CHEN Li*,CHEN Yufeng,ZHANG Jianda.Corrosion Failure Behavior of Silicate Sealed Phosphating Film on Surface of Magnesium Alloy[J].Plating & Finishing,2022,(1):57-62.[doi:10.3969/j.issn.1001-3849.2022.01.010]
镁合金表面硅酸盐封闭磷化膜的腐蚀失效行为
- Title:
- Corrosion Failure Behavior of Silicate Sealed Phosphating Film on Surface of Magnesium Alloy
- Keywords:
- silicate sealed phosphating film; magnesium alloy; corrosion failure behavior; protective effect; corrosion inhibition efficiency
- 分类号:
- TB43
- 文献标志码:
- A
- 摘要:
- 在镁合金表面制备磷化膜并对其进行硅酸盐封闭,然后以3.5%氯化钠溶液作为腐蚀介质浸泡不同时间,采用全浸腐蚀法和电化学工作站考察硅酸盐封闭磷化膜的腐蚀失效行为。结果表明,浸泡48 h以内,磷化膜的腐蚀程度较轻,晶粒间的缝隙较少,其电化学阻抗谱表现为单一容抗弧且容抗弧半径相差不大,能较好的抑制腐蚀发生。随着浸泡时间延长,磷化膜表面锈斑明显增多且颜色加深,腐蚀面积呈大幅度增加的趋势,表面较粗糙、晶粒间形成了细长的缝隙,电荷转移电阻和缓蚀效率都呈现先大幅度降低然后基本不变的趋势,耐蚀性能逐步下降。当浸泡超过168 h后,磷化膜遭到严重破坏,表面几乎完全覆盖锈斑且形成了贯穿性缝隙,电化学阻抗谱表现为容抗弧和感抗弧特征,其耐蚀性能很差处于失效状态,对镁合金起不到防护作用。
- Abstract:
- Phosphating film was prepared on the surface of magnesium alloy and then sealed with silicate, and the corrosion failure behavior of silicate sealed phosphating film was investigated by total immersion corrosion method and electrochemical workstation taking 3.5% sodium chloride solution as corrosion medium immersed for different time. The results showed that the corrosion degree of phosphating film was light and the gaps between the grains was less when immersed less than 48 h, the electrochemical impedance spectrum showed a single capacitive arc, and the radius of capacitive arc had little difference, indicating that the phosphating film could effectively inhibit the corrosion. With the prolongation of immersion time, the rust spots on the surface of phosphating film increased obviously and the color deepened, the corrosion area increased greatly, and the surface was rough and the thin cracks were formed between the grains. Moreover, the charge transfer resistance and corrosion inhibition efficiency both decreased greatly at first and then basically remained the same, indicating that the corrosion resistance weakened gradually. After immersed for more than 168 h, the phosphating film was seriously damaged and its surface was almost completely covered with rust spots and formed penetrating cracks. The electrochemical impedance spectra showed capacitive arc and inductive arc characteristics, its corrosion resistance was poor and was in failure state, and it could not play a protective effect on magnesium alloy
参考文献/References:
[1] 周虎亮, 周勇, 陈钇江, 等. 高锰酸盐对镁合金表面磷化膜形貌和防护性能的影响[J]. 材料保护, 2018, 51(10): 84-87.
Zhou H L, Zhou Y, Chen Y J, et al. Effects of permanganate anions on surface morphology and corrosion resistance of phosphate conversion coatings on AZ91D magnesium alloy[J]. Materials Protection, 2018, 51(10): 84-87 (in Chinese).
[2] 曹京宜, 王臣业, 徐敏, 等. 镁铝合金表面锶磷化膜的改性及其腐蚀性能研究[J]. 材料导报, 2017, 31(z2): 282-285.
Cao J Y, Wang C Y, Xu M, et al. Modification of strontium phosphate film on magnesium-aluminum alloy surface and its corrosion properties[J]. Materials Review, 2017, 31(z2): 282-285 (in Chinese).
