XU Jiaojiao*.Process Research of Chromic acid Passivation on the Tinplate[J].Plating & Finishing,2021,(7):56-59.[doi:10.3969/j.issn.1001-3849.2021.07.011]
镀锡板铬酸钝化工艺研究
- Title:
- Process Research of Chromic acid Passivation on the Tinplate
- 文献标志码:
- A
- 摘要:
- 采用铬酸溶液对镀锡板进行钝化,对钝化液组成、阴极电流密度、温度等工艺条件进行研究,通过宏观表面质量、钝化膜的组成、漆膜附着力评价等方面对钝化膜的性能进行考察。结果表明:在50 g/L CrO3+0.5 g/L H2SO4的钝化液中,阴极钝化电流密度控制在6~10 A/dm2、温度保持在50~60 ℃较为合适;在此条件下得到钝化膜总Cr含量达到10 mg/m2且Cr(OH)3/ Cr2O3含量比在0.9~1.5,钝化膜附着力较优,耐蒸煮。
- Abstract:
- The process conditions of passivation of tinplate with chromic acid solution were studied, including the composition of passivation solution, cathode current density and temperature. The performance of passivation film was investigated from the aspects of macro surface quality, composition of passivation film and adhesion evaluation of paint film. The results showed that in the passivation solution 50 g/L CrO3+0.5 g/L H2SO4, it was suitable to control the cathodic passivation current density at 6~10 A/dm2 and keep the temperature at 50 ~ 60 ℃. Under these conditions, the total Cr content of the passivation film reached more than 10 mg/m2 and the Cr(OH)3/Cr2O3 content ratio was 1~1.5, the passivation film had better adhesion and cooking resistance.
参考文献/References:
[1] 曾林, 李宁, 黎德育, 等. 镀锡板钝化膜影响涂漆附着力的XPS分析[J]. 材料保护, 2011, 44(2): 64-66.
Zeng L, Li N, Li D Y, et al. XPS analysis of the effect of passive film on the adhesion of tinplate[J]. Materials Protection, 2011, 44(2): 64-66 (in Chinese).
[2] 谢龙, 黄久贵, 翟运飞, 等. 镀锡钢板表面钝化膜的形成机制[J]. 材料保护, 2013, 64(7): 1-4.
Xie L, Huang J G, Zhai Y F, et al. Formation mechanism of passive film on tinplate surface[J]. Materials Protection, 2013, 64(7): 1-4 (in Chinese).
[3] 王洺浩, 陆永亮, 翟运飞, 等. 钝化方式对镀锡板钝化膜组成与性能的影响[J]. 电镀与涂饰, 2016, 34(16):903-908.
Wang M H, Lu Y L, Zhai Y F, et al. Effects of different passivation methods on composition and performances of the passivation film on tinplate[J]. Electroplating & Finishing, 2016, 34(16): 903-908 (in Chinese).
[4] 孙鹏, 龚志强, 孙力, 等. 钝化工艺对镀锡板钝化膜附着力的影响[J]. 电镀与精饰, 2018, 40(9):10-13.
Sun P, Gong Z Q, Sun L, et al. Effect of different passivation process on adhesion for tinplate passivation films[J]. Plating & Finishing, 2018, 40(9): 10-13 (in Chinese).
[5] 朱国和, 闫元媛, 陈成增. 宝钢冷轧镀铬板(TFS)产品的表面形貌、结构与组成分析[J]. 上海金属, 2014, 36(2):5-8.
Zhu G H, Yan Y Y, Chen C Z. Analysis of the structure and surface morphology of double cold rolled tin free steel products of Baosteel[J]. Shanghai Metal, 2014, 36(2): 5-8 (in Chinese).
