Wang Qingqing*,Wang Gang.Analysis and elimination of unqualified reasons for salt spray test of Ni-Cd thermal diffusion coating[J].Plating & Finishing,2023,(8):104-107.[doi:10.3969/j.issn.1001-3849.2023.08.017]
镍镉热扩散镀层盐雾试验不合格原因分析与排除
- Title:
- Analysis and elimination of unqualified reasons for salt spray test of Ni-Cd thermal diffusion coating
- Keywords:
- electroplating ; Ni-Cd thermal diffusion coating ; salt spray test ; failure analysis
- 分类号:
- TQ153.12
- 文献标志码:
- A
- 摘要:
- 针对一例镍镉热扩散镀层盐雾试验不合格问题,对电镀过程和试验过程所涉及的基体、镀层、外界环境等因素进行逐一分析和排查。结果显示,导致镍镉热扩散镀层盐雾试验不合格的原因是镀层的局部脱落和镀层孔隙。通过采取如下改进措施解决了该问题:一是采用工艺规定下限电流密度电镀;二是增加电镀过程对试片的晃动频次;三是将盐雾试验试片四周打蜡绝缘;四是严禁赤手触摸试片。
- Abstract:
- : In view of a case of unqualified salt spray test of Ni-Cd thermal diffusion coating , the factors such as substrate , coating and external environment involved in the electroplating process and test process were analyzed and checked one by one. The results show that the reasons for the disqualification of the salt spray test of the Ni-Cd thermal diffusion coating are the local peeling of the coating and the coating porosity. The following improvement measures were taken to solve the problem : ( 1 ) Electroplate with the lower current density specified by the process ; ( 2 ) Increase the shaking frequency of the test piece during the electroplating process ; ( 3 ) Wax and insulate the salt spray test specimen around ; ( 4 ) Do not touch the test piece with bare hands.
参考文献/References:
[1] 刘臣 , 孙红梅 , 马海强 , 等 . 某型航空发动机镍镉合金扩散镀层工艺研究 [J]. 航空与维修工程 , 2022(6): 88-91.
[2] 中华人民共和国航空工业部 . HB/Z31 — 82 镍镉扩散镀层通用工艺说明书 [S]. 北京 : 航空工业部第六二一研究所 , 1982.
[3] 朱永春 , 曹中秋 . 电化学与腐蚀科学 [M]. 北京 : 化学工业出版社 , 2012.
[4] 冯立明 , 王玥 . 电镀工艺学 [M]. 北京 : 化学工业出版社 , 2010.
[5] 常占河 , 柳泉 , 赵洪达 , 等 . 用电化学阻抗谱研究钢表面三种电镀镍层的耐蚀性 [J]. 材料与冶金报 , 2016, 4(15): 291-297.
[6] 彭云超 , 马凯军 , 贾犇 , 等 . 电镀 NiCoCe 合金层的制备及耐蚀性能研究 [J]. 材料保护 , 2021, 54(8): 101-108.
[7] 李晓静 , 杨青原 , 李玉明 . 电镀光亮镍脆化故障原因分析与排除 [J]. 电镀与涂饰 , 2019, 38(15): 777-779.
[8] 张允诚 , 胡如南 , 向荣 , 等 . 电镀手册 ( 上册 )[M]. 北京 : 国防工业出版社 , 1997: 317-319.
[9] 刘伟 , 高光辉 . 提升铬酸阳极化盐雾试片耐蚀性的措施 [J]. 内燃机与配件 , 2018, 3(2): 30-31.
[10] 罗刚 . 镍镉合金扩散层耐高温和耐盐雾腐蚀性 [J]. 工具技术 , 2010, 44(1): 115-116.
[11] 胡云 , 赵洪图 . 锌 - 镍合金电镀工艺及镀层耐蚀性研究 [J]. 电镀与环保 , 2018, 38(6): 21-23.
相似文献/References:
[1]王晓丽,顾 海,周昭昌,等.铜镀层工艺参数优化的正交实验研究[J].电镀与精饰,2018,(12):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
WANG Xiaoli,GU Hai,ZHOU Zhaochang,et al.Orthogonal Experimental Research on Optimization of Process Parameters of Copper Electroplating[J].Plating & Finishing,2018,(8):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
[2]王 秀.电镀智能监控系统设计[J].电镀与精饰,2018,(12):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
WANG Xiu.Design of Intelligent Electroplating Monitoring System[J].Plating & Finishing,2018,(8):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
[3]王明亮,杨海燕,李 明,等.电镀硬金的研究现状[J].电镀与精饰,2019,(11):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
WANG Mingliang,YANG Haiyan,LI Ming,et al.Research Progress on Hard Gold Electrodeposition[J].Plating & Finishing,2019,(8):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
[4]刘 光*,文 桦,徐启杰.基于TIA和PLC的全自动ABS塑料电镀控制系统设计[J].电镀与精饰,2020,(2):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
LIU Guang*,WEN Hua,XU Qijie.Design of Automatic Control System for ABS Plastics Electroplating Line Based on TIA and PLC[J].Plating & Finishing,2020,(8):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
[5]宋青员,何荣祥,陈朝会,等.高度梯度微纳结构的自动化电镀制备方法[J].电镀与精饰,2020,(7):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
SONG Qingyuan,HE Rongxiang,CHEN Chaohui,et al.Automated Electroplating for Gradient Height Micro-nano Structures Fabricating[J].Plating & Finishing,2020,(8):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
[6]雷翔霄?,徐立娟,唐春霞.基于神经网络PID算法的镀液温度控制系统[J].电镀与精饰,2020,(8):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
LEI Xiangxiao,XU Lijuan,et al.Bath Temperature Control System Based on Neural Network PID[J].Plating & Finishing,2020,(8):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
[7]范文俊,崔红兵,王 萌,等.从三价铬溶液电沉积非晶Cr-C镀层及其性能研究[J].电镀与精饰,2020,(12):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
FAN Wenjun,CUI Hongbing,WANG Meng,et al.Preparation and Performance Study of Amorphous Cr-C Coating Electrodeposited from Trivalent Chromium Solution[J].Plating & Finishing,2020,(8):37.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
[8]薛迪杰*,陈 军,陈景召.基于ZigBee的电镀生产线温度集中监控系统[J].电镀与精饰,2021,(1):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
XUE Dijie*,CHEN Jun,CHEN Jingzhao,et al.Temperature Centralized Monitoring System of Electroplating Production Line Based on ZigBee[J].Plating & Finishing,2021,(8):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
[9]王昱开*.不锈钢工具电镀金刚石工艺研究[J].电镀与精饰,2021,(3):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
WANG Yukai*.王昱开*[J].Plating & Finishing,2021,(8):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
[10]杨航城,田海燕.工艺参数对电镀镍钴合金及其性能的影响[J].电镀与精饰,2021,(4):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]
YANG Hangcheng,TIAN Haiyan.Effect of Process Parameters on Electrodepositing Ni-Co Alloy and Its Properties[J].Plating & Finishing,2021,(8):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]
备注/Memo
收稿日期: 2022-12-11 修回日期: 2023-02-14 * 通信作者: 王晴晴( 1990 ―),女,硕士研究生,工程师, email : 985699401@163.com?/html>