Zhang Lu,Zhang Zhongquan,Yu Yundan,et al.Electrodeposition of CoFe/ZrO 2 composite films and their oxygen evolution performance[J].Plating & Finishing,2024,(1):9-14.[doi:10.3969/j.issn.1001-3849.2024.01.002]
CoFe/ZrO2复合膜的电沉积及其析氧性能研究
- Title:
- Electrodeposition of CoFe/ZrO 2 composite films and their oxygen evolution performance
- Keywords:
- electrodeposition ; composite films ; bath temperature ; oxygen evolution reaction
- 分类号:
- TQ153.2
- 文献标志码:
- A
- 摘要:
- 为降低电解水阳极析氧反应的过电位,采用电化学沉积技术制备了 CoFe/ZrO 2 复合膜。在碱性介质中,该复合膜表现出了优异的析氧反应( OER )活性,在电流密度 10 mA/cm?#1602下过电势仅为 1.56 V ,远低于 CoFe ( 1.694 V ),这主要是由于 CoFe/ZrO 2 复合膜具有足够暴露的活性位点和较高的电子转移能力。进一步的研究表明, CoFe/ZrO 2 复合膜可以在 1.58 V 过电位下稳定运行 12 h ,经 2000 圈循环伏安测试后, OER 活性曲线未存在明显差别,显示 CoFe/ZrO 2 复合膜具有良好稳定性。本文工作可为探索经济高效的 OER 催化电极膜材料开辟一条新途径,替代贵金属在可再生能源转换中应用。
- Abstract:
- : In order to reduce the overpotential of anodic oxygen evolution reaction during water electrolysis , CoFe/ZrO 2 composite films were prepared using electrochemical deposition technology. The composite films exhibit excellent oxygen evolution reaction ( OER ) activity in alkaline media , with an overpotential of only 1.56 V at a current density of 10 mA/cm 2 , which is significantly lower than that of CoFe ( 1.694 V ) . This is mainly due to the sufficient exposed active sites and high electron transfer capacity of the CoFe/ZrO 2 composite film. Further studies have shown that the CoFe/ZrO 2 composite membrane can operate stably at an overpotential of 1.58 V for 12 h.After 2000 cycles of cyclic voltammetry testing , there is no significant difference in the OER activity curves , indicating that the CoFe/ZrO 2 composite membrane has good stability. The work may open up a new way to explore cost-effective OER catalytic electrode membrane materials to replace precious metals in the application of renewable energy conversion.
参考文献/References:
[1] Li G Z, Sun T, Niu H J, et al. Triple interface optimization of Ru-based electrocatalyst with enhanced activity and stability for hydrogen evolution reaction[J]. Advanced Functional Materials, 2023, 2212514.
[2] Wang X, Mao Z L, Mao X, et al. Dual integrating oxygen and sulphur on surface of CoTe nanorods triggers enhanced oxygen evolution reaction[J]. Advanced Science, 2023, 2206204.
[3] Zhang Y W, Zhang X F, Li Y T, et al. FeCo alloy/N, S co-doped carbon aerogel derived from directional-casting cellulose nanofibers for rechargeable liquid flow and flexible Zn-air batteries[J/OL]. Nano Research, 2023, https://link.springer.com/article/10.1007/s12274-023-5409-4
[4] Kuo D Y, Paik H, Kloppenburg J, et al. Measurements of oxygen electroadsorption energies and oxygen evolution reaction on RuO 2 (110): A discussion of the sabatier principle and its role in electrocatalysis[J]. Journal of the American Chemical Society, 2018, 140(50): 17597-17605.
[5] Kim M, Kang S B, Fundamental analysis for active phase of rutile-based IrO2 catalyst: Comparison study of CH 4 oxidation on IrO 2 (100) and IrO 2 (110) [J]. Applied Surface Science, 2022, 605: 154827.
[6] Meng X, Li Z, Liu Y Y, et al. Enabling unassisted solar water splitting with concurrent high efficiency and stability by robust earth-abundant bifunctional electrocatalysts[J]. Nano Energy, 2023, 109: 108296.
