Liu Zhongshu,Liu Chun,Chi Lin,et al.Preparation and corrosion resistance of phytic acid conversion coating on aluminum alloys[J].Plating & Finishing,2023,(11):54-59.[doi:10.3969/j.issn.1001-3849.2023.11.008]
铝合金表面植酸转化膜的制备及耐腐蚀性能研究
- Title:
- Preparation and corrosion resistance of phytic acid conversion coating on aluminum alloys
- Keywords:
- aluminum alloy ; phytic acid ; chemical conversion ; corrosion resistance
- 分类号:
- TG178
- 文献标志码:
- A
- 摘要:
- 对 Al-Cu-Mg 合金在单一植酸溶液、植酸 +Zn 2+ 溶液、植酸 +Mn 2+ 溶液中分别进行化学转化处理。结果显示,合金在植酸 +Zn 2+ 溶液和植酸 +Mn 2+ 溶液中得到的表面膜层比在单一植酸溶液中的膜层更完整致密。化学转化处理提高了合金试样的腐蚀电位,并减小了其阳极电流密度。与在单一植酸中转化的合金相比,在植酸 +Zn 2+ 、植酸 +Mn 2+ 溶液中处理的合金具有更好的耐蚀性。
- Abstract:
- : The phytic acid conversion coating was prepared by immerging the Al-Cu-Mg alloy samples in single phytic acid solution , phytic acid+Zn 2+ solution , and phytic acid+Mn 2+ solution respectively. The results show that the conversion coating on the samples in phytic acid+Zn 2+ solution or phytic acid+Mn 2+ solution is denser than that in single phytic acid solution. Moreover , the chemical conversion increases the corrosion potential of the alloy , and decreases the anodic current density of the samples. Compared with the sample in single phytic acid solution , the samples in phytic acid+Zn 2+ solution or phytic acid+Mn 2+ solution have better corrosion resistance.
参考文献/References:
[1] 崔珊 , 安成强 , 郝建军 . 铝及铝合金无铬钝化研究进展 [J]. 表面技术 , 2016, 45(6): 63-69.
[2] 陈福瑞 , 李文芳 , 杜军 , 等 . 化学转化膜的自愈性研究进展 [J]. 材料保护 , 2021, 54(2): 122-126.
[3] 赵晶晶 , 胡爽飞 , 于得水 , 等 . 大型体育球馆用铝网壳结构表面三价铬转化膜性能研究 [J]. 材料保护 , 2022, 55(2): 105-108.
[4] 纪红 , 朱祖芳 . 铝及铝合金无铬表面处理技术研究进展 [J]. 电镀与涂饰 , 2009, 28(6): 34-37.
[5] 王双红 , 刘常升 , 单凤君 . 铝及其合金无铬钝化的研究进展 [J]. 电镀与涂饰 , 2007, 26(7): 48-51.
[6] 张曌 , 范云鹰 . 有机为主复合钝化的综合对比研究与展望 [J]. 材料保护 , 2021, 55(5): 134-141.
[7] 郭绍福 , 赵春红 . 植酸封孔对铝制件阳极氧化膜耐蚀性的影响 [J]. 电镀与精饰 , 2021, 43(8): 6-10.
[8] 卢勇 , 冯辉霞 , 张晓芳 . 金属表面植酸转化膜研究进展 [J]. 材料导报 , 2019, 33(5): 1455-1461.
[9] 曾纪勇 , 郭兴伍 , 彭立明 , 等 . 镁合金植酸化学转化膜研究进展 [J]. 材料保护 , 2019, 52(12): 124-128.
[10] 林继兴 , 牛丽媛 , 高光亮 , 等 . 镁表面防腐蚀植酸处理方法 [J]. 轻合金加工技术 , 2008, 36(9): 36-39.
[11] 高焕方 , 龙飞 , 谭怀琴 , 等 . 转化时间对 AZ31B 镁合金植酸转化膜的影响 [J]. 腐蚀与防护 , 2014, 35(11): 1108-1112.