[3] 张涵. 镀锌钢板表面磷化膜的制备与性能研究[D]. 新乡: 河南师范大学, 2018.
[4] 陈晓明. 镁合金上单宁酸系转化膜和钙系磷化膜的制备和性能的研究[D]. 长春: 吉林大学, 2010.
[5] 安成强, 刘新院, 陈梨, 等. 锌锰系磷化膜硅酸钠封闭工艺研究[J]. 表面技术, 2012, 41(3): 84-86.
An C Q, Liu X Y, Chen L, et al. Study on process of sodium silicate sealing for zinc-manganese phosphate coating[J]. Surface Technology, 2012, 41(3): 84-86 (in Chinese).
[6] Lin B L, Lu J T. Self-healing mechanism of composite coatings obtained by phosphating and silicate sol post-sealing[J]. Transactions of Nonferrous Metals Society of China, 2014, 24(8): 2723-2728.
[7] 齐迎萍, 李振兴, 邵帅, 等. 磷化与封护处理对铁质文物的保护作用[J]. 腐蚀与防护, 2018, 39(4): 318-322.
Qi Y P, Li Z X, Shao S, et al. Protection of phsphating and sealing for iron cultural relics[J]. Corrosion & Protection, 2018, 39(4): 318-322 (in Chinese).
[8] 张彤丹, 曹中秋, 张媛, 等. 纳米化对Ag-50Ni在H3PO4介质中腐蚀电化学行为影响[J]. 沈阳师范大学学报(自然科学版), 2012, 30(1): 85-89.
Zhang T D, Cao Z Q, Zhang Y, et al. On corrosion electrochemical behaviors of nanocrystalline bulk Ag-50Ni alloy in H3PO4 solution[J]. Journal of Shenyang Normal University (Natural Science Edition), 2012, 30(1): 85-89 (in Chinese).
[9] Chen H X, Kong D J. Effects of laser remelting speeds on microstructure, immersion corrosion, and electrochemical corrosion of arc-sprayed amorphous Al-Ti-Ni coatings[J]. Journal of Alloys and Compounds, 2019(771): 584-594.
[10] Xu Y Z, Liu L, Xu C B, et al. Electrochemical characteristics of the dynamic progression of erosion-corrosion under different flow conditions and their effects on corrosion rate calculation[J]. Journal of Solid State Electrochemistry, 2020(24): 2511-2524.
[11] 吕丹丹. 铁表面构建烷氧基硅烷超疏水涂层及其耐蚀性能研究[D]. 济南: 山东大学, 2017.
[12] 高正源, 曹献龙, 刘浪, 等. 镁合金表面有机/无机杂化涂层的性能[J]. 材料研究学报, 2017, 31(3): 211-218.
相似文献/References:
[1]徐美玲,亢淑梅,陈婷婷,等.添加氯化铈对镁合金Ni?P化学镀镀层性能影响[J].电镀与精饰,2019,(1):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
XU Meiling,KANG Shumei,CHEN Tingting,et al.Properties of Electroless Plating Ni?P on Magnesium AlloySubstrate by Adding CeCl3[J].Plating & Finishing,2019,(1):37.[doi:10.3969/j.issn.1001-3849.2019.01.008]
[2]牟世辉,尹鸿鹍,代肇一.镀铜优化对AZ91D镁合金疏水膜性能的影响[J].电镀与精饰,2019,(6):29.[doi:10.3969/j.issn.1001-3849.2019.06.006]
MU Shihui,YIN Hongkun,DAI Zhaoyi.Effect of Copper Plating Optimization on the Performance of AZ91D Magnesium Alloy Hydrophobic Membrane[J].Plating & Finishing,2019,(1):29.[doi:10.3969/j.issn.1001-3849.2019.06.006]
[3]刘 玮,安成强*,郝建军,等.钼酸钠对AZ91D镁合金钒/锆复合转化膜性能的影响[J].电镀与精饰,2019,(8):10.[doi:10.3969/j.issn.1001-3849.2019.08.003]