[7] Lee D, Moru S, Reddy K P, et al. Bimetallic Cu-Ni core-shell nanoparticles anchored N-doped reduced graphene oxide as a high-performance bifunctional electrocatalyst for alkaline water splitting[J]. Applied Surface Science, 2023, 622: 156928.
[8] Gaur A, John J M, Pundir V, et al. Electronegativity-induced valence state augmentation of Ni and Co through electronic redistribution between Co-Ni 3 N/CeF 3 interfaces for oxygen evolution reaction[J]. ACS Applied Energy Materials, 2023, 6(3): 1763 – 1770.
[9] Liu R B, Song T. S, Xue H, et al. Surface reconstruction of iron – cobalt – nickel phosphides to achieve high-current-density water oxidation performance[J]. ACS Applied Energy Materials, 2023, 6(2): 692-701.
[10] Ogawa S, Nakayama K, Katayama M, et al. Highly durable bifunctional gas diffusion electrodes fabricated with melilite-type Fe/Co/Ni-mixed oxide electrocatalysts[J]. ACS Applied Energy Materials, 2022, 5(12), 15502-15509.
[11] Xie S, Jin H C, Wang C, et al. A comparison study on single metal atoms (Fe, Co, Ni) within nitrogen-doped graphene for oxygen electrocatalysis and rechargeable Zn-air batteries[J/OL]. Chinese Chemical Letters, 2022, https://doi.org/10.1016/j.cclet.2022.07.024
[12] Moloudi M, Noori A, Rahmanifar M S, et al. Layered double hydroxide templated synthesis of amorphous NiCoFeB as a multifunctional electrocatalyst for overall water splitting and rechargeable zinc – air batteries[J]. Advanced Energy Materials, 2023, 13(4), 2203002.
[13] Naqvi S T R, Rasheed T, Majeed S, et al. Development of nitrogen doped carbon dots modified CuCo alloy nanoparticles for potential electrocatalytic water splitting[J]. Journal of Molecular Liquids, 2020, 309: 113111.
[14] Li N, Liu X. A comparison of the catalytic efficiency of copper-based bimetallic nanoparticles in the click reactions[J]. Journal of Chemical Research. 2020, 44(9-10):566-570.
[15] Wei Y, Zheng M B, Zhu W, et al. Preparation of hierarchical hollow CoFe Prussian blue analogues and its heat-treatment derivatives for the electrocatalyst of oxygen evolution reaction[J]. Journal of Colloid and Interface Science, 2023, 631: 8-16.
相似文献/References:
[1]张冰怡,张莎莎*,姚正军,等.电沉积Ni-W纳米晶镀层制备与显微硬度研究[J].电镀与精饰,2019,(8):20.[doi:10.3969/j.issn.1001-3849.2019.08.005]
ZHANG Bingyi,ZHANG Shasha*,YAO Zhengjun,et al.Preparation and Microhardness of Electrodeposited Ni-W Nanocrystalline Coatings[J].Plating & Finishing,2019,(1):20.[doi:10.3969/j.issn.1001-3849.2019.08.005]
[2]雷同鑫,鞠 辉,张长科,等.电镀Ni-W-P合金在钻杆接头上的应用[J].电镀与精饰,2019,(10):38.[doi:10.3969/j.issn.1001-3849.2019.10.009]
LEI Tongxin,JU Hui,ZHANG Changke,et al.Application of Ni-W-P Alloy Prepared by Electroplating to Tool Joints[J].Plating & Finishing,2019,(1):38.[doi:10.3969/j.issn.1001-3849.2019.10.009]
