体在草酸电解液中进行阳极氧化,并采用不同方法封孔,表征了封孔前后氧化膜的微观形貌、表面成分及耐腐蚀性能。结果表明,封孔后的氧化膜的微观形貌明显不同于未封孔氧化膜,封孔氧化膜的耐蚀性明显提高,但不同封孔工艺的氧化膜的耐蚀性存在一定差异,铬酸盐封孔氧化膜的耐蚀性优于热水封孔和镍-钴盐封孔的氧化膜。
- Abstract:
- The automobile 2036 aluminum alloy was used as the substrate for anodic oxidation in oxalic acid electrolyte, and the holes were sealed by different methods. The micromorphology, surface composition and corrosion resistance of the oxide film before and after sealing were characterized. The results showed that the microscopic morphology of the sealed oxide film was obviously different from that of the unsealed film. The corrosion resistance of the sealing oxide film was significantly improved, but there were certain differences in the corrosion resistance of the oxide film with different sealing processes. The corrosion resistance of the chromate sealing oxide film was better than that of hot water sealing and nickel-cobalt salt sealing.
参考文献/References:
[1] 刘莉,张鲲,熊辉辉,等.阳极氧化工艺对 6061 铝合金草酸氧化膜耐磨耐蚀性的影响[J]. 材料热处理学报,2015, 36(11):225-232.
Liu L, Zhang K, Xiong H H, et al. Effect of anodizing process on corrosion and wear resistance of 6061 alloy anodic oxide films formed in oxalic acid[J]. Transactions of Materials and Heat Treatment, 2015, 36(11): 225-232 (in Chinese) .
[2] 刘昌明,张 弟,赵怀鹏,等.草酸阳极氧化工艺研究[J]. 铝加工,2017, 4, 42-45.
Liu C M, Zhang D, Zhao H P, et al. Study of oxalic acid oxidation process[J]. Aluminium Fabrication, 2017, 4, 42-45 (in Chinese) .
[3] Wan Y. Study on anodic oxidation and sealing of aluminum alloy[J]. International Journal of Electrochemical Science, 2018, 13(2): 2175-2185.
[4] Yang Y S, Cheng J, Liu S L, et al. Effect of NaAlO2 sealing on corrosion resistance of 2024 aluminum alloy anodized film[J]. Materials and Corrosion, 2019, 70(1):120-127.
[5] 黄允芳,蔡锡昌.铝阳极氧化膜采用复合无镍封孔工艺的研究[J]. 电镀与精饰,2017,39(3):4-8.
Huang Y F, Cai X C. Study on the composite nickel-free sealing process for the anodic aluminum oxide film[J]. Plating & Finishing, 2017, 39(3): 4-8 (in Chinese) .
[6] Wu Y C, Zhao W J, Yu J Y, et al. Influence of the self-sealing layer on the corrosion of anodic aluminum oxide films[J]. ACS Applied Nano Materials, 2018, 1(9): 5142-5147.
[7] 时军,靳惠明,李露,等.6063铝合金多种阳极氧化封孔膜性能比较[J]. 化学工程与装备,2013(1):13-15.
Shi J, Jing H M, Li L, et al. Comparison of properties of 6063 aluminum alloy anodic oxidation sealing film[J]. Fujian Chemical Industry, 2013(1): 13-15 (in Chinese) .
[8] 王玲玲,张元华,赵江招,等.复合封孔处理对汽车用5052铝合金草酸氧化膜性能的影响[J]. 电镀与精饰,2020, 42(6):8-12.
Wang L L, Zhang Y H, Zhao J Z, et al. Effect of compound sealing treatment on performances of oxalic acid oxide film on 5052 aluminum alloy for automobile[J]. Plating & Finishing, 2020, 42(6): 8-12 (in Chinese) .
[9] 冒佳卫.阳极氧化及封孔处理对2024铝合金耐腐蚀性能的影响[D]. 南京:南京邮电大学,2018.
[10] 刘莉.阳极氧化及封孔处理对2A12铝合金抗腐蚀性能的影响[D]. 成都:西南交通大学,2015.
[11] Wan Y. Study on anodic oxidation and sealing of aluminum alloy[J]. International Journal of Electrochemical Science, 2018, 13(2): 2175-2185.
[12] 周鹏,李扬,陈颖欣,等.阳极氧化膜封孔质量评定方法探讨[J]. 物理测试,2019,37(3):11-13.
Zhou P, Li Y, Chen Y X, et al. Discussion about method for testing the sealing quality of anodic oxidation film[J]. Physics Examination and Testing, 2019, 37(3): 11-13 (in Chinese) .
[13] Wu Y H, Zhao W J, Wang W R, et al. Novel anodic oxide film with self-sealing layer showing excellent corrosion resistance[J]. Scientific Reports, 2017, 7(1): 1344.
[14] 刘志远,王吉平.纳米Al2O3颗粒掺杂的锡基复合镀层的制备及耐蚀性研究[J]. 电镀与精饰,2020,42(11):1-4.
Liu Z Y, Wang J P. Preparation and corrosion resistance of tin-based composite coating doped with nano-Al2O3 particles[J]. Plating and Finishing, 2020, 42(11): 1-4 (in Chinese) .
相似文献/References:
[1]王玲玲*,张元华,赵江招,等.复合封孔处理对汽车用5052铝合金草酸氧化膜性能的影响[J].电镀与精饰,2020,(6):8.[doi:10.3969/j.issn.1001-3849.2020.06.0020]
WANG Lingling*,ZHANG Yuanhua,ZHAO Jiangzhao,et al.Effect of Compound Sealing Treatment on Performances of Oxalic Acid Oxide Film on 5052 Aluminum Alloy for Automobile[J].Plating & Finishing,2020,(8):8.[doi:10.3969/j.issn.1001-3849.2020.06.0020]
备注/Memo
收稿日期: 2020-12-29;修回日期: 2021-01-22
作者简介: 袁荷伟(1979—),男,硕士,副教授,研究方向:汽车材料、表面工程等,Emai:teacher_yuan28@163.com
基金项目: 河南省高等教育教学改革研究与实践项目(2019SJGLX735),河南交通职业技术学院校级科研项目(2020-