LIU Yan*,XU Yanwei,YIN Xiaojian,et al.Corrosion Resistance of Aluminum Coatings on Fastener[J].Plating & Finishing,2020,(10):12-16.[doi:10.3969/j.issn.1001-3849.2020.10.0030]
紧固件真空镀铝层耐腐蚀性能评价
- Title:
- Corrosion Resistance of Aluminum Coatings on Fastener
- 文献标志码:
- A
- 摘要:
- 铝镀层是航空航天紧固件腐蚀防护最常用的涂镀层之一，用于防止紧固件与铝合金基体之间的接触腐蚀。本文通过中性盐雾试验（NSS）、醋酸盐雾试验、湿热试验、海洋大气暴晒试验等综合对比了带真空镀铝层紧固件的耐腐蚀性能。结果表明，磁控溅射镀铝和离化蒸发镀铝的耐腐蚀性能大体相当，但磁控溅射镀铝层黑斑相对较少，中性盐雾试验2000 h无基体腐蚀，耐腐蚀性能略优。
- Abstract:
- Aluminum is one of the most common protective coating used on aerospace fasteners preventing contact corrosion occurred in aluminum structure coupled with fasteners. Neutral salt spray test （NSS）, acetic acid salt spray, damp heat test and marine atmospheric exposure test were adopted to characterize the corrosion resistance of fasteners with two types of aluminum coatings. The result showed that the corrosion resistance of fasteners with magnetic sputtering aluminum coating was equivalent to that with vapor deposition aluminum coating. Sputtering aluminum coating presented slightly better corrosion resistance with less black corrosion speckle, and no corrosion occurred on the substrate of the fastener after 2000 h NSS test.
参考文献/References:
[1] Elizabeth B, Eric B. Investigation of chemical vapor deposited aluminum as a replacement coating for cadmium[C] //Joint Cadmium Alternatives Team Annual Meeting, 2007.
[2] 赵创业. 军械零件的离子镀铝[J]. 表面技术, 1984, 4: 3-8.
Zhao C Y. Ion vapor deposition aluminum on military instruments parts[J]. Surface Technology, 1984, 4: 3-8 （in Chinese）.
[3] 胡如南, 黄子勋. 离子气相沉积镀铝层的应用[J]. 航空工艺技术, 1981, 7: 24-27.
Hu R N, Huang Z X. Application of ion vapor deposition aluminum coatings[J]. Aerospace Process Technology, 1981, 7: 24-27 （in Chinese）.
[4] 李月辉. 航空螺栓用钛合金材料及镀铝工艺研究[J]. 稀有金属材料与工程, 1996, 26: 6.
Li Y H. Investigation on titanium alloy material and aluminum deposition process on aerospace bolts[J]. Rare Metal Materials and Engineering, 1996, 26: 6 （in Chinese）.
[5] 于家斗. 离子镀铝[J]. 稀有金属材料与工程, 1990, 3: 12-15.
Yu J D. Aluminum ion vapor deposition[J]. Rare Metal Materials and Engineering, 1990, 3:12-15 （in Chinese）.
[6] 陈宝清. 真空离子镀部分代替电镀技术研究及国内外现状[J]. 材料保护, 2011, 44（11）: 80-86.
Chen B Q. Investigation on technology and present situation of substitution of ion vapor deposition to partial electroplating[J]. Materials Protection, 2011, 44（11）: 80-86 （in Chinese）.
[7] 廖富达, 侯惠君, 石倩, 等. 离子辅助蒸发沉积镀铝膜的结构及耐腐蚀性[J]. 金属热处理, 2017, 42（10）: 149-154.
Liao F D, Hou H J, Shi Q, et al. Microstructure and corrosion resistance of aluminum film deposited by ion assisted thermal evaporation[J]. Heat Treatment of Metals, 2017, 42（10）: 149-154 （in Chinese）.
[8] 谢发勤, 金石, 严密林, 等. 离子镀铝的钛合金紧固件的耐腐蚀性能研究[J]. 西北工业大学学报, 1995, 13（1）: 147-150.
Xie F Q, Jin S, Yan M L, et al. Corrosion resistance of titanium alloy fastener ion-plated with aluminum[J]. Journal of Northwestern Polytechnical University, 1995, 13（11）: 147-150 （in Chinese）.
[9] 胡芳, 代明江, 侯惠君, 等. 30CrMnSiNi2A钢紧固件磁控溅射铝膜的腐蚀和氢脆性能[J]. 中国表面工程, 2016, 29（5）: 41-48.
Hu F, Dai M J, Hou H J, et al. Corrosion resistance and hydrogen embrittlement performance of Al film deposited by magnetron sputtering on fasteners of 30CrMnSiNi2A steel[J]. China Surface Engineering, 2016, 29（5）: 41-48 （in Chinese）.
[10] 杨专钊. 钛合金紧固件连接结构接触腐蚀行为及其控制技术研究[D]. 西安: 西北工业大学, 2004.
相似文献/References:
[1]詹兴刚,胡军林,刘 燕*,等.航空发动机用离子镀银紧固件的耐酸性盐雾性能研究[J].电镀与精饰,2022,(11):12.[doi:10.3969/j.issn.1001-3849.2022.11.003]
ZHAN Xinggang,HU Junlin,LIU Yan*,et al.Study on Acid Salt Spray Corrosion Resistance of Fasteners with Vacuum ion Plated Silver Coating used on Aero Engine[J].Plating & Finishing,2022,(10):12.[doi:10.3969/j.issn.1001-3849.2022.11.003]
[2]宋启良*,李吉丹,郑玉杰,等.航天用T9A-D弹簧表面离子液体镀Al工艺研究[J].电镀与精饰,2024,(2):10.[doi:10.3969/j.issn.1001-3849.2024.02.002]
Song Qiliang*,Li Jidan,Zheng Yujie,et al.Study on ionic liquid Al plating technology on surface of T9A-D spring for aerospace applications[J].Plating & Finishing,2024,(10):10.[doi:10.3969/j.issn.1001-3849.2024.02.002]
备注/Memo
收稿日期： 2020-03-20；修回日期： 2020-05-07
通信作者： 刘燕， email: aliya0719@163.com
基金项目： 中国航天科工集团公司共性工艺项目