FAN Wenjun,CUI Hongbing,WANG Meng,et al.Preparation and Performance Study of Amorphous Cr-C Coating Electrodeposited from Trivalent Chromium Solution[J].Plating & Finishing,2020,(12):37-42.[doi:10.3969/j.issn.1001-3849.2020.12.0080]
从三价铬溶液电沉积非晶Cr-C镀层及其性能研究
- Title:
- Preparation and Performance Study of Amorphous Cr-C Coating Electrodeposited from Trivalent Chromium Solution
- 分类号:
- TQ153.1
- 文献标志码:
- A
- 摘要:
- 以316L不锈钢为基体,在不同沉积电流密度下制备了非晶Cr-C镀层,研究了沉积电流密度对镀层表面形貌、化学组成、耐腐蚀性以及表面疏水性的影响。结果表明,随着电流密度增大,镀层C含量减少,表面缺陷增多,耐腐蚀性下降,疏水性降低。在20 A/dm2电流密度下制备的Cr-C镀层表面平整无缺陷,含碳量最高,耐腐蚀性最强,对应腐蚀电流密度为5×10-9 A/dm2,表面疏水性也最强。
- Abstract:
- The amorphous Cr-C coatings were prepared under different deposition current densities on the substrate of 316L stainless steel, and the effects of deposition current density on the surface morphology, chemical composition, corrosion resistance and surface hydrophobicity of the coating were studied. The results showed that the C content of the coating decreased as the current density increased, as well as the surface defects increased, the corrosion resistance decreased, and the hydrophobicity decreased. The Cr-C coating prepared at a current density of 20 A/dm2 showed a smooth surface without defects, the highest carbon content, the best corrosion resistance with the corrosion current density of 5×10-9 A/dm2, and the strongest surface hydrophobicity.
参考文献/References:
[1] Sheibani A A, Allahkaram S R, Mahdavi S . Corrosion and tribological behavior of Ni-Cr alloy coatings electrodeposited on low carbon steel in Cr (III)-Ni (II) bath[J]. Surface and Coatings Technology, 2015, 281(4):S0257897215303042.
[2] Fedrizzi L, Rossi S, Bellei F, et al. Wear-corrosion mechanism of hard chromium coatings[J]. Wear, 2002, 253(11-12):1173-1181.
[3] Sohi M H, Kashi A A, Hadavi S M M. Comparative tribological study of hard and crack-free electrodeposited chromium coatings [J]. Journal of Materials Processing Technology, 2003, 138(1-3):219-222.
[4] Ke N S, Xin N H, Ji H Z, et al. Electrodeposited Cr-Al2O3 composite coating for wear resistance[J]. Wear, 1996, 196(1-2):295-297.
[5] Song Y B, Chin D T. Current efficiency and polarization behavior of trivalent chromium electrodeposition process[J]. Electrochimica Acta, 2003, 48(4):349-356.
[6] Huang C A, Liu Y W, Yu C, et al. Role of carbon in the chromium deposit electroplated from a trivalent chromium-based bath[J]. Surface & Coatings Technology, 2011, 205(11):3461-3466.
[7] Huang C A, Lieu U W, Chuang C H. Role of nickel undercoat and reduction-flame heating on the mechanical properties of Cr-C deposit electroplated from a trivalent chromium based bath[J]. Surface & Coatings Technology, 2009, 203(19):2921-2926.
[8] Wang L, Gao Y, Xu T, et al. Corrosion resistance and lubricated sliding wear behaviour of novel Ni-P graded alloys as an alternative to hard Cr deposits[J]. Applied Surface Science, 2006, 252(20):7361-7372.
[9] Sahraoui T, Guessasma S, Fenineche N E, et al. Friction and wear behaviour prediction of HVOF coatings and electroplated hard chromium using neural computation[J]. Materials Letters, 2004, 58(5):655-660.
[10] Paul A, Lim J, Choi K, et al. Effects of deposition parameters on the properties of chromium carbide coatings deposited onto steel by sputtering[J]. Materials Science & Engineering A, 2002, 332(1-2):123-128.
[11] Huang C A, Liu Y W, Yu C, et al. Role of carbon in the chromium deposit electroplated from a trivalent chromium-based bath[J]. Surface & Coatings Technology, 2011, 205(11):3461-3466.
[12] Ghaziof S, Golozar M A, Raeissi K. Characterization of as-deposited and annealed Cr-C alloy coatings produced from a trivalent chromium bath[J]. Journal of Alloys and Compounds, 2010, 496(1-2):164-168.
[13] Ghaziof S, Raeissi K, Golozar M A. Improving the corrosion performance of Cr-C amorphous coatings on steel substrate by modifying the steel surface preparation[J]. Surface & Coatings Technology, 2010, 205(7):2174-2183.
[14] Zeng Z, Wang L, Liang A , et al. Tribological and electrochemical behavior of thick Cr-C alloy coatings electrodeposited in trivalent chromium bath as an alternative to conventional Cr coatings[J]. Electrochimica Acta, 2007, 52(3):1366-1373.
[15] 王先友, 蒋汉瀛. 电化学方法制备非晶态铬工艺的研究[J]. 材料科学与工程学报, 1995(4):35-37.
Wang X Y, Jiang H Y. The study of producing amorphous chromium coating process by electrochemical methods[J]. Materials Science and Engineering, 1995(4):35-37 (in Chinese).