LIU Wei,AN Chengqiang*,HAO Jianjun,et al.Effect of Na2MoO4 on Properties of Vanadium/Zirconate Conversion Coating on AZ91D Magnesium Alloy[J].Plating & Finishing,2019,(1):10.[doi:10.3969/j.issn.1001-3849.2019.08.003]
[4]李佳霖,郝建军,牟世辉.Fe2+对镁合金电化学磷化改性研究[J].电镀与精饰,2019,(10):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
LI Jialin,HAO Jianjun,MOU Shihui.Study on Electrochemical Phosphating Modification of Magnesium Alloy by Fe2+[J].Plating & Finishing,2019,(1):1.[doi:10.3969/j.issn.1001-3849.2019.10.001]
[5]贾启华,许晓娟*.沉积时间对镁合金化学镀镍的影响[J].电镀与精饰,2019,(12):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
JIA Qihua,XU Xiaojuan*.Effect of Deposition Time on Direct Electroless Plating of Magnesium Alloys[J].Plating & Finishing,2019,(1):1.[doi:10.3969/j.issn.1001-3849.2019.12.001]
[6]王 丽,顾 威,郭 荣,等.环保型无机缓蚀剂对AZ91D镁合金的缓蚀效果[J].电镀与精饰,2020,(4):18.[doi:10.3969/j.issn.1001-3849.2020.04.0040]
WANG Li,GU Wei,GUO Rong,et al.Inhibition Effect of Environmental Protection Inorganic Corrosion Inhibitor on AZ91D Magnesium Alloy[J].Plating & Finishing,2020,(1):18.[doi:10.3969/j.issn.1001-3849.2020.04.0040]
[7]党在清*.镁合金复合镀层的制备及其结构与性能表征[J].电镀与精饰,2020,(11):16.[doi:10.3969/j.issn.1001-3849.2020.11.0040]
DANG Zaiqing*.Study on the Structure and Properties of Composite Coating on Magnesium Alloy[J].Plating & Finishing,2020,(1):16.[doi:10.3969/j.issn.1001-3849.2020.11.0040]
[8]王晓奇*,曹 慧,雷 彪.镁合金表面电弧离子镀TiAlN薄膜的结构与性能研究[J].电镀与精饰,2021,(6):25.[doi:10.3969/j.issn.1001-3849.2021.06.006]
WANG Xiaoqi*,CAO Hui,LEI Biao.Structure and Properties of TiAlN Films by Arc Ion Plating on Mg Alloys[J].Plating & Finishing,2021,(1):25.[doi:10.3969/j.issn.1001-3849.2021.06.006]
[9]宋政伟*,丁莉峰,王沛霖,等.镁合金表面Ni-P/Cu-Zn超疏水复合涂层制备及耐蚀性研究[J].电镀与精饰,2021,(7):10.[doi:10.3969/j.issn.1001-3849.2021.07.002]
SONG Zhengwei*,DING Lifeng,WANG Peilin,et al.Preparation and Corrosion Resistance of Ni-P/Cu-Zn Super-Hydrophobic Composite Coating on the Surface of Mg Alloy[J].Plating & Finishing,2021,(1):10.[doi:10.3969/j.issn.1001-3849.2021.07.002]
[10]牟世辉*,李鑫宇.恒电流作用下AZ91D镁合金磷化膜生长研究[J].电镀与精饰,2021,(9):1.[doi:10.3969/j.issn.1001-3849.2021.09.001]
MU Shihui*,LI Xinyu.Growth of Phosphating Film on AZ91D Magnesium Alloy Under Constant Current[J].Plating & Finishing,2021,(1):1.[doi:10.3969/j.issn.1001-3849.2021.09.001]
备注/Memo
收稿日期: 2021-04-09 修回日期: 2021-06-03 作者简介: 陈力(1972-),硕士,高级工程师,研究方向:化工工艺、材料工程等,email:chen_education00@163.com