HUANG Bifang*,LI Yuanhui,WANG Li,et al.Study on the Conversion Process of Ferrous Phosphomolybdate on Aluminum Alloy[J].Plating & Finishing,2019,(9):29-32.[doi:10.3969/j.issn.1001-3849.2019.09.006]
铝合金磷钼酸亚铁转化体系工艺研究
- Title:
- Study on the Conversion Process of Ferrous Phosphomolybdate on Aluminum Alloy
- 文献标志码:
- A
- 摘要:
- 本文以磷钼酸亚铁转化体系为研究对象,以点滴时间为判定标准,采用单因素实验研究磷钼酸浓度、Fe2+浓度、NaF浓度、pH值、络合剂浓度、温度、处理时间等因素对铝合金转化膜耐蚀性的影响。结果表明,当磷钼酸浓度为0.030 mol/L、Fe2+为0.004 mol/L、NaF为0.026 mol/L、络合剂为0.00051 mol/L、pH=4、温度为45 ℃、处理时间为120 min时,能够形成耐蚀能力良好的转化膜,其腐蚀电位为-0.71391 V,腐蚀电流密度为8.7579×10-8 A/cm2。
- Abstract:
- In this paper, taking the conversion system of ferrous phosphomolybdate as the research object and the droping time as criterion, the influences of phosphomolybdate concentration, Fe2+ concentration, NaF concentration, pH value, complexant concentration, temperature and treatment time on the corrosion resistance of the aluminum alloy conversion film were studied by single factor experiment. The results showed that when the concentration of phosphomolybdic acid was 0.030 mol/L, Fe2+ was 0.004 mol/L, NaF was 0.026 mol/L, complexant was 0.00051 mol/L, pH value was 4, temperature was 45 ℃ and treatment time was 120 min, the aluminum alloy conversion film showed a good corrosion resistance, its corrosion potential was -0.71391 V and corrosion current density was 8.7579×10-8 A/cm2.
参考文献/References:
[1] 王恩波, 胡长文, 许林. 多酸化学导论[M]. 北京: 化学工业出版社, 1997.
[2] Okuhara T, Nishimura T, Ohashi K, et al. A pronounced catalytic activity of an acidic cesium salt of 12-tungstophosphoric acid for ester decomposition in solid-liquid system[J]. Chemistry Letters, 1990, 19(7): 1201-1202.
[3] 方景礼, 王济奎, 刘彤秋, 等. 钢铁表面硅钼杂多酸化学转化膜的研究[J]. 应用化学, 1993(5): 53-56.
[4] 何刚, 高勤卫. 钢铁表面环保型杂多酸化学转化膜的耐蚀性[J]. 腐蚀科学与防护技术, 2009, 21(1): 66-68.
[5] 张圣麟, 陈华辉, 张明明, 等. Fe2+对铝合金无铬磷化的影响[J]. 金属热处理, 2007, 32(12): 78-80.
[6] 郝建军, 安成强, 刘常升. 磷钼杂多酸钝化工艺研究[J]. 材料保护, 2005(7): 28-30.
[7] 王成, 江峰, 林海潮, 等. 铝合金钼酸盐转化膜研究[J]. 电镀与精饰, 2001, 23(3): 8-10.
[8] 唐鋆磊, 唐聿明, 左禹. 稀土转化膜钼酸盐后处理工艺研究[J]. 材料保护, 2006, 39(11): 27-28.
[9] 肖鑫, 许律, 邓轾轩, 等. 铝及铝合金无铬氟锆酸盐化学转化膜[J]. 电镀与涂饰, 2011, 30(10): 37-40.
[10] 赵丹丹, 王志强, 孙瑞雪, 等. EDTA对AZ91D镁合金锡酸盐转化膜形貌与性能的影响[J]. 材料热处理学报, 2014, 35(s2): 162-165.
[11] 桑延霞, 唐鹏, 张军军. 成膜温度对转化膜性能的影响[J]. 材料热处理学报, 2013, 34(11): 188-194.
[12] 薛丽华, 张学颖, 吕坤, 等. 时间对2024铝合金表面铬酸盐转化膜耐蚀性的影响[J]. 内蒙古科技大学学报, 2011, 30(1): 22-24.
[13] 杨丁, 黄芸珠, 杨崛. 铝合金表面处理技术[M]. 北京: 化学工业出版社, 2012.
[14] 李鑫庆, 欧阳贵, 王菊荣. 金属化学转化膜实用手册[M]. 北京: 机械工业出版社, 2016.
[15] 张书第, 杜鹏飞, 李礼, 等. 铝合金Ce-Mn转化膜的制备工艺研究[J]. 电镀与环保, 2017, 37(2): 32-35.
[16] 李红玲. 铝合金表面无铬环保型化学转化膜工艺[J]. 腐蚀与防护, 2014, 35(2): 169-174.