[3]李晓峰*,孟 芳,董会超,等.电沉积法制备掺铋金属锌及其性能表征[J].电镀与精饰,2020,(1):12.[doi:10.3969/j.issn.1001-3849.2020.01.003]
LI Xiaofeng*,MENG Fang,DONG Huichao,et al.Electrodeposited Preparation of Bi-Doped Metal Zinc and Its Performance Characterization[J].Plating & Finishing,2020,(1):12.[doi:10.3969/j.issn.1001-3849.2020.01.003]
[4]张永霞,王 玫,方 华*,等.Co3O4/碳纳米管复合膜的超级电容器性能[J].电镀与精饰,2020,(2):1.[doi:10.3969/j.issn.1001-3849.2020.02.001]
ZHANG Yongxia,WANG Mei,FANG Hua*,et al.Co3O4/Carbon Nanotube Composite Film for Supercapacitor and Its Performances[J].Plating & Finishing,2020,(1):1.[doi:10.3969/j.issn.1001-3849.2020.02.001]
[5]侯珂珂,陈新华,张万强,等.电沉积法制备仿生超疏水滤网及其油水分离性能[J].电镀与精饰,2020,(4):1.[doi:10.3969/j.issn.1001-3849.2020.04.0010]
HOU Keke,CHEN Xinhua,ZHANG Wanqiang,et al.Preparation of Biomimetic Superhydrophobic Filter Screen by Electrodeposition and the Oil-Water Separation Performance[J].Plating & Finishing,2020,(1):1.[doi:10.3969/j.issn.1001-3849.2020.04.0010]
[6]肖成龙,梁世雍,于兆勤*.可控阵列微柱超疏水表面实验研究[J].电镀与精饰,2020,(7):27.[doi:10.3969/j.issn.1001-3849.2020.07.0060]
XIAO Chenglong,LIANG Shiyong,YU Zhaoqin*.Experimental Study on Superhydrophobic Surface of Controllable Array Microcolumns[J].Plating & Finishing,2020,(1):27.[doi:10.3969/j.issn.1001-3849.2020.07.0060]
[7]徐 超,王淼宇,周建波,等.电沉积Ni-Mo-Fe-La合金析氢电极的工艺研究[J].电镀与精饰,2020,(8):7.[doi:10.3969/j.issn.1001-3849.2020.08.0020]
XU Chao,WANG Miaoyu,ZHOU Jianbo,et al.Study on Electrodeposition Process of Ni-Mo-Fe-La Alloy Hydrogen Evolution Electrode[J].Plating & Finishing,2020,(1):7.[doi:10.3969/j.issn.1001-3849.2020.08.0020]
[8]高 辉,刘伟杰*.2A12铝合金电沉积Ni-Co-MoS2复合镀层的耐磨性能研究[J].电镀与精饰,2020,(10):1.[doi:10.3969/j.issn.1001-3849.2020.10.0010]
GAO Hui,LIU Weijie*.Research on Wear Resistance of Ni-Co-MoS2 Composite Coating Electrodeposited on 2A12 Aluminium Alloy[J].Plating & Finishing,2020,(1):1.[doi:10.3969/j.issn.1001-3849.2020.10.0010]
[9]王 羽,刘励昀,杜荣斌*,等.添加剂MPS、DDAC、Cl-对铜箔电沉积的影响[J].电镀与精饰,2021,(5):1.[doi:10.3969/j.issn.1001-3849.2021.05.001]
WANG Yu,LIU Liyun,DU Rongbin*,et al.Effects of Additives MPS, DDAC and Cl- on the Copper Foil[J].Plating & Finishing,2021,(1):1.[doi:10.3969/j.issn.1001-3849.2021.05.001]
[10]杨惠良*.硫酸盐镀液中紫铜电沉积Ni-Co/WC复合镀层的工艺条件优化[J].电镀与精饰,2021,(6):30.[doi:10.3969/j.issn.1001-3849.2021.06.007]
YANG Huiliang*.Optimization of Process Conditions for Electrodeposition of Ni-Co/WC Composite Coatings on Red Copper from Sulfate Bath[J].Plating & Finishing,2021,(1):30.[doi:10.3969/j.issn.1001-3849.2021.06.007]
备注/Memo
收稿日期: 2023-02-27 修回日期: 2023-03-21 作者简介: 张璐( 1995 ―),男,硕士研究生, email : zl154109739@163.com * 通信作者: 卫国英, email : guoyingwei@cjlu.edu.cn 基金项目: 国家自然科学基金资助项目( 52171083 )