[12] Cui X F, Li Q F, Li Y, et al. Microstructure and corrosion resistance of phytic acid conversion coatings for magnesium alloy[J]. Applied Surface Science, 2008, 255(5): 2098-2103.
[13] Cui X F, Li Y, Li Q F, et al. Influence of phytic acid concentration on performance of phytic acid conversion coatings onthe AZ91D magnesium alloy[J]. Materials Chemistry and Physics, 2008, 111: 503-507.
[14] Hernández-Alvarado L A, Hernández L S, Garrido J, et al. Statistical design of the parameters involved in the obtainment of a biodegradable phytate coating over AZ31 alloyfor possible endoprosthetic temporary applications[J]. Surface and Coatings Technology, 2017, 325: 473-481.
[15] 张华云 , 刘治国 . 工艺参数对镁合金植酸转化膜的影响 [J]. 材料保护 , 2009, 42(8): 46-50.
[16] Pan F, Yang X, Zhang D. Chemical nature of phyticacid conversion coating on AZ61 magnesium alloy[J]. Applied Surface Science, 2009, 255(20): 8363-8371.
[17] Ye C H, Zheng Y F, Wang S Q, et al. In vitro corrosionand biocompatibility study of phytic acid modified WE43 magnesium alloy[J]. Applied Surface Science, 2012, 258(8): 3420-3427.
[18] Gao L L, Zhang M L, Huang X M, et al, Phytic acid conversion coating on Mg-Li alloy[J]. Journal of Alloys and Compounds, 2009, 485: 789-793.
[19] Chen Y Q, Wan G J, Wang J, et al. Covalent immobilization of phytic acid on Mg by alkaline pre-treatment: Corrosion and degradation behavior in phosphate buffered saline[J]. Corrosion Science, 2013, 75: 280-286.
[20] Ou J F, Chen X. Corrosion resistance of phytic acid/Ce(III) nanocomposite coating with superhydrophobicity on magnesium[J]. Journal of Alloys and Compounds, 2019, 787: 145-151.
[21] Gupta R K, Mensah D K, Kuma R D. Effect of post heat treatment on corrosion resistance of phytic acid conversion coated magnesium[J]. Journal of Materials Science and Technology, 2013, 29(2): 180-186.
[22] 行舒乐 , 肖伟中 , 车威 , 等 . AZ31 铸轧镁合金植酸转化成膜过程机理研究 [J]. 热加工工艺 , 2021, 51(4): 95-99.
[23] Gao H F, Tan H Q, Li J, et al. Synergistic effect of cerium conversion coating and phytic acid conversion coatingon AZ31B magnesium alloy[J]. Surface and Coatings Technology, 2012, 212: 32-36.
[24] 林碧兰 . 铝合金表面钼酸盐改进植酸转化膜的耐蚀性能 [J]. 表面技术 , 2016, 45(3): 115-119.
[25] Shi H W, Han E H, Liu F C, et al. Protection of 2024-T3 aluminium alloy by corrosion resistant phytic acid conversion coating[J]. Applied Surface Science, 2013, 280: 325-331.
[26] Kim M, Choi E, So J, et al. Improvement of corrosion properties of plasma in an aluminum alloy 6061-T6 by phytic acid anodization temperature[J]. Journal of Materials Research and Technology, 2021, 11: 219-226.
[27] Gao X, Li W H, Yan R, et al. Effect of zinc ion on the microstructure and electrochemical behavior of phytic acid based conversion coatings on Q235 steels[J]. Surface and Coatings Technology, 2017, 325(25): 248-256.