相似文献/References:
[1]李发闯,苏 光,郭战永,等.电化学合成聚苯胺膜及其腐蚀防护性能[J].电镀与精饰,2019,(10):5.[doi:10.3969/j.issn.1001-3849.2019.10.002]
LI Fachuang,SU Guang,et al.Electrochemical Synthesis and Corrosion Protective Behavior of Polyaniline Film[J].Plating & Finishing,2019,(7):5.[doi:10.3969/j.issn.1001-3849.2019.10.002]
[2]谭 悦,陈 燕*.电解复合磁力研磨GH4169管内表面的光整研究[J].电镀与精饰,2020,(1):27.[doi:10.3969/j.issn.1001-3849.2020.01.006]
TAN Yue,CHEN Yan*.Surface Finishing of GH4169 Tube by Electrolytic Composite Magnetic Grinding[J].Plating & Finishing,2020,(7):27.[doi:10.3969/j.issn.1001-3849.2020.01.006]
[3]宋 浩 *,方 圆,石云光,等.镀锡板边部漆膜附着力影响因素研究[J].电镀与精饰,2022,(11):47.[doi:10.3969/j.issn.1001-3849.2022.11.009]
SONG Hao *,FANG Yuan,SHI Yunguang,et al.Study of Influence Factors on the Edge Lacquer Adhesion of Tinplate[J].Plating & Finishing,2022,(7):47.[doi:10.3969/j.issn.1001-3849.2022.11.009]
[4]周桂海*,王德智,胡宏卫.电感耦合等离子原子发射法测定镀锡板中钝化锆[J].电镀与精饰,2022,(11):95.[doi:10.3969/j.issn.1001-3849.2022.11.017]
ZHOU Guihai*,WANG Dezhi,HU Hongwei.Determination of Passivated Zirconium of Tin Plate by Inductively Coupled Plasma Atomic Emission Spectrometry[J].Plating & Finishing,2022,(7):95.[doi:10.3969/j.issn.1001-3849.2022.11.017]
[5]宋浩,杨鸿建,吴明辉*,等.镀锡板硫化斑分析及控制工艺研究[J].电镀与精饰,2022,(12):54.[doi:10.3969/j.issn.1001-3849.2022.12.008]
SONG Hao,YANG Hongjian,WU Minghui*,et al.Analysis and Control Technology of Sulfide Staining on Tinplate[J].Plating & Finishing,2022,(7):54.[doi:10.3969/j.issn.1001-3849.2022.12.008]
[6]万一群,齐韦*,沈鹏杰,等.基板表面形貌对镀锡板润湿能力影响的研究[J].电镀与精饰,2023,(4):38.[doi:10.3969/j.issn.1001-3849.2023.04.007]
Wan Yiqun,Qi Wei*,Shen Pengjie,et al.Study on blackplate surface morphology effect on wettability for tinplate[J].Plating & Finishing,2023,(7):38.[doi:10.3969/j.issn.1001-3849.2023.04.007]
[7]吴明辉,王振文,石云光,等.镀锡板耐黑变性能影响因素研究[J].电镀与精饰,2023,(5):80.[doi:10.3969/j.issn.1001-3849.2023.05.011]
Wu Minghui,Wang Zhenwen,Shi Yunguang,et al.Study on influencing factors of blackening resistance of tinplate[J].Plating & Finishing,2023,(7):80.[doi:10.3969/j.issn.1001-3849.2023.05.011]
[8]宋乙峰,王悦鼎,岳重祥*,等.表面膜层对镀锡板表面张力及印铁缩孔的影响[J].电镀与精饰,2023,(12):8.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.002]
Song Yifeng,Wang Yueding,Yue Chongxiang*,et al.Effect of surface films on surface tension of tinplate and shrinkage hole during printing?/html>[J].Plating & Finishing,2023,(7):8.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.002]
[9]孙 宇*,陈艺敏,石云光,等. 气雾阀用镀锡板表面黑点缺陷分析 [J].电镀与精饰,2023,(12):110.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.016]
Sun Yu*,Chen Yimin,Shi Yunguang,et al.Black point defect analysis of tinplate for aerosol valve[J].Plating & Finishing,2023,(7):110.[doi:doi : 10.3969/j.issn.1001-3849.2023.12.016]
[10]陈艺敏 *,孙 宇,常树林,等.不同工艺条件对低锡量镀锡板耐蚀性的影响莫志英?/span>[J].电镀与精饰,2024,(1):34.[doi:10.3969/j.issn.1001-3849.2024.01.006]
Chen Yimin*,Sun Yu,Chang Shulin,et al.Effect of different process conditions on the corrosion resistance of low tin content tinplate[J].Plating & Finishing,2024,(7):34.[doi:10.3969/j.issn.1001-3849.2024.01.006]
备注/Memo
收稿日期: 2021-04-18;修回日期: 2021-05-18
作者简介: 许姣姣, 760204@baosteel.com