Tian Huijuan*,Zhao Yue,Guo Qiangqiang,et al.Study on corrosion inhibition of a ternary complex inhibitor composed of o-toluenesulfonamide[J].Plating & Finishing,2024,(2):62-70.[doi:10.3969/j.issn.1001-3849.2024.02.009]
邻甲苯磺酰胺三元复配缓蚀剂的缓蚀性能研究
- Title:
- Study on corrosion inhibition of a ternary complex inhibitor composed of o-toluenesulfonamide
- Keywords:
- corrosion inhibitor ; o-toluenesulfonamide ; synergistic effect ; carbon steel
- 分类号:
- TG174.42
- 文献标志码:
- A
- 摘要:
- 为了研制出用量少、效率高的低毒高效缓蚀剂,采用失重法、电化学和扫描电镜( SEM )研究了邻甲苯磺酰胺( OTS )、碘化钾( KI )和十六烷基三甲基溴化铵( CTAB )复配的三元缓蚀剂在 0.5 mol·L -1 硫酸溶液中的缓蚀作用。通过正交试验得到三元缓蚀剂最优浓度比为 OTS ∶ KI ∶ CTAB=15 ∶ 6 ∶ 5 ,总浓度 130 mg·L -1 时,缓蚀率可达 98.18 % 。添加三元缓蚀剂后腐蚀过程的活化能增大,说明腐蚀反应更难发生。三元缓蚀剂符合 Langmuir 吸附等温式,在碳钢表面的吸附为自发的弱化学吸附过程。极化曲线法和电化学阻抗法( EIS )计算的缓蚀率均与失重法一致。极化曲线表明三元缓蚀剂是以抑制阳极反应为主的混合型缓蚀剂。 SEM 微观相貌可看出添加三元缓蚀剂后,碳钢表面几乎无腐蚀痕迹,说明三元缓蚀剂分子之间具有缓蚀协同作用,形成了致密牢固的保护膜。
- Abstract:
- : In order to develop a low toxicity and high efficiency corrosion inhibitor with less dosage and high efficiency , the corrosion inhibition effect of a ternary corrosion inhibitor composed of o-toluenesulfonamide ( OTS ), potassium iodide ( KI ) and cetyltrimethyl ammonium bromide ( CTAB ) in 0.5 mol·L -1 sulfuric acid solution was studied by weight loss method , electrochemistry and scanning electron microscopy ( SEM ) . The optimal concentration ratio of the ternary corrosion inhibitor was OTS ∶ KI ∶ CTAB=15 ∶ 6 ∶ 5 , and the corrosion inhibition efficiency reached 98.18 % with the total concentration of 130 mg·L -1 . The activation energy of corrosion process increased after the addition of ternary corrosion inhibitor , indicating that the corrosion reaction was more difficult to occur. The ternary corrosion inhibitor conformed to the Langmuir adsorption isothermal formula , and the adsorption on the surface of carbon steel was a spontaneous weak chemical adsorption process. The corrosion inhibition efficiencies calculated by polarization curve method and electrochemical impedance method were consistent with that by weight loss method. The polarization curve showed that the ternary corrosion inhibitor was a mixed type corrosion inhibitor which mainly inhibited anode reaction. SEM microscopic appearance showed that there was almost no corrosion trace on the surface of carbon steel after the addition of ternary corrosion inhibitor , indicating that there was a synergistic effect of corrosion inhibition between ternary corrosion inhibitor molecules , forming a dense and firm protective film.
相似文献/References:
[1]郝鑫铭,廖欣怡,周晓荣*,等.从富硒茶叶中提取碳钢酸洗缓蚀剂[J].电镀与精饰,2022,(2):71.[doi:doi: 10.3969/j.issn.1001-3849.2022.02.015]
GU Yuan,SONG Yao.Acid Corrosion Inhibitor for Carbon Steel Extracted from Se-Rich Tea Leaves[J].Plating & Finishing,2022,(2):71.[doi:doi: 10.3969/j.issn.1001-3849.2022.02.015]
[2]周闻云*,郭 蓓,李冬冬,等. 钢材用缓蚀剂研究进展 [J].电镀与精饰,2023,(3):83.[doi:10.3969/j.issn.1001-3849.2023.03.012]
Zhou Wenyun*,Guo Bei,Li Dongdong,et al.Research progress of corrosion inhibitor for steel[J].Plating & Finishing,2023,(2):83.[doi:10.3969/j.issn.1001-3849.2023.03.012]
[3]胡超鹤*,杭智军,王媛.氯盐型融雪剂用高效复合缓蚀剂的性能研究[J].电镀与精饰,2023,(9):23.[doi:10.3969/j.issn.1001-3849.2023.09.004]
Hu Chaohe*,Hang Zhijun,Wang Yuan.Properties of the high-efficiency composite corrosion inhibitor for chloride-based deicing agents[J].Plating & Finishing,2023,(2):23.[doi:10.3969/j.issn.1001-3849.2023.09.004]
[4]李雨洹,曹献龙 *,田维玮,等. 过期医疗药品对镁合金缓蚀作用的电化学研究 [J].电镀与精饰,2023,(9):85.[doi:10.3969/j.issn.1001-3849.2023.09.014]
Li Yuhuan,Cao Xianlong *,Tian Weiwei,et al.Electrochemical study on corrosion inhibition of expired medical drug on magnesium alloy[J].Plating & Finishing,2023,(2):85.[doi:10.3969/j.issn.1001-3849.2023.09.014]
[5]田会娟*,赵 玥,曹玉霞,等.酪氨酸衍生物对Q235钢的缓蚀性能研究[J].电镀与精饰,2023,(10):40.[doi:10.3969/j.issn.1001-3849.2023.10.007]
Tian Huijuan*,Zhao Yue,Cao Yuxia,et al.Study on corrosion inhibition of Q235 steel by tyrosine derivative[J].Plating & Finishing,2023,(2):40.[doi:10.3969/j.issn.1001-3849.2023.10.007]
[6]唐晓军*.环保缓蚀剂在金属管材中的应用研究进展[J].电镀与精饰,2023,(11):93.[doi:10.3969/j.issn.1001-3849.2023.11.014]
Tang Xiaojun *.Application research progress of environmentally friendly corrosion inhibitors in metal pipes[J].Plating & Finishing,2023,(2):93.[doi:10.3969/j.issn.1001-3849.2023.11.014]
[7]田子诚,李国楼,周晓荣*,等.薄荷叶多糖作为碳钢酸洗缓蚀剂的研究[J].电镀与精饰,2024,(6):34.[doi:10.3969/j.issn.1001-3849.2024.06.005]
Tian Zicheng,Li Guolou,Zhou Xiaorong*,et al.Study on inhibition performance of extracted polysaccharides from mint leaves for pickling of carbon steel[J].Plating & Finishing,2024,(2):34.[doi:10.3969/j.issn.1001-3849.2024.06.005]
备注/Memo
收稿日期: 2023-07-19 修回日期: 2023-09-01 * 通信作者: 田会娟( 1982 —),女,博士,副教授, email : hjtian82@163.com 基金项目: 唐山市科技局项目( 21130232C );河北省高等学校科学技术(青年)项目( QN202205 );唐山师范学院校内项目( 2222C40 )