相似文献/References:
[1]王艳伟.填充工序对铝合金壳体零件铬酸阳极化色差的影响[J].电镀与精饰,2019,(7):40.[doi:10.3969/j.issn.1001-3849.2019.07.009]
WANG Yanwei.Influence of Filling Process on Color Difference of Aluminum Alloy Shell after Chromic Acid Anodization[J].Plating & Finishing,2019,(11):40.[doi:10.3969/j.issn.1001-3849.2019.07.009]
[2]黄碧芳*,李远会,王 丽,等.铝合金磷钼酸亚铁转化体系工艺研究[J].电镀与精饰,2019,(9):29.[doi:10.3969/j.issn.1001-3849.2019.09.006]
HUANG Bifang*,LI Yuanhui,WANG Li,et al.Study on the Conversion Process of Ferrous Phosphomolybdate on Aluminum Alloy[J].Plating & Finishing,2019,(11):29.[doi:10.3969/j.issn.1001-3849.2019.09.006]
[3]元 泉,邱 媛*,刘 洋,等.铝合金漆层与氧化层激光清洗应用研究[J].电镀与精饰,2019,(12):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
YUAN Quan,QIU Yuan#,LIU Yang,et al.Research on Laser Cleaning Application for Coating and Oxide Layer of Aluminum Alloy[J].Plating & Finishing,2019,(11):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
[4]季 伟,孟繁东,潘科宇,等.铝合金表面油污清洗剂的制备及其腐蚀性研究[J].电镀与精饰,2021,(2):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
JI Wei,MENG Fandong,PAN Keyu,et al.季 伟1,孟繁东1,潘科宇1,王文军1,潘明华1,韩怡秋2,邵明亮2,刘 东3,周 勇3*[J].Plating & Finishing,2021,(11):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
[5]张子聪,郝建军*,赵荣兴.铝合金复合石墨烯薄膜的制备及腐蚀性能研究[J].电镀与精饰,2021,(7):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
ZHANG Zicong,HAO Jianjun*,ZHAO Rongxing.Study on Preparation and Corrosion Performance of Aluminum Alloy Composite Graphene Film[J].Plating & Finishing,2021,(11):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
[6]刘奋照*.几种铝合金材料在汽车防冻液中的腐蚀行为[J].电镀与精饰,2021,(9):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
LIU Fenzhao*.Corrosion Behavior of Several Aluminum Alloy in Automobile Antifreeze[J].Plating & Finishing,2021,(11):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
[7]刘 静,马小昭,王帅星.绝缘保护用铬酸阳极氧化工艺研究[J].电镀与精饰,2022,(6):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
LIU Jing,MA Xiaozhao,WANG Shuaixing.Research on Chromic Acid Anodizing Technique for Insulation Protection[J].Plating & Finishing,2022,(11):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
[8]李志强,魏红阳,陈东初*,等.电源参数对铝合金表面复合氧化膜的多彩电解着色的影响规律研究[J].电镀与精饰,2022,(6):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
LI Zhiqiang,WEI Hongyang,CHEN Dongchu*,et al.Effects of Power Parameters on Electrolytic Colouring of Colorful Composite Oxide Film on Aluminum Alloy Surface[J].Plating & Finishing,2022,(11):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
[9]李廷取 *,刘祥玲,刘文异. 不同占空比对6061铝合金微弧氧化着色及性能的影响研究 [J].电镀与精饰,2022,(9):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
LI Tingqu *,LIU Xiangling,LIU Wenyi.Study on Microarc Oxidation Coloring and Properties of 6061 Aluminum Alloy with Different Duty Ratios[J].Plating & Finishing,2022,(11):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
[10]刘巧娣*,邓国军. 硫酸阳极化膜层出现白色粉末问题原因分析 [J].电镀与精饰,2022,(10):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
LIU Qiaodi*,DENG Guojun.Cause Analysis of White Powder in Sulfuric Acid Anodized Film[J].Plating & Finishing,2022,(11):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
备注/Memo
收稿日期: 2022-11-25 修回日期: 2022-12-10 作者简介: 刘钟书( 2001 —),男,本科生, email : 1000610@neuq.edu.cn * 通信作者: 房大然, email : fangdaran@163.com 基金项目: 河北省自然科学基金资助项目( E2021501019 )?/html>