[17] 赵思萌, 郝建军, 田鑫奇, 等. 镁合金锆酸盐体系转化膜工艺的研究[J]. 电镀与精饰, 2017, 39(2): 5-8.
相似文献/References:
[1]王艳伟.填充工序对铝合金壳体零件铬酸阳极化色差的影响[J].电镀与精饰,2019,(7):40.[doi:10.3969/j.issn.1001-3849.2019.07.009]
WANG Yanwei.Influence of Filling Process on Color Difference of Aluminum Alloy Shell after Chromic Acid Anodization[J].Plating & Finishing,2019,(9):40.[doi:10.3969/j.issn.1001-3849.2019.07.009]
[2]元 泉,邱 媛*,刘 洋,等.铝合金漆层与氧化层激光清洗应用研究[J].电镀与精饰,2019,(12):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
YUAN Quan,QIU Yuan#,LIU Yang,et al.Research on Laser Cleaning Application for Coating and Oxide Layer of Aluminum Alloy[J].Plating & Finishing,2019,(9):25.[doi:10.3969/j.issn.1001-3849.2019.12.006]
[3]季 伟,孟繁东,潘科宇,等.铝合金表面油污清洗剂的制备及其腐蚀性研究[J].电镀与精饰,2021,(2):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
JI Wei,MENG Fandong,PAN Keyu,et al.季 伟1,孟繁东1,潘科宇1,王文军1,潘明华1,韩怡秋2,邵明亮2,刘 东3,周 勇3*[J].Plating & Finishing,2021,(9):38.[doi:10.3969/j.issn.1001-3849.2021.02.0080]
[4]张子聪,郝建军*,赵荣兴.铝合金复合石墨烯薄膜的制备及腐蚀性能研究[J].电镀与精饰,2021,(7):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
ZHANG Zicong,HAO Jianjun*,ZHAO Rongxing.Study on Preparation and Corrosion Performance of Aluminum Alloy Composite Graphene Film[J].Plating & Finishing,2021,(9):15.[doi:10.3969/j.issn.1001-3849.2021.07.003]
[5]刘奋照*.几种铝合金材料在汽车防冻液中的腐蚀行为[J].电镀与精饰,2021,(9):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
LIU Fenzhao*.Corrosion Behavior of Several Aluminum Alloy in Automobile Antifreeze[J].Plating & Finishing,2021,(9):59.[doi:10.3969/j.issn.1001-3849.2021.09.010]
[6]刘 静,马小昭,王帅星.绝缘保护用铬酸阳极氧化工艺研究[J].电镀与精饰,2022,(6):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
LIU Jing,MA Xiaozhao,WANG Shuaixing.Research on Chromic Acid Anodizing Technique for Insulation Protection[J].Plating & Finishing,2022,(9):41.[doi:10.3969/j.issn.1001-3849.2022.06.009]
[7]李志强,魏红阳,陈东初*,等.电源参数对铝合金表面复合氧化膜的多彩电解着色的影响规律研究[J].电镀与精饰,2022,(6):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
LI Zhiqiang,WEI Hongyang,CHEN Dongchu*,et al.Effects of Power Parameters on Electrolytic Colouring of Colorful Composite Oxide Film on Aluminum Alloy Surface[J].Plating & Finishing,2022,(9):52.[doi:10.3969/j.issn.1001-3849.2022.06.011]
[8]李廷取 *,刘祥玲,刘文异. 不同占空比对6061铝合金微弧氧化着色及性能的影响研究 [J].电镀与精饰,2022,(9):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
LI Tingqu *,LIU Xiangling,LIU Wenyi.Study on Microarc Oxidation Coloring and Properties of 6061 Aluminum Alloy with Different Duty Ratios[J].Plating & Finishing,2022,(9):20.[doi:10.3969/j.issn.1001-3849.2022.09.004]
[9]刘巧娣*,邓国军. 硫酸阳极化膜层出现白色粉末问题原因分析 [J].电镀与精饰,2022,(10):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
LIU Qiaodi*,DENG Guojun.Cause Analysis of White Powder in Sulfuric Acid Anodized Film[J].Plating & Finishing,2022,(9):88.[doi:10.3969/j.issn.1001-3849.2022.10.015]
[10]杨 丹,孙翠玲,林修洲,等.铝合金表面改性对ZIF-8膜层生长行为的影响[J].电镀与精饰,2023,(1):16.[doi:10.3969/j.issn.1001-3849.2023.01.003]
Yang Dan,Sun Cuiling,Lin Xiuzhou,et al.Effect of modification methods on ZIF-8 film growth behaviors on aluminum alloy[J].Plating & Finishing,2023,(9):16.[doi:10.3969/j.issn.1001-3849.2023.01.003]
备注/Memo
收稿日期: 2018-12-14;修回日期: 2019-01-06
通信作者: 黄碧芳,email:1615758962@qq.com
基金项目: 国家自然科学基金(51661006;51361004)