[16] 李惠东, 李敏. 从三价铬镀液中电沉积可替代硬铬镀层的铬合金镀层[J]. 电化学, 1998(2):217-222.
Li H D, Li M. Study on the substitution of chromium alloy electroplating from trivalent plating bath for the hard chromium plating[J]. Electrochemistry, 1998(2):217-222 (in Chinese).
[17] 孙化松, 屠振密, 李永彦, 等. 常温高效硫酸盐三价铬电镀工艺[J]. 材料保护, 2010(1):25-27.
Sun H S, Tu Z M, Li Y Y, et al. Technology for efficient chromium electroplating at ambient temperature in trivalent chromium sulfate bath[J]. Journal of Materials Protection, 2010(1):25-27 (in Chinese).
[18] Vykhodtseva L N, Edigaryan A A, Lubnin E N, et al. Composition, structure, and corrosion electrochemical properties of chromium coatings deposited from chromium(III) electrolytes containing formic acid and its derivatives[J]. Russian Journal of Electrochemistry, 2004, 40(4):387-393.
[19] Surviliene S, Jasulaitiene V, Cesuniene A, et al. The use of XPS for study of the surface layers of Cr-Co alloy electrodeposited from Cr(III) formate-urea baths[J]. Solid State Ionics, Diffusion and Reactions, 2008, 179(1-6):222-227.
相似文献/References:
[1]王晓丽,顾 海,周昭昌,等.铜镀层工艺参数优化的正交实验研究[J].电镀与精饰,2018,(12):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
WANG Xiaoli,GU Hai,ZHOU Zhaochang,et al.Orthogonal Experimental Research on Optimization of Process Parameters of Copper Electroplating[J].Plating & Finishing,2018,(12):19.[doi:10.3969/j.issn.1001?3849.2018.12.005]
[2]王 秀.电镀智能监控系统设计[J].电镀与精饰,2018,(12):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
WANG Xiu.Design of Intelligent Electroplating Monitoring System[J].Plating & Finishing,2018,(12):30.[doi:10.3969/j.issn.1001?3849.2018.12.007]
[3]王明亮,杨海燕,李 明,等.电镀硬金的研究现状[J].电镀与精饰,2019,(11):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
WANG Mingliang,YANG Haiyan,LI Ming,et al.Research Progress on Hard Gold Electrodeposition[J].Plating & Finishing,2019,(12):26.[doi:10.3969/j.issn.1001-3849.2019.11.007]
[4]刘 光*,文 桦,徐启杰.基于TIA和PLC的全自动ABS塑料电镀控制系统设计[J].电镀与精饰,2020,(2):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
LIU Guang*,WEN Hua,XU Qijie.Design of Automatic Control System for ABS Plastics Electroplating Line Based on TIA and PLC[J].Plating & Finishing,2020,(12):33.[doi:10.3969/j.issn.1001-3849.2020.02.007]
[5]宋青员,何荣祥,陈朝会,等.高度梯度微纳结构的自动化电镀制备方法[J].电镀与精饰,2020,(7):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
SONG Qingyuan,HE Rongxiang,CHEN Chaohui,et al.Automated Electroplating for Gradient Height Micro-nano Structures Fabricating[J].Plating & Finishing,2020,(12):23.[doi:10.3969/j.issn.1001-3849.2020.07.0050]
[6]雷翔霄?,徐立娟,唐春霞.基于神经网络PID算法的镀液温度控制系统[J].电镀与精饰,2020,(8):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
LEI Xiangxiao,XU Lijuan,et al.Bath Temperature Control System Based on Neural Network PID[J].Plating & Finishing,2020,(12):39.[doi:10.3969/j.issn.1001-3849.2020.08.0080]
[7]薛迪杰*,陈 军,陈景召.基于ZigBee的电镀生产线温度集中监控系统[J].电镀与精饰,2021,(1):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
XUE Dijie*,CHEN Jun,CHEN Jingzhao,et al.Temperature Centralized Monitoring System of Electroplating Production Line Based on ZigBee[J].Plating & Finishing,2021,(12):31.[doi:10.3969/j.issn.1001-3849.2021.01.0060]
[8]王昱开*.不锈钢工具电镀金刚石工艺研究[J].电镀与精饰,2021,(3):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
WANG Yukai*.王昱开*[J].Plating & Finishing,2021,(12):6.[doi:10.3969/j.issn.1001-3849.2021.03.002]
[9]杨航城,田海燕.工艺参数对电镀镍钴合金及其性能的影响[J].电镀与精饰,2021,(4):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]
YANG Hangcheng,TIAN Haiyan.Effect of Process Parameters on Electrodepositing Ni-Co Alloy and Its Properties[J].Plating & Finishing,2021,(12):5.[doi:10.3969/j.issn.1001-3849.2021.04.002]
[10]孙小平*,吕春雷.薄带连铸结晶辊表面处理[J].电镀与精饰,2021,(5):43.[doi:10.3969/j.issn.1001-3849.2021.05.007]
SUN Xiaoping*,LV Chunlei.Surface Treatment Technology of Crystallization Roller for Strip Continuous Casting[J].Plating & Finishing,2021,(12):43.[doi:10.3969/j.issn.1001-3849.2021.05.007]
备注/Memo
收稿日期: 2019-06-17;修回日期: 2019-09-06
作者简介: 范文俊(1993-),男,硕士,从事PEMFC燃料电池金属双极板表面改性技术研究,Email:953851576@